Effects of dodecacalcium heptaaluminate content on the setting time, compressive strength, alkalinity, and cytocompatibility of tricalcium silicate cement

• Autor(a) principal: Choi, Yoorina
• Data de Publicação: 2019
• Outros Autores: Bae, Jong-Lye, Kim, Hee-Jin, Yu, Mi-Kyung, Lee, Kwang-Won, Min, Kyung-San
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Journal of applied oral science (Online)
• Texto Completo: https://www.revistas.usp.br/jaos/article/view/158559
• topic: Calcium silicate; Dental pulp; Physicochemical analysis; Material testing

Objective: This study aimed to investigate the effects of dodecacalcium hepta-aluminate (C12A7) content on some physicochemical properties and cytocompatibility of tricalcium silicate (C3S) cement using human dental pulp cells (hDPCs). Material and Methods: High purity C3S cement was manufactured by a solid phase method. C12A7 was mixed with the cement in proportions of 0, 5, 8, and 10 wt% (C12A7-0, -5, -8, and -10, respectively). Physicochemical properties including initial setting time, compressive strength, and alkalinity were evaluated. Cytocompatibility was assessed with cell viability tests and cell number counts. Statistical analysis was performed by using one-way analysis of variance (ANOVA) and Tukey’s test (p<0.05). Results: The initial setting time of C3S-based cement was shorter in the presence of C12A7 (p<0.05). After 1 day, C12A7-5 showed significantly higher compressive strength than the other groups (p<0.05). After 7 days, the compressive strength of C12A7-5 was similar to that of C12A7-0, whereas other groups showed strength lower than C12A7-0. The pH values of all tested groups showed no significant differences after 1 day (p>0.05). The C12A7-5 group showed similar cell viability to the C12A7-0 group (p>0.05), while the other experimental groups showed lower values compared to C12A7-0 group (p<0.05). The number of cells grown on the C12A7-5 specimen was higher than that on C12A7-8 and -10 (p<0.05). Conclusions: The addition of C12A7 to C3S cement at a proportion of 5% resulted in rapid initial setting time and higher compressive strength with no adverse effects on cytocompatibility.