Evaluation of the remineralizing capacity of silver diamine fluoride on demineralized dentin under pH-cycling conditions

• Autor(a) principal: Cifuentes-Jiménez, Carolina Cecilia
• Data de Publicação: 2023
• Outros Autores: Bolaños-Carmona, María Victoria, Enrich-Essvein, Tatiana, González-López, Santiago, Álvarez-Lloret, Pedro
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Journal of applied oral science (Online)
• Texto Completo: https://www.revistas.usp.br/jaos/article/view/210005
• topic: Dentin; Sodium fluoride; Biomineralization; Dental caries; Silver compounds; Silver diamine; Crystallization

Objective: (1) to determine the effects of the silver diamine fluoride (SDF) and sodium fluoride (NaF) in demineralized dentin exposed to an acid challenge by pH-cycling, (2) to evaluate the remineralizing capacity of SDF/NaF products based on the physicochemical and mechanical properties of the treated dentin surfaces. Methodology: In total, 57 human molars were evaluated in different stages of the experimental period: sound dentin – negative control (Stage 1), demineralized dentin – positive control (Stage 2), and dentin treated with SDF/NaF products + pH-c (Stage 3). Several commercial products were used for the SDF treatment: Saforide, RivaStar, and Cariestop. The mineral composition and crystalline and morphological characteristics of the dentin samples from each experimental stage were evaluated by infrared spectroscopy (ATR-FTIR), X-ray diffraction, and electron microscopy (SEM-EDX) analytical techniques. Moreover, the mechanical response of the samples was analyzed by means of the three-point bending test. Statistics were estimated for ATR-FTIR variables by Wilcoxon test, while the mechanical data analyses were performed using Kruskal-Wallis and Mann Whitney U tests. Results: Regarding the chemical composition, we observed a higher mineral/organic content in the SDF/NaF treated dentin + pH-c groups (Stage 3) than in the positive control groups (Saforide p=0.03; Cariestop p=0.008; RivaStar p=0.013; NaF p=0.04). The XRD results showed that the crystallite size of hydroxyapatite increased in the SDF/NaF treated dentin + pH-c groups (between +63% in RivaStar to +108% in Saforide), regarding the positive control. SEM images showed that after application of the SDF/NaF products a crystalline precipitate formed on the dentin surface and partially filled the dentin tubules. The flexural strength (MPa) values were higher in the dentin treated with SDF/NaF + pH-c (Stage 3) compared to the positive control groups (Saforide p=0.002; Cariestop p=0.04; RivaStar p=0.04; NaF p=0.02). Conclusions: The application of SDF/NaF affected the physicochemical and mechanical properties of demineralized dentin. According to the results, the use of SFD/NaF had a remineralizing effect on the dentin surface even under acid challenge.