Effect of the bur grit size on the flexural strength of a glass-ceramic

• Autor(a) principal: Kist,P. P.
• Data de Publicação: 2016
• Outros Autores: Aurélio,I. L., Amaral,M., May,L. G.
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Cerâmica (São Paulo. Online)
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0366-69132016000200121
• topic: IPS Empress CAD; leucite; grinding; surface roughness; flexural strength

Abstract The purpose of the present study was to determine the biaxial flexural strength (BFS) of a CAD/CAM leucite reinforced glass-ceramic ground by diamond burs of different grit sizes and the influence of surface roughness on the BFS. For this, 104 plates were obtained from CAD/CAM ceramic blocks and divided into 4 groups (n = 26), according to bur grit size: extra-fine, fine, medium and coarse. Roughness parameters (Ra, RyMax) were measured, and plates were kept dry for 7 days. The flexural test was carried out and BFS was calculated. Ra, RyMax and BFS data were subjected to analysis of variance and post-hoc test. Weibull analysis was used to compare characteristic strength and Weibull modulus. Regression analysis was performed for BFS vs. Ra and RyMax. When burs with coarse grit were used, higher surface roughness values were found, causing a negative effect on the ceramic BFS (117 MPa for extra-fine, and 83 MPa for coarse). Correlation (r) between surface roughness and BFS was 0.78 for RyMax and 0.73 for Ra. Increases in diamond grit size have a significant negative effect on the BFS of leucite-reinforced glass-ceramics, suggesting that grinding of sintered glass-ceramic should be performed using burs with the finest grit possible in order to minimize internal surface flaws and maximize flexural strength.