Characterization of the calcium-fluoroaluminosilicate glass prepared by a non-hydrolytic sol-gel route for future dental application as glass ionomer cement

• Autor(a) principal: Cestari,Alexandre
• Data de Publicação: 2009
• Outros Autores: Avila,Lilian Rodrigues, Nassor,Evelisy Cristina Oliveira, Pereira,Paula Fabiana dos Santos, Calefi,Paulo Sergio, Ciuffi,Katia Jorge, Nakagaki,Shirley, Gomes,Antonio Carlos Pereira, Nassar,Eduardo Jose
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Materials research (São Carlos. Online)
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1516-14392009000200005
• topic: aluminosilicate; dental cement; glass ionomer; NMR27Al-29Si

Glass ionomer cements are widely employed in dentistry due to their physical, biological and mainly anti-caries properties. Glass ionomers consist of an aluminosilicate glass matrix modified with other elements, and they contain large quantities of fluorine. In this study, we report on the preparation of calcium-fluoroaluminosilicate glasses by a nonhydrolytic sol-gel route as an alternative approach to obtaining alumina-silica matrices. The glass powders were prepared via the non-hydrolytic sol-gel method, by mixing AlCl3, SiCl4, CaF2, AlF3, NaF, and AlPO4. The powders were studied by thermal analysis (TG/DTA/DSC), photoluminescence (PL), nuclear magnetic resonance (NMR27Al-29Si), and X ray diffraction (XRD). TG/DTA/DSC analyses revealed a constant mass loss due to structural changes during the heating process, which was confirmed by NMR and PL. A stable aluminosilicate matrix with potential future application as a glass ionomer base was obtained.