Influence of alloy microstructure on the microshear bond strength of basic alloys to a resin luting cement
Autor(a) principal: | |
---|---|
Data de Publicação: | 2012 |
Outros Autores: | , , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Brazilian Dental Journal |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402012000500004 |
Resumo: | The aim of this study was to evaluate the influence of microstructure and composition of basic alloys on their microshear bond strength (µSBS) to resin luting cement. The alloys used were: Supreme Cast-V (SC), Tilite Star (TS), Wiron 99 (W9), VeraBond II (VBII), VeraBond (VB), Remanium (RM) and IPS d.SIGN 30 (IPS). Five wax patterns (13mm in diameter and 4mm height) were invested, and cast in a centrifugal casting machine for each basic alloy. The specimens were embedded in resin, polished with a SiC paper and sandblasted. After cleaning the metal surfaces, six tygon tubes (0.5 mm height and 0.75 mm in diameter) were placed on each alloy surface, the resin cement (Panavia F) was inserted, and the excess was removed before light-curing. After storage (24 h/37°C), the specimens were subjected to µSBS testing (0.5 mm/min). The data were subjected to a one-way repeated measures analysis of variance and Turkey's test (α=0.05). After polishing, their microstructures were revealed with specific conditioners. The highest µSBS (mean/standard deviation in MPa) were observed in the alloys with dendritic structure, eutectic formation or precipitation: VB (30.6/1.7), TS (29.8/0.9), SC (30.6/1.7), with the exception of IPS (31.1/0.9) which showed high µSBS but no eutectic formation. The W9 (28.1/1.5), VBII (25.9/2.0) and RM (25.9/0.9) showed the lowest µSBS and no eutectic formation. It seems that alloys with eutectic formation provide the highest µSBS values when bonded to a light-cured resin luting cement. |
id |
FUNORP-1_03284fa0d231bf2bdb2c2d608a481725 |
---|---|
oai_identifier_str |
oai:scielo:S0103-64402012000500004 |
network_acronym_str |
FUNORP-1 |
network_name_str |
Brazilian Dental Journal |
repository_id_str |
|
spelling |
Influence of alloy microstructure on the microshear bond strength of basic alloys to a resin luting cementdental cementsdental alloysshear strengthThe aim of this study was to evaluate the influence of microstructure and composition of basic alloys on their microshear bond strength (µSBS) to resin luting cement. The alloys used were: Supreme Cast-V (SC), Tilite Star (TS), Wiron 99 (W9), VeraBond II (VBII), VeraBond (VB), Remanium (RM) and IPS d.SIGN 30 (IPS). Five wax patterns (13mm in diameter and 4mm height) were invested, and cast in a centrifugal casting machine for each basic alloy. The specimens were embedded in resin, polished with a SiC paper and sandblasted. After cleaning the metal surfaces, six tygon tubes (0.5 mm height and 0.75 mm in diameter) were placed on each alloy surface, the resin cement (Panavia F) was inserted, and the excess was removed before light-curing. After storage (24 h/37°C), the specimens were subjected to µSBS testing (0.5 mm/min). The data were subjected to a one-way repeated measures analysis of variance and Turkey's test (α=0.05). After polishing, their microstructures were revealed with specific conditioners. The highest µSBS (mean/standard deviation in MPa) were observed in the alloys with dendritic structure, eutectic formation or precipitation: VB (30.6/1.7), TS (29.8/0.9), SC (30.6/1.7), with the exception of IPS (31.1/0.9) which showed high µSBS but no eutectic formation. The W9 (28.1/1.5), VBII (25.9/2.0) and RM (25.9/0.9) showed the lowest µSBS and no eutectic formation. It seems that alloys with eutectic formation provide the highest µSBS values when bonded to a light-cured resin luting cement.Fundação Odontológica de Ribeirão Preto2012-10-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402012000500004Brazilian Dental Journal v.23 n.5 2012reponame:Brazilian Dental Journalinstname:Fundação Odontológica de Ribeirão Preto (FUNORP)instacron:FUNORP10.1590/S0103-64402012000500004info:eu-repo/semantics/openAccessBauer,JoséCosta,José FerreiraCarvalho,Ceci NunesSouza,Douglas Nesadal deLoguercio,Alessandro DouradoGrande,Rosa Helena Mirandaeng2013-01-08T00:00:00Zoai:scielo:S0103-64402012000500004Revistahttps://www.scielo.br/j/bdj/https://old.scielo.br/oai/scielo-oai.phpbdj@forp.usp.br||sergio@fosjc.unesp.br1806-47600103-6440opendoar:2013-01-08T00:00Brazilian Dental Journal - Fundação Odontológica de Ribeirão Preto (FUNORP)false |
dc.title.none.fl_str_mv |
Influence of alloy microstructure on the microshear bond strength of basic alloys to a resin luting cement |
title |
Influence of alloy microstructure on the microshear bond strength of basic alloys to a resin luting cement |
spellingShingle |
Influence of alloy microstructure on the microshear bond strength of basic alloys to a resin luting cement Bauer,José dental cements dental alloys shear strength |
title_short |
Influence of alloy microstructure on the microshear bond strength of basic alloys to a resin luting cement |
title_full |
Influence of alloy microstructure on the microshear bond strength of basic alloys to a resin luting cement |
title_fullStr |
Influence of alloy microstructure on the microshear bond strength of basic alloys to a resin luting cement |
title_full_unstemmed |
Influence of alloy microstructure on the microshear bond strength of basic alloys to a resin luting cement |
title_sort |
Influence of alloy microstructure on the microshear bond strength of basic alloys to a resin luting cement |
author |
Bauer,José |
author_facet |
Bauer,José Costa,José Ferreira Carvalho,Ceci Nunes Souza,Douglas Nesadal de Loguercio,Alessandro Dourado Grande,Rosa Helena Miranda |
author_role |
author |
author2 |
Costa,José Ferreira Carvalho,Ceci Nunes Souza,Douglas Nesadal de Loguercio,Alessandro Dourado Grande,Rosa Helena Miranda |
author2_role |
author author author author author |
dc.contributor.author.fl_str_mv |
Bauer,José Costa,José Ferreira Carvalho,Ceci Nunes Souza,Douglas Nesadal de Loguercio,Alessandro Dourado Grande,Rosa Helena Miranda |
dc.subject.por.fl_str_mv |
dental cements dental alloys shear strength |
topic |
dental cements dental alloys shear strength |
description |
The aim of this study was to evaluate the influence of microstructure and composition of basic alloys on their microshear bond strength (µSBS) to resin luting cement. The alloys used were: Supreme Cast-V (SC), Tilite Star (TS), Wiron 99 (W9), VeraBond II (VBII), VeraBond (VB), Remanium (RM) and IPS d.SIGN 30 (IPS). Five wax patterns (13mm in diameter and 4mm height) were invested, and cast in a centrifugal casting machine for each basic alloy. The specimens were embedded in resin, polished with a SiC paper and sandblasted. After cleaning the metal surfaces, six tygon tubes (0.5 mm height and 0.75 mm in diameter) were placed on each alloy surface, the resin cement (Panavia F) was inserted, and the excess was removed before light-curing. After storage (24 h/37°C), the specimens were subjected to µSBS testing (0.5 mm/min). The data were subjected to a one-way repeated measures analysis of variance and Turkey's test (α=0.05). After polishing, their microstructures were revealed with specific conditioners. The highest µSBS (mean/standard deviation in MPa) were observed in the alloys with dendritic structure, eutectic formation or precipitation: VB (30.6/1.7), TS (29.8/0.9), SC (30.6/1.7), with the exception of IPS (31.1/0.9) which showed high µSBS but no eutectic formation. The W9 (28.1/1.5), VBII (25.9/2.0) and RM (25.9/0.9) showed the lowest µSBS and no eutectic formation. It seems that alloys with eutectic formation provide the highest µSBS values when bonded to a light-cured resin luting cement. |
publishDate |
2012 |
dc.date.none.fl_str_mv |
2012-10-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402012000500004 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402012000500004 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/S0103-64402012000500004 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
Fundação Odontológica de Ribeirão Preto |
publisher.none.fl_str_mv |
Fundação Odontológica de Ribeirão Preto |
dc.source.none.fl_str_mv |
Brazilian Dental Journal v.23 n.5 2012 reponame:Brazilian Dental Journal instname:Fundação Odontológica de Ribeirão Preto (FUNORP) instacron:FUNORP |
instname_str |
Fundação Odontológica de Ribeirão Preto (FUNORP) |
instacron_str |
FUNORP |
institution |
FUNORP |
reponame_str |
Brazilian Dental Journal |
collection |
Brazilian Dental Journal |
repository.name.fl_str_mv |
Brazilian Dental Journal - Fundação Odontológica de Ribeirão Preto (FUNORP) |
repository.mail.fl_str_mv |
bdj@forp.usp.br||sergio@fosjc.unesp.br |
_version_ |
1754204092243116032 |