Effect of cement type and water storage time on the push-out bond strength of a glass fiber post

• Autor(a) principal: Reis,Kátia Rodrigues
• Data de Publicação: 2011
• Outros Autores: Spyrides,George Miguel, Oliveira,Jonas Alves de, Jnoub,Alexandre Abrão, Dias,Kátia Regina Hostilio Cervantes, Bonfantes,Gerson
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Brazilian Dental Journal
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402011000500002
• topic: fiber post; resin cement; glass ionomer cement; hygroscopic ex

This study investigated the effects of the cement type and the water storage time on the push-out bond strength of a glass fiber post. Glass fiber posts (Fibrekor, Jeneric Pentron) were luted to post spaces using a self-cured resin cement (C&B Cement [CB]), a glass ionomer cement (Ketac Cem [KC]) or a resin-modified glass ionomer cement (GC FujiCEM [FC]) according to the manufacturers’ instructions. For each luting agent, the specimens were exposed to one of the following water storage times (n=5): 1 day (T1), 7 days (T7), 90 days (T90) and 180 days (T180). Push-out tests were performed after the storage times. Control specimens were not exposed to water storage, but subjected to the push-out test 10 min after post cementation. Data (in MPa) were analyzed by Kruskal-Wallis and Dunn`s test (α=0.05). Cement type and water storage time had a significant effect (p<0.05) on the push-out bond strength. CB showed significantly higher values of retention (p<0.05) than KC and FC, irrespective of the water storage time. Water storage increased significantly the push-out bond strength in T7 and T90, regardless of the cement type (p<0.05). The results showed that fiber posts luted to post spaces with the self-cured resin cement exhibited the best bonding performance throughout the 180-day water storage period. All cements exhibited a tendency to increase the bond strength after 7 and 90 days of water storage, decreasing thereafter.