Polytetrafluorethylene added to acrylic resins: mechanical properties
Autor(a) principal: | |
---|---|
Data de Publicação: | 2010 |
Outros Autores: | , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Brazilian Dental Journal |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402010000100009 |
Resumo: | The addition of different polymers, such as polytetrafluorethylene (PTFE), to denture base resins could be an option to modify acrylic resin mechanical properties. This study evaluated the surface hardness, impact and flexural strength, flexural modulus and peak load of 2 acrylic resins, one subjected to a long and another subjected to a short polymerization cycle, which were prepared with or without the addition of 2% PTFE. Four groups were formed according to the polymerization cycle and addition or not of PTFE. Forty specimens were prepared for each test (10 per group) with the following dimensions: hardness (30 mm diameter x 5 mm thick), impact strength (50 x 6 x 4 mm) and flexural strength (64 x 10 x 3.3 mm) test. The results of the flexural strength test allowed calculating flexural modulus and peak of load values. All tests were performed in accordance with the ISO 1567:1999 standard. Data were analyzed statistically by ANOVA and Tukey's test with the level of significance set at 5%. No statistically significant differences (p>0.05) were found for surface hardness. Flexural strength, impact strength and peak load were significantly higher (p<0.05) for resins without added PTFE. The flexural modulus of the acrylic resin with incorporated 2% PTFE polymerized by long cycle was significantly higher (p<0.05) than that of the other resins. Within the limits of this study, it may be concluded that the addition of PTFE did not improve the mechanical properties of the evaluated acrylic resins. |
id |
FUNORP-1_ed90f5ff8e76c22438d81465453259c7 |
---|---|
oai_identifier_str |
oai:scielo:S0103-64402010000100009 |
network_acronym_str |
FUNORP-1 |
network_name_str |
Brazilian Dental Journal |
repository_id_str |
|
spelling |
Polytetrafluorethylene added to acrylic resins: mechanical propertiesacrylic resinpolytetrafluoroethylenesurface hardnessimpact strength and flexural strengthThe addition of different polymers, such as polytetrafluorethylene (PTFE), to denture base resins could be an option to modify acrylic resin mechanical properties. This study evaluated the surface hardness, impact and flexural strength, flexural modulus and peak load of 2 acrylic resins, one subjected to a long and another subjected to a short polymerization cycle, which were prepared with or without the addition of 2% PTFE. Four groups were formed according to the polymerization cycle and addition or not of PTFE. Forty specimens were prepared for each test (10 per group) with the following dimensions: hardness (30 mm diameter x 5 mm thick), impact strength (50 x 6 x 4 mm) and flexural strength (64 x 10 x 3.3 mm) test. The results of the flexural strength test allowed calculating flexural modulus and peak of load values. All tests were performed in accordance with the ISO 1567:1999 standard. Data were analyzed statistically by ANOVA and Tukey's test with the level of significance set at 5%. No statistically significant differences (p>0.05) were found for surface hardness. Flexural strength, impact strength and peak load were significantly higher (p<0.05) for resins without added PTFE. The flexural modulus of the acrylic resin with incorporated 2% PTFE polymerized by long cycle was significantly higher (p<0.05) than that of the other resins. Within the limits of this study, it may be concluded that the addition of PTFE did not improve the mechanical properties of the evaluated acrylic resins.Fundação Odontológica de Ribeirão Preto2010-01-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402010000100009Brazilian Dental Journal v.21 n.1 2010reponame:Brazilian Dental Journalinstname:Fundação Odontológica de Ribeirão Preto (FUNORP)instacron:FUNORP10.1590/S0103-64402010000100009info:eu-repo/semantics/openAccessStraioto,Fabiana GouveiaRicomini Filho,Antonio PedroFernandes Neto,Alfredo JúlioDel Bel Cury,Altair Antoninhaeng2010-05-04T00:00:00Zoai:scielo:S0103-64402010000100009Revistahttps://www.scielo.br/j/bdj/https://old.scielo.br/oai/scielo-oai.phpbdj@forp.usp.br||sergio@fosjc.unesp.br1806-47600103-6440opendoar:2010-05-04T00:00Brazilian Dental Journal - Fundação Odontológica de Ribeirão Preto (FUNORP)false |
dc.title.none.fl_str_mv |
Polytetrafluorethylene added to acrylic resins: mechanical properties |
title |
Polytetrafluorethylene added to acrylic resins: mechanical properties |
spellingShingle |
Polytetrafluorethylene added to acrylic resins: mechanical properties Straioto,Fabiana Gouveia acrylic resin polytetrafluoroethylene surface hardness impact strength and flexural strength |
title_short |
Polytetrafluorethylene added to acrylic resins: mechanical properties |
title_full |
Polytetrafluorethylene added to acrylic resins: mechanical properties |
title_fullStr |
Polytetrafluorethylene added to acrylic resins: mechanical properties |
title_full_unstemmed |
Polytetrafluorethylene added to acrylic resins: mechanical properties |
title_sort |
Polytetrafluorethylene added to acrylic resins: mechanical properties |
author |
Straioto,Fabiana Gouveia |
author_facet |
Straioto,Fabiana Gouveia Ricomini Filho,Antonio Pedro Fernandes Neto,Alfredo Júlio Del Bel Cury,Altair Antoninha |
author_role |
author |
author2 |
Ricomini Filho,Antonio Pedro Fernandes Neto,Alfredo Júlio Del Bel Cury,Altair Antoninha |
author2_role |
author author author |
dc.contributor.author.fl_str_mv |
Straioto,Fabiana Gouveia Ricomini Filho,Antonio Pedro Fernandes Neto,Alfredo Júlio Del Bel Cury,Altair Antoninha |
dc.subject.por.fl_str_mv |
acrylic resin polytetrafluoroethylene surface hardness impact strength and flexural strength |
topic |
acrylic resin polytetrafluoroethylene surface hardness impact strength and flexural strength |
description |
The addition of different polymers, such as polytetrafluorethylene (PTFE), to denture base resins could be an option to modify acrylic resin mechanical properties. This study evaluated the surface hardness, impact and flexural strength, flexural modulus and peak load of 2 acrylic resins, one subjected to a long and another subjected to a short polymerization cycle, which were prepared with or without the addition of 2% PTFE. Four groups were formed according to the polymerization cycle and addition or not of PTFE. Forty specimens were prepared for each test (10 per group) with the following dimensions: hardness (30 mm diameter x 5 mm thick), impact strength (50 x 6 x 4 mm) and flexural strength (64 x 10 x 3.3 mm) test. The results of the flexural strength test allowed calculating flexural modulus and peak of load values. All tests were performed in accordance with the ISO 1567:1999 standard. Data were analyzed statistically by ANOVA and Tukey's test with the level of significance set at 5%. No statistically significant differences (p>0.05) were found for surface hardness. Flexural strength, impact strength and peak load were significantly higher (p<0.05) for resins without added PTFE. The flexural modulus of the acrylic resin with incorporated 2% PTFE polymerized by long cycle was significantly higher (p<0.05) than that of the other resins. Within the limits of this study, it may be concluded that the addition of PTFE did not improve the mechanical properties of the evaluated acrylic resins. |
publishDate |
2010 |
dc.date.none.fl_str_mv |
2010-01-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402010000100009 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402010000100009 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/S0103-64402010000100009 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
Fundação Odontológica de Ribeirão Preto |
publisher.none.fl_str_mv |
Fundação Odontológica de Ribeirão Preto |
dc.source.none.fl_str_mv |
Brazilian Dental Journal v.21 n.1 2010 reponame:Brazilian Dental Journal instname:Fundação Odontológica de Ribeirão Preto (FUNORP) instacron:FUNORP |
instname_str |
Fundação Odontológica de Ribeirão Preto (FUNORP) |
instacron_str |
FUNORP |
institution |
FUNORP |
reponame_str |
Brazilian Dental Journal |
collection |
Brazilian Dental Journal |
repository.name.fl_str_mv |
Brazilian Dental Journal - Fundação Odontológica de Ribeirão Preto (FUNORP) |
repository.mail.fl_str_mv |
bdj@forp.usp.br||sergio@fosjc.unesp.br |
_version_ |
1754204091310931968 |