Collagen cross-linking agents + dimethyl sulfoxide improving the adhesive properties of erosive lesion dentin

• Autor(a) principal: Siqueira,Fabiana Suelen Figueredo de
• Data de Publicação: 2021
• Outros Autores: Szesz,Anna Luiza, Moreira,Pedro Henrique de Aguiar, Araujo,Lucila Cristina Rodrigues, Reis,Alessandra, Cardenas,Andres Felipe Millan, Loguercio,Alessandro D.
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Brazilian Dental Journal
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-64402021000600093
• topic: Erosive tooth wear; Microtensile bond strength, Nanoleakage; Cross-linking agents, DMSO

Abstract To investigate the effect of the dimethyl sulfoxide combined with cross-linking agents on microtensile bond strength, silver nitrate penetration and in situ degree of conversion analysis of adhesives to the erosive dentin treatment with Cola-based soft drink. One hundred and sixty-six molars were assigned to 20 groups: (1) Treatment: Sound dentin; Erosive dentin; Erosive dentin treated with primer of dimethyl sulfoxide; Erosive dentin treated with DMSO primer containing proanthocyanidin and rivoflavin; (2) Adhesive systems: iBond Universal and Scotchbond Universal; and (3) adhesive strategy: etch-and-rinse or self-etch strategy. After restoration, specimens were sectioned into sticks to be tested. The data from microtensile bond strength (MPa), silver nitrate penetration (%) and in situ degree of conversion (%) were analyzed by (three- and two-factor ANOVA; Tukey's test α=5%). The application of dimethyl sulfoxide combined of not with cross-linkers improved all properties evaluated when compared to only erosive dentin treatment with Cola-based soft drink. However, only when dimethyl sulfoxide was combined to cross-linkers, the values of the microtensile bond strength, silver nitrate penetration and in situ degree of conversion in erosive dentin treatment with Cola-based soft drink was similar to sound dentin, for both adhesives and adhesive strategies. The application of dimethyl sulfoxide combined with the collagen cross-linking agent contributed to increasing the bond strength and degree of conversion in erosive lesion dentin, at the same time that significantly reduction of nanoleakage in this substrate.