Influence of chisel width on shear bond strength of composite to enamel
Autor(a) principal: | |
---|---|
Data de Publicação: | 2008 |
Outros Autores: | , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Revista odonto ciência (Online) |
Texto Completo: | https://revistaseletronicas.pucrs.br/ojs/index.php/fo/article/view/4349 |
Resumo: | Purpose: To evaluate the effect of chisel width on shear bond strength of composite to dental enamel. Methods: Sixty crowns of bovine incisors were embedded in acrylic resin, and their enamel surfaces were flattened and etched with 35% phosphoric acid. Single Bond (3M/ESPE) adhesive system and Z-250 (3M/ESPE) composite were used to build a cylindrical-shaped restoration perpendicular to the conditioned enamel flat surface. Specimens were divided into four groups and subjected to the shear bond strength testing using a chisel-shaped shearing blade with a 0.5, 1.0, 2.0, or 3.0 mm-width blunt edge in a universal testing machine at crosshead speed of 0.5 mm/min. Data on shear bond strength were analyzed by ANOVA and Duncan’s test (α=0.05). Results: Shear bond strength means for the experimental groups were: 0.5 mm – 19.66 MPa; 1 mm – 18.78 MPa; 2 mm – 16.77 MPa; 3 mm – 16.06 MPa. Bond strength was significantly different between the groups tested with chisels of 0.5 and 3 mm-width (P=0.045) showing an inverse relationship between shear bond strength and chisel width. Conclusion: The results suggest that shear bond strength varies as a function of chisel width. Key words: Dental materials; mechanical properties; shear strength |
id |
PUC_RS-22_d86d97d321ff07ff02f1d4e190711f33 |
---|---|
oai_identifier_str |
oai:ojs.revistaseletronicas.pucrs.br:article/4349 |
network_acronym_str |
PUC_RS-22 |
network_name_str |
Revista odonto ciência (Online) |
repository_id_str |
|
spelling |
Influence of chisel width on shear bond strength of composite to enamelInfluência da largura do cinzel sobre a resistência ao cisalhamento da união esmalte/resina compostaDental materialsmechanical propertiesshear strengthDental Materialsmaterials testingPurpose: To evaluate the effect of chisel width on shear bond strength of composite to dental enamel. Methods: Sixty crowns of bovine incisors were embedded in acrylic resin, and their enamel surfaces were flattened and etched with 35% phosphoric acid. Single Bond (3M/ESPE) adhesive system and Z-250 (3M/ESPE) composite were used to build a cylindrical-shaped restoration perpendicular to the conditioned enamel flat surface. Specimens were divided into four groups and subjected to the shear bond strength testing using a chisel-shaped shearing blade with a 0.5, 1.0, 2.0, or 3.0 mm-width blunt edge in a universal testing machine at crosshead speed of 0.5 mm/min. Data on shear bond strength were analyzed by ANOVA and Duncan’s test (α=0.05). Results: Shear bond strength means for the experimental groups were: 0.5 mm – 19.66 MPa; 1 mm – 18.78 MPa; 2 mm – 16.77 MPa; 3 mm – 16.06 MPa. Bond strength was significantly different between the groups tested with chisels of 0.5 and 3 mm-width (P=0.045) showing an inverse relationship between shear bond strength and chisel width. Conclusion: The results suggest that shear bond strength varies as a function of chisel width. Key words: Dental materials; mechanical properties; shear strengthObjetivo: Avaliar a influência de diferentes larguras de cinzel sobre a resistência de união ao cisalhamento na interface esmalte dental/resina composta. Metodologia: As coroas de 60 dentes incisivos bovinos foram incluídas em resina acrílica e as superfícies vestibulares de esmalte foram planificadas e condicionadas com ácido fosfórico a 35 %. O sistema adesivo Single Bond (3M/ESPE) e de resina composta Z-250 (3M/ESPE) foram utilizados para fabricar restaurações cilíndricas de resina composta perpendiculares à superfície plana do esmalte condicionado. Para o teste de cisalhamento, os espécimes foram submetidos ao ensaio mecânico com cinzéis de 0,5 mm, 1,0 mm, 2,0 mm ou 3,0 mm de largura da parte ativa romba, em uma máquina de ensaio universal à velocidade de 0,5 mm/min. Os dados obtidos foram analisados por análise de variância e teste de Duncan ao nível de significância de 5 %. Resultados: As médias de resistência de união ao cisalhamento dos grupos testados foram: 0,5 mm – 19,66 MPa; 1,0 mm – 18,78 MPa; 2,0 mm – 16,77 MPa; 3,0 mm –16,06 MPa. Houve diferença estatisticamente significativa entre os grupos de 0,5 e 3,0 mm (P=0,045), com uma relação inversa entre resistência de união ao cisalhamento e largura do cinzel. Conclusão: Os resultados sugerem que a resistência de união ao cisalhamento sofre influência da largura do cinzel utilizado no ensaio. Palavras-chave: Materiais dentários; propriedades mecânicas; cisalhamentoEDIPUCRS - Editora Universitária da PUCRS2008-12-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionPeer-reviewed Articlelaboratotyapplication/pdfhttps://revistaseletronicas.pucrs.br/ojs/index.php/fo/article/view/4349Revista Odonto Ciência; Vol. 24 No. 1 (2009); 19 - 21Revista Odonto Ciência; v. 24 n. 1 (2009); 19 - 211980-65230102-9460reponame:Revista odonto ciência (Online)instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSenghttps://revistaseletronicas.pucrs.br/ojs/index.php/fo/article/view/4349/3662Oliveira, Antônio Carlos CastellanOshima, Hugo Mitsuo SilvaMota, Eduardo GonçalvesGrossi, Márcio Limainfo:eu-repo/semantics/openAccess2013-11-11T13:23:39Zoai:ojs.revistaseletronicas.pucrs.br:article/4349Revistahttps://revistaseletronicas.pucrs.br/ojs/index.php/foPRIhttps://revistaseletronicas.pucrs.br/ojs/index.php/fo/oai||odontociencia@pucrs.br1980-65230102-9460opendoar:2013-11-11T13:23:39Revista odonto ciência (Online) - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false |
dc.title.none.fl_str_mv |
Influence of chisel width on shear bond strength of composite to enamel Influência da largura do cinzel sobre a resistência ao cisalhamento da união esmalte/resina composta |
title |
Influence of chisel width on shear bond strength of composite to enamel |
spellingShingle |
Influence of chisel width on shear bond strength of composite to enamel Oliveira, Antônio Carlos Castellan Dental materials mechanical properties shear strength Dental Materials materials testing |
title_short |
Influence of chisel width on shear bond strength of composite to enamel |
title_full |
Influence of chisel width on shear bond strength of composite to enamel |
title_fullStr |
Influence of chisel width on shear bond strength of composite to enamel |
title_full_unstemmed |
Influence of chisel width on shear bond strength of composite to enamel |
title_sort |
Influence of chisel width on shear bond strength of composite to enamel |
author |
Oliveira, Antônio Carlos Castellan |
author_facet |
Oliveira, Antônio Carlos Castellan Oshima, Hugo Mitsuo Silva Mota, Eduardo Gonçalves Grossi, Márcio Lima |
author_role |
author |
author2 |
Oshima, Hugo Mitsuo Silva Mota, Eduardo Gonçalves Grossi, Márcio Lima |
author2_role |
author author author |
dc.contributor.author.fl_str_mv |
Oliveira, Antônio Carlos Castellan Oshima, Hugo Mitsuo Silva Mota, Eduardo Gonçalves Grossi, Márcio Lima |
dc.subject.por.fl_str_mv |
Dental materials mechanical properties shear strength Dental Materials materials testing |
topic |
Dental materials mechanical properties shear strength Dental Materials materials testing |
description |
Purpose: To evaluate the effect of chisel width on shear bond strength of composite to dental enamel. Methods: Sixty crowns of bovine incisors were embedded in acrylic resin, and their enamel surfaces were flattened and etched with 35% phosphoric acid. Single Bond (3M/ESPE) adhesive system and Z-250 (3M/ESPE) composite were used to build a cylindrical-shaped restoration perpendicular to the conditioned enamel flat surface. Specimens were divided into four groups and subjected to the shear bond strength testing using a chisel-shaped shearing blade with a 0.5, 1.0, 2.0, or 3.0 mm-width blunt edge in a universal testing machine at crosshead speed of 0.5 mm/min. Data on shear bond strength were analyzed by ANOVA and Duncan’s test (α=0.05). Results: Shear bond strength means for the experimental groups were: 0.5 mm – 19.66 MPa; 1 mm – 18.78 MPa; 2 mm – 16.77 MPa; 3 mm – 16.06 MPa. Bond strength was significantly different between the groups tested with chisels of 0.5 and 3 mm-width (P=0.045) showing an inverse relationship between shear bond strength and chisel width. Conclusion: The results suggest that shear bond strength varies as a function of chisel width. Key words: Dental materials; mechanical properties; shear strength |
publishDate |
2008 |
dc.date.none.fl_str_mv |
2008-12-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion Peer-reviewed Article laboratoty |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
https://revistaseletronicas.pucrs.br/ojs/index.php/fo/article/view/4349 |
url |
https://revistaseletronicas.pucrs.br/ojs/index.php/fo/article/view/4349 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
https://revistaseletronicas.pucrs.br/ojs/index.php/fo/article/view/4349/3662 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
EDIPUCRS - Editora Universitária da PUCRS |
publisher.none.fl_str_mv |
EDIPUCRS - Editora Universitária da PUCRS |
dc.source.none.fl_str_mv |
Revista Odonto Ciência; Vol. 24 No. 1 (2009); 19 - 21 Revista Odonto Ciência; v. 24 n. 1 (2009); 19 - 21 1980-6523 0102-9460 reponame:Revista odonto ciência (Online) instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) instacron:PUC_RS |
instname_str |
Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
instacron_str |
PUC_RS |
institution |
PUC_RS |
reponame_str |
Revista odonto ciência (Online) |
collection |
Revista odonto ciência (Online) |
repository.name.fl_str_mv |
Revista odonto ciência (Online) - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
repository.mail.fl_str_mv |
||odontociencia@pucrs.br |
_version_ |
1754820874774511616 |