Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM

Detalhes bibliográficos
Autor(a) principal: Costa, Heloísa
Data de Publicação: 2016
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da PUC_RS
Texto Completo: http://tede2.pucrs.br/tede2/handle/tede/6870
Resumo: Aims: to evaluate the microtensile bond strength of an adhesive (Signum Ceramic Bond (Heraeus / Kulzer) made for repairing fractured CAD/CAM ceramics after different surface treatments. Materials and Methods: Three different types of ceramic blocks for CAD / CAM were used: Mark II, Empress CAD and e.max CAD. The ceramics were divided into four subgroups according to the following surface treatment: G1: roughening with specific drill (ASP, Signum) + adhesive system; G2: hydrofluoric acid (HF) 5% + Signum, G3: ASP + 5% + AF Signum, G4: ASP + AF 10% + Signum. After the adhesive system application, a 6.0 mm resin composite block (Charisma) was made for the microtensile test. After 15 days of storage in distilled water, the blocks were cut and selected 20 sticks with cross sectional area of 1.0 mm2. The specimens were submitted to microtensile in a universal testing machine. Results: The use of ASP + AF 10% promoted the highest bond strength values in the ceramic Mark II (23.08 MPa) and Empress CAD (29.36 MPa). In e.max CAD, the use of ASP + AF 5% led to the highest values of bond strength (25.19 MPa). Based on these results we conclude that the adhesion of the adhesive system Signum for ceramics repairing depends on surface treatment being the association abrasion + hydrofluoric acid the most suitable.
id P_RS_2d0734932659f34ee187d9d2a16e7d34
oai_identifier_str oai:tede2.pucrs.br:tede/6870
network_acronym_str P_RS
network_name_str Biblioteca Digital de Teses e Dissertações da PUC_RS
repository_id_str
spelling Burnett Junior, Luiz Henrique670.150.690-91http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4778680J0Burnett Junior, Luiz Henrique833.745.820-87http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4216135E3Costa, Heloísa2016-08-01T16:58:26Z2016-02-29http://tede2.pucrs.br/tede2/handle/tede/6870Aims: to evaluate the microtensile bond strength of an adhesive (Signum Ceramic Bond (Heraeus / Kulzer) made for repairing fractured CAD/CAM ceramics after different surface treatments. Materials and Methods: Three different types of ceramic blocks for CAD / CAM were used: Mark II, Empress CAD and e.max CAD. The ceramics were divided into four subgroups according to the following surface treatment: G1: roughening with specific drill (ASP, Signum) + adhesive system; G2: hydrofluoric acid (HF) 5% + Signum, G3: ASP + 5% + AF Signum, G4: ASP + AF 10% + Signum. After the adhesive system application, a 6.0 mm resin composite block (Charisma) was made for the microtensile test. After 15 days of storage in distilled water, the blocks were cut and selected 20 sticks with cross sectional area of 1.0 mm2. The specimens were submitted to microtensile in a universal testing machine. Results: The use of ASP + AF 10% promoted the highest bond strength values in the ceramic Mark II (23.08 MPa) and Empress CAD (29.36 MPa). In e.max CAD, the use of ASP + AF 5% led to the highest values of bond strength (25.19 MPa). Based on these results we conclude that the adhesion of the adhesive system Signum for ceramics repairing depends on surface treatment being the association abrasion + hydrofluoric acid the most suitable.Objetivos: Esse estudo teve por objetivo avaliar, in vitro, a influência do tratamento de superfície de cerâmicas para CAD/CAM na resistência de união do adesivo Signum Ceramic Bond (Heraeus/Kulzer) utilizado para reparo de cerâmicas fraturadas. Materiais e Métodos: três diferentes tipos de blocos de cerâmica para CAD/CAM foram utilizados: Mark II, Empress CAD e e.Max CAD. As cerâmicas foram divididas em 4 subgrupos de acordo com o tratamento de superfície empregado: G1: asperização com broca específica (ASP, Signum) + sistema adesivo; G2: ácido fluorídrico (AF) 5% + Signum, G3: ASP + AF 5% + Signum, G4: ASP + AF 10% + Signum. Após a aplicação do sistema adesivo, um bloco de resina composta (Charisma) foi confeccionado para o ensaio de microtração. Após 15 dias de armazenamento em água destilada, os blocos foram seccionados e selecionados 20 palitos com área adesiva de aproximadamente 1,0 mm2. Os corpos de prova foram submetidos ao ensaio de microtração em uma máquina de ensaios universal. Resultados: O uso da ASP + AF 10% promoveu os maiores valores de resistência adesiva nas cerâmicas Mark II (23,08 MPa) e Empress CAD (29,36 MPa). No e.max CAD, o uso da ASP + AF 5% propiciou os maiores valores de resistência adesiva (25,19 MPa). Com base nos resultados encontrados é possível concluir que a adesão do sistema adesivo Signum para reparo de cerâmicas para CAD/CAM depende do tratamento de superfície empregado sendo que a associação abrasão + ácido fluorídrico é a mais indicada.Submitted by Setor de Tratamento da Informação - BC/PUCRS (tede2@pucrs.br) on 2016-08-01T16:58:26Z No. of bitstreams: 1 DIS_HELOISA_COSTA_PARCIAL.pdf: 121948 bytes, checksum: b60caab299692040c6bbd09f4274ab38 (MD5)Made available in DSpace on 2016-08-01T16:58:26Z (GMT). No. of bitstreams: 1 DIS_HELOISA_COSTA_PARCIAL.pdf: 121948 bytes, checksum: b60caab299692040c6bbd09f4274ab38 (MD5) Previous issue date: 2016-02-29Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/165872/DIS_HELOISA_COSTA_PARCIAL.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em OdontologiaPUCRSBrasilFaculdade de OdontologiaCERÂMICA DENTÁRIAADESIVOS DENTÁRIOSRESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA)ODONTOLOGIACIENCIAS DA SAUDE::ODONTOLOGIAInfluência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAMinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-80965548187336651646006006006004673435736271820140-20704984698792443492075167498588264571info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSTHUMBNAILDIS_HELOISA_COSTA_PARCIAL.pdf.jpgDIS_HELOISA_COSTA_PARCIAL.pdf.jpgimage/jpeg3474http://tede2.pucrs.br/tede2/bitstream/tede/6870/5/DIS_HELOISA_COSTA_PARCIAL.pdf.jpg61dbc0b5ff094a31ea08e47054185ac8MD55TEXTDIS_HELOISA_COSTA_PARCIAL.pdf.txtDIS_HELOISA_COSTA_PARCIAL.pdf.txttext/plain14448http://tede2.pucrs.br/tede2/bitstream/tede/6870/4/DIS_HELOISA_COSTA_PARCIAL.pdf.txt39282efdc7e5525a932daea2eff86e77MD54LICENSElicense.txtlicense.txttext/plain; charset=utf-8610http://tede2.pucrs.br/tede2/bitstream/tede/6870/3/license.txt5a9d6006225b368ef605ba16b4f6d1beMD53ORIGINALDIS_HELOISA_COSTA_PARCIAL.pdfDIS_HELOISA_COSTA_PARCIAL.pdfapplication/pdf121948http://tede2.pucrs.br/tede2/bitstream/tede/6870/2/DIS_HELOISA_COSTA_PARCIAL.pdfb60caab299692040c6bbd09f4274ab38MD52tede/68702016-08-01 20:00:28.987oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2016-08-01T23:00:28Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false
dc.title.por.fl_str_mv Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM
title Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM
spellingShingle Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM
Costa, Heloísa
CERÂMICA DENTÁRIA
ADESIVOS DENTÁRIOS
RESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA)
ODONTOLOGIA
CIENCIAS DA SAUDE::ODONTOLOGIA
title_short Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM
title_full Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM
title_fullStr Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM
title_full_unstemmed Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM
title_sort Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM
author Costa, Heloísa
author_facet Costa, Heloísa
author_role author
dc.contributor.advisor2ID.por.fl_str_mv Burnett Junior, Luiz Henrique
dc.contributor.advisor1.fl_str_mv Burnett Junior, Luiz Henrique
dc.contributor.advisor1ID.fl_str_mv 670.150.690-91
dc.contributor.advisor1Lattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4778680J0
dc.contributor.authorID.fl_str_mv 833.745.820-87
dc.contributor.authorLattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4216135E3
dc.contributor.author.fl_str_mv Costa, Heloísa
contributor_str_mv Burnett Junior, Luiz Henrique
dc.subject.por.fl_str_mv CERÂMICA DENTÁRIA
ADESIVOS DENTÁRIOS
RESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA)
ODONTOLOGIA
topic CERÂMICA DENTÁRIA
ADESIVOS DENTÁRIOS
RESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA)
ODONTOLOGIA
CIENCIAS DA SAUDE::ODONTOLOGIA
dc.subject.cnpq.fl_str_mv CIENCIAS DA SAUDE::ODONTOLOGIA
description Aims: to evaluate the microtensile bond strength of an adhesive (Signum Ceramic Bond (Heraeus / Kulzer) made for repairing fractured CAD/CAM ceramics after different surface treatments. Materials and Methods: Three different types of ceramic blocks for CAD / CAM were used: Mark II, Empress CAD and e.max CAD. The ceramics were divided into four subgroups according to the following surface treatment: G1: roughening with specific drill (ASP, Signum) + adhesive system; G2: hydrofluoric acid (HF) 5% + Signum, G3: ASP + 5% + AF Signum, G4: ASP + AF 10% + Signum. After the adhesive system application, a 6.0 mm resin composite block (Charisma) was made for the microtensile test. After 15 days of storage in distilled water, the blocks were cut and selected 20 sticks with cross sectional area of 1.0 mm2. The specimens were submitted to microtensile in a universal testing machine. Results: The use of ASP + AF 10% promoted the highest bond strength values in the ceramic Mark II (23.08 MPa) and Empress CAD (29.36 MPa). In e.max CAD, the use of ASP + AF 5% led to the highest values of bond strength (25.19 MPa). Based on these results we conclude that the adhesion of the adhesive system Signum for ceramics repairing depends on surface treatment being the association abrasion + hydrofluoric acid the most suitable.
publishDate 2016
dc.date.accessioned.fl_str_mv 2016-08-01T16:58:26Z
dc.date.issued.fl_str_mv 2016-02-29
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://tede2.pucrs.br/tede2/handle/tede/6870
url http://tede2.pucrs.br/tede2/handle/tede/6870
dc.language.iso.fl_str_mv por
language por
dc.relation.program.fl_str_mv -8096554818733665164
dc.relation.confidence.fl_str_mv 600
600
600
600
dc.relation.department.fl_str_mv 4673435736271820140
dc.relation.cnpq.fl_str_mv -2070498469879244349
dc.relation.sponsorship.fl_str_mv 2075167498588264571
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.publisher.none.fl_str_mv Pontifícia Universidade Católica do Rio Grande do Sul
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Odontologia
dc.publisher.initials.fl_str_mv PUCRS
dc.publisher.country.fl_str_mv Brasil
dc.publisher.department.fl_str_mv Faculdade de Odontologia
publisher.none.fl_str_mv Pontifícia Universidade Católica do Rio Grande do Sul
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS
instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
instacron:PUC_RS
instname_str Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
instacron_str PUC_RS
institution PUC_RS
reponame_str Biblioteca Digital de Teses e Dissertações da PUC_RS
collection Biblioteca Digital de Teses e Dissertações da PUC_RS
bitstream.url.fl_str_mv http://tede2.pucrs.br/tede2/bitstream/tede/6870/5/DIS_HELOISA_COSTA_PARCIAL.pdf.jpg
http://tede2.pucrs.br/tede2/bitstream/tede/6870/4/DIS_HELOISA_COSTA_PARCIAL.pdf.txt
http://tede2.pucrs.br/tede2/bitstream/tede/6870/3/license.txt
http://tede2.pucrs.br/tede2/bitstream/tede/6870/2/DIS_HELOISA_COSTA_PARCIAL.pdf
bitstream.checksum.fl_str_mv 61dbc0b5ff094a31ea08e47054185ac8
39282efdc7e5525a932daea2eff86e77
5a9d6006225b368ef605ba16b4f6d1be
b60caab299692040c6bbd09f4274ab38
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
MD5
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
repository.mail.fl_str_mv biblioteca.central@pucrs.br||
_version_ 1799765321040527360

Registros relacionados