Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM
Autor(a) principal: | |
---|---|
Data de Publicação: | 2016 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da PUC_RS |
Texto Completo: | http://tede2.pucrs.br/tede2/handle/tede/6870 |
Resumo: | Aims: to evaluate the microtensile bond strength of an adhesive (Signum Ceramic Bond (Heraeus / Kulzer) made for repairing fractured CAD/CAM ceramics after different surface treatments. Materials and Methods: Three different types of ceramic blocks for CAD / CAM were used: Mark II, Empress CAD and e.max CAD. The ceramics were divided into four subgroups according to the following surface treatment: G1: roughening with specific drill (ASP, Signum) + adhesive system; G2: hydrofluoric acid (HF) 5% + Signum, G3: ASP + 5% + AF Signum, G4: ASP + AF 10% + Signum. After the adhesive system application, a 6.0 mm resin composite block (Charisma) was made for the microtensile test. After 15 days of storage in distilled water, the blocks were cut and selected 20 sticks with cross sectional area of 1.0 mm2. The specimens were submitted to microtensile in a universal testing machine. Results: The use of ASP + AF 10% promoted the highest bond strength values in the ceramic Mark II (23.08 MPa) and Empress CAD (29.36 MPa). In e.max CAD, the use of ASP + AF 5% led to the highest values of bond strength (25.19 MPa). Based on these results we conclude that the adhesion of the adhesive system Signum for ceramics repairing depends on surface treatment being the association abrasion + hydrofluoric acid the most suitable. |
id |
P_RS_2d0734932659f34ee187d9d2a16e7d34 |
---|---|
oai_identifier_str |
oai:tede2.pucrs.br:tede/6870 |
network_acronym_str |
P_RS |
network_name_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
repository_id_str |
|
spelling |
Burnett Junior, Luiz Henrique670.150.690-91http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4778680J0Burnett Junior, Luiz Henrique833.745.820-87http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4216135E3Costa, Heloísa2016-08-01T16:58:26Z2016-02-29http://tede2.pucrs.br/tede2/handle/tede/6870Aims: to evaluate the microtensile bond strength of an adhesive (Signum Ceramic Bond (Heraeus / Kulzer) made for repairing fractured CAD/CAM ceramics after different surface treatments. Materials and Methods: Three different types of ceramic blocks for CAD / CAM were used: Mark II, Empress CAD and e.max CAD. The ceramics were divided into four subgroups according to the following surface treatment: G1: roughening with specific drill (ASP, Signum) + adhesive system; G2: hydrofluoric acid (HF) 5% + Signum, G3: ASP + 5% + AF Signum, G4: ASP + AF 10% + Signum. After the adhesive system application, a 6.0 mm resin composite block (Charisma) was made for the microtensile test. After 15 days of storage in distilled water, the blocks were cut and selected 20 sticks with cross sectional area of 1.0 mm2. The specimens were submitted to microtensile in a universal testing machine. Results: The use of ASP + AF 10% promoted the highest bond strength values in the ceramic Mark II (23.08 MPa) and Empress CAD (29.36 MPa). In e.max CAD, the use of ASP + AF 5% led to the highest values of bond strength (25.19 MPa). Based on these results we conclude that the adhesion of the adhesive system Signum for ceramics repairing depends on surface treatment being the association abrasion + hydrofluoric acid the most suitable.Objetivos: Esse estudo teve por objetivo avaliar, in vitro, a influência do tratamento de superfície de cerâmicas para CAD/CAM na resistência de união do adesivo Signum Ceramic Bond (Heraeus/Kulzer) utilizado para reparo de cerâmicas fraturadas. Materiais e Métodos: três diferentes tipos de blocos de cerâmica para CAD/CAM foram utilizados: Mark II, Empress CAD e e.Max CAD. As cerâmicas foram divididas em 4 subgrupos de acordo com o tratamento de superfície empregado: G1: asperização com broca específica (ASP, Signum) + sistema adesivo; G2: ácido fluorídrico (AF) 5% + Signum, G3: ASP + AF 5% + Signum, G4: ASP + AF 10% + Signum. Após a aplicação do sistema adesivo, um bloco de resina composta (Charisma) foi confeccionado para o ensaio de microtração. Após 15 dias de armazenamento em água destilada, os blocos foram seccionados e selecionados 20 palitos com área adesiva de aproximadamente 1,0 mm2. Os corpos de prova foram submetidos ao ensaio de microtração em uma máquina de ensaios universal. Resultados: O uso da ASP + AF 10% promoveu os maiores valores de resistência adesiva nas cerâmicas Mark II (23,08 MPa) e Empress CAD (29,36 MPa). No e.max CAD, o uso da ASP + AF 5% propiciou os maiores valores de resistência adesiva (25,19 MPa). Com base nos resultados encontrados é possível concluir que a adesão do sistema adesivo Signum para reparo de cerâmicas para CAD/CAM depende do tratamento de superfície empregado sendo que a associação abrasão + ácido fluorídrico é a mais indicada.Submitted by Setor de Tratamento da Informação - BC/PUCRS (tede2@pucrs.br) on 2016-08-01T16:58:26Z No. of bitstreams: 1 DIS_HELOISA_COSTA_PARCIAL.pdf: 121948 bytes, checksum: b60caab299692040c6bbd09f4274ab38 (MD5)Made available in DSpace on 2016-08-01T16:58:26Z (GMT). No. of bitstreams: 1 DIS_HELOISA_COSTA_PARCIAL.pdf: 121948 bytes, checksum: b60caab299692040c6bbd09f4274ab38 (MD5) Previous issue date: 2016-02-29Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/165872/DIS_HELOISA_COSTA_PARCIAL.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em OdontologiaPUCRSBrasilFaculdade de OdontologiaCERÂMICA DENTÁRIAADESIVOS DENTÁRIOSRESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA)ODONTOLOGIACIENCIAS DA SAUDE::ODONTOLOGIAInfluência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAMinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-80965548187336651646006006006004673435736271820140-20704984698792443492075167498588264571info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSTHUMBNAILDIS_HELOISA_COSTA_PARCIAL.pdf.jpgDIS_HELOISA_COSTA_PARCIAL.pdf.jpgimage/jpeg3474http://tede2.pucrs.br/tede2/bitstream/tede/6870/5/DIS_HELOISA_COSTA_PARCIAL.pdf.jpg61dbc0b5ff094a31ea08e47054185ac8MD55TEXTDIS_HELOISA_COSTA_PARCIAL.pdf.txtDIS_HELOISA_COSTA_PARCIAL.pdf.txttext/plain14448http://tede2.pucrs.br/tede2/bitstream/tede/6870/4/DIS_HELOISA_COSTA_PARCIAL.pdf.txt39282efdc7e5525a932daea2eff86e77MD54LICENSElicense.txtlicense.txttext/plain; charset=utf-8610http://tede2.pucrs.br/tede2/bitstream/tede/6870/3/license.txt5a9d6006225b368ef605ba16b4f6d1beMD53ORIGINALDIS_HELOISA_COSTA_PARCIAL.pdfDIS_HELOISA_COSTA_PARCIAL.pdfapplication/pdf121948http://tede2.pucrs.br/tede2/bitstream/tede/6870/2/DIS_HELOISA_COSTA_PARCIAL.pdfb60caab299692040c6bbd09f4274ab38MD52tede/68702016-08-01 20:00:28.987oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2016-08-01T23:00:28Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false |
dc.title.por.fl_str_mv |
Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM |
title |
Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM |
spellingShingle |
Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM Costa, Heloísa CERÂMICA DENTÁRIA ADESIVOS DENTÁRIOS RESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA) ODONTOLOGIA CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM |
title_full |
Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM |
title_fullStr |
Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM |
title_full_unstemmed |
Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM |
title_sort |
Influência do tempo de condicionamento e concentração do ácido fluorídrico na resistência de união de um sistema adesivo à superfície de cerâmicas para CAD/CAM |
author |
Costa, Heloísa |
author_facet |
Costa, Heloísa |
author_role |
author |
dc.contributor.advisor2ID.por.fl_str_mv |
Burnett Junior, Luiz Henrique |
dc.contributor.advisor1.fl_str_mv |
Burnett Junior, Luiz Henrique |
dc.contributor.advisor1ID.fl_str_mv |
670.150.690-91 |
dc.contributor.advisor1Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4778680J0 |
dc.contributor.authorID.fl_str_mv |
833.745.820-87 |
dc.contributor.authorLattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4216135E3 |
dc.contributor.author.fl_str_mv |
Costa, Heloísa |
contributor_str_mv |
Burnett Junior, Luiz Henrique |
dc.subject.por.fl_str_mv |
CERÂMICA DENTÁRIA ADESIVOS DENTÁRIOS RESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA) ODONTOLOGIA |
topic |
CERÂMICA DENTÁRIA ADESIVOS DENTÁRIOS RESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA) ODONTOLOGIA CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.cnpq.fl_str_mv |
CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
Aims: to evaluate the microtensile bond strength of an adhesive (Signum Ceramic Bond (Heraeus / Kulzer) made for repairing fractured CAD/CAM ceramics after different surface treatments. Materials and Methods: Three different types of ceramic blocks for CAD / CAM were used: Mark II, Empress CAD and e.max CAD. The ceramics were divided into four subgroups according to the following surface treatment: G1: roughening with specific drill (ASP, Signum) + adhesive system; G2: hydrofluoric acid (HF) 5% + Signum, G3: ASP + 5% + AF Signum, G4: ASP + AF 10% + Signum. After the adhesive system application, a 6.0 mm resin composite block (Charisma) was made for the microtensile test. After 15 days of storage in distilled water, the blocks were cut and selected 20 sticks with cross sectional area of 1.0 mm2. The specimens were submitted to microtensile in a universal testing machine. Results: The use of ASP + AF 10% promoted the highest bond strength values in the ceramic Mark II (23.08 MPa) and Empress CAD (29.36 MPa). In e.max CAD, the use of ASP + AF 5% led to the highest values of bond strength (25.19 MPa). Based on these results we conclude that the adhesion of the adhesive system Signum for ceramics repairing depends on surface treatment being the association abrasion + hydrofluoric acid the most suitable. |
publishDate |
2016 |
dc.date.accessioned.fl_str_mv |
2016-08-01T16:58:26Z |
dc.date.issued.fl_str_mv |
2016-02-29 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://tede2.pucrs.br/tede2/handle/tede/6870 |
url |
http://tede2.pucrs.br/tede2/handle/tede/6870 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-8096554818733665164 |
dc.relation.confidence.fl_str_mv |
600 600 600 600 |
dc.relation.department.fl_str_mv |
4673435736271820140 |
dc.relation.cnpq.fl_str_mv |
-2070498469879244349 |
dc.relation.sponsorship.fl_str_mv |
2075167498588264571 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Odontologia |
dc.publisher.initials.fl_str_mv |
PUCRS |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Faculdade de Odontologia |
publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) instacron:PUC_RS |
instname_str |
Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
instacron_str |
PUC_RS |
institution |
PUC_RS |
reponame_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
collection |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
bitstream.url.fl_str_mv |
http://tede2.pucrs.br/tede2/bitstream/tede/6870/5/DIS_HELOISA_COSTA_PARCIAL.pdf.jpg http://tede2.pucrs.br/tede2/bitstream/tede/6870/4/DIS_HELOISA_COSTA_PARCIAL.pdf.txt http://tede2.pucrs.br/tede2/bitstream/tede/6870/3/license.txt http://tede2.pucrs.br/tede2/bitstream/tede/6870/2/DIS_HELOISA_COSTA_PARCIAL.pdf |
bitstream.checksum.fl_str_mv |
61dbc0b5ff094a31ea08e47054185ac8 39282efdc7e5525a932daea2eff86e77 5a9d6006225b368ef605ba16b4f6d1be b60caab299692040c6bbd09f4274ab38 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
repository.mail.fl_str_mv |
biblioteca.central@pucrs.br|| |
_version_ |
1799765321040527360 |