Desenvolvimento do campo retrodifusor seletivo de alumínio e boro em células solares de silício

Detalhes bibliográficos
Autor(a) principal: Crestani, Thais
Data de Publicação: 2016
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da PUC_RS
Texto Completo: http://tede2.pucrs.br/tede2/handle/tede/6985
Resumo: The typical solar cells of the industry are fabricated in p-type crystalline silicon wafers and have a pn junction at one side and, on the other side, the back surface field (BSF). The objective of this work is to develop solar cells with aluminum and boron selective back surface field to enable the passivation on the rear face with an industrial process. Czochralski p-type silicon wafers of solar grade quality were used. The boron diffusion was performed on the whole back side of the silicon wafers and the aluminum was screen-printed to form the selective back surface field under the metal grid. The boron diffusion temperature and time, the firing temperature of the metal pastes, the percentage of the rear area covered with aluminum and the passivation with SiO2 were evaluated in the electrical parameters. The best boron diffusion temperature was 970 ° C for 20 minutes and firing temperature of the metal pastes was 870 ° C. The solar cell with the highest efficiency were obtained for a rear metal grid with 14 % of the area covered by aluminum. The passivation by SiO2 on both surfaces increased the minority charge carrier diffusion length from 490 μm to 665 μm. Consequently, the passivation increased the efficiency from 15.6 % to 16.1 %, as a result of an increasing of the fill factor and the open circuit voltage. The passivation also increased the internal quantum efficiency in the range of violet/blue wavelengths as well as in the near infrared region.
id P_RS_3e895b4c241d97215247dbb51eae68c1
oai_identifier_str oai:tede2.pucrs.br:tede/6985
network_acronym_str P_RS
network_name_str Biblioteca Digital de Teses e Dissertações da PUC_RS
repository_id_str
spelling Zanesco, Izete469.034.370-53http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4787917H3Moehlecke, Adrianohttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4787919H0013.725.520-90http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K8783497T7Crestani, Thais2016-10-06T11:11:46Z2016-07-07http://tede2.pucrs.br/tede2/handle/tede/6985The typical solar cells of the industry are fabricated in p-type crystalline silicon wafers and have a pn junction at one side and, on the other side, the back surface field (BSF). The objective of this work is to develop solar cells with aluminum and boron selective back surface field to enable the passivation on the rear face with an industrial process. Czochralski p-type silicon wafers of solar grade quality were used. The boron diffusion was performed on the whole back side of the silicon wafers and the aluminum was screen-printed to form the selective back surface field under the metal grid. The boron diffusion temperature and time, the firing temperature of the metal pastes, the percentage of the rear area covered with aluminum and the passivation with SiO2 were evaluated in the electrical parameters. The best boron diffusion temperature was 970 ° C for 20 minutes and firing temperature of the metal pastes was 870 ° C. The solar cell with the highest efficiency were obtained for a rear metal grid with 14 % of the area covered by aluminum. The passivation by SiO2 on both surfaces increased the minority charge carrier diffusion length from 490 μm to 665 μm. Consequently, the passivation increased the efficiency from 15.6 % to 16.1 %, as a result of an increasing of the fill factor and the open circuit voltage. The passivation also increased the internal quantum efficiency in the range of violet/blue wavelengths as well as in the near infrared region.As células solares típicas da indústria são fabricadas em silício cristalino tipo p e possuem uma junção pn em uma das faces, e na outra face, é formado o campo retrodifusor. O objetivo deste trabalho foi desenvolver células solares com o campo retrodifusor seletivo de alumínio e boro para possibilitar a passivação na face posterior, com processo industrial. Foram utilizadas lâminas de silício Czochralski tipo p, grau solar. A difusão de boro foi realizada em toda a face posterior da lâmina de silício e por serigrafia foi depositada a pasta de alumínio para formar o campo retrodifusor seletivo nas trilhas metálicas. Avaliou-se influência da temperatura e do tempo de difusão de boro, a temperatura de queima das pastas metálicas, o percentual da área posterior recoberta por alumínio e a passivação com SiO2 nos parâmetros elétricos. A melhor temperatura de difusão de boro foi de 970 °C durante 20 minutos e a temperatura de queima das pastas metálicas foi de 870 °C. A célula com maior eficiência foi obtida com a malha posterior com área de recobrimento de alumínio de 14%. A passivação com SiO2 em ambas as superfícies aumentou a eficiência e o comprimento de difusão dos portadores de carga minoritária aumentou de 490 μm para 665 μm. Com a passivação, a eficiência aumentou de 15,6 % para 16,1 %, devido ao aumento do fator de forma e da tensão de circuito aberto. A passivação também aumentou a eficiência quântica interna no intervalo de comprimento de onda do violeta/azul bem como na região do infravermelho próximo.Submitted by Setor de Tratamento da Informação - BC/PUCRS (tede2@pucrs.br) on 2016-10-06T11:11:45Z No. of bitstreams: 1 DIS_THAIS_CRESTANI_COMPLETO.pdf: 3613694 bytes, checksum: 40503ab7961f50b87d67545be969f402 (MD5)Made available in DSpace on 2016-10-06T11:11:46Z (GMT). No. of bitstreams: 1 DIS_THAIS_CRESTANI_COMPLETO.pdf: 3613694 bytes, checksum: 40503ab7961f50b87d67545be969f402 (MD5) Previous issue date: 2016-07-07application/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/166388/DIS_THAIS_CRESTANI_COMPLETO.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em Engenharia e Tecnologia de MateriaisPUCRSBrasilFaculdade de EngenhariaCÉLULAS SOLARESSILÍCIOENGENHARIAENGENHARIASDesenvolvimento do campo retrodifusor seletivo de alumínio e boro em células solares de silícioDevelopment of the selective back surface field of aluminium and boron in silicon solar cellsinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-7432719344215120122600600600-6557705727614397854518971056484826825info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSTHUMBNAILDIS_THAIS_CRESTANI_COMPLETO.pdf.jpgDIS_THAIS_CRESTANI_COMPLETO.pdf.jpgimage/jpeg3947http://tede2.pucrs.br/tede2/bitstream/tede/6985/5/DIS_THAIS_CRESTANI_COMPLETO.pdf.jpg06fbac9bdabbb222df0f073b987b23a7MD55TEXTDIS_THAIS_CRESTANI_COMPLETO.pdf.txtDIS_THAIS_CRESTANI_COMPLETO.pdf.txttext/plain201248http://tede2.pucrs.br/tede2/bitstream/tede/6985/4/DIS_THAIS_CRESTANI_COMPLETO.pdf.txt1cadc55eae0496ddc8659244ecd13c91MD54LICENSElicense.txtlicense.txttext/plain; charset=utf-8610http://tede2.pucrs.br/tede2/bitstream/tede/6985/3/license.txt5a9d6006225b368ef605ba16b4f6d1beMD53ORIGINALDIS_THAIS_CRESTANI_COMPLETO.pdfDIS_THAIS_CRESTANI_COMPLETO.pdfapplication/pdf3613694http://tede2.pucrs.br/tede2/bitstream/tede/6985/2/DIS_THAIS_CRESTANI_COMPLETO.pdf40503ab7961f50b87d67545be969f402MD52tede/69852016-10-06 20:00:59.284oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2016-10-06T23:00:59Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false
dc.title.por.fl_str_mv Desenvolvimento do campo retrodifusor seletivo de alumínio e boro em células solares de silício
dc.title.alternative.eng.fl_str_mv Development of the selective back surface field of aluminium and boron in silicon solar cells
title Desenvolvimento do campo retrodifusor seletivo de alumínio e boro em células solares de silício
spellingShingle Desenvolvimento do campo retrodifusor seletivo de alumínio e boro em células solares de silício
Crestani, Thais
CÉLULAS SOLARES
SILÍCIO
ENGENHARIA
ENGENHARIAS
title_short Desenvolvimento do campo retrodifusor seletivo de alumínio e boro em células solares de silício
title_full Desenvolvimento do campo retrodifusor seletivo de alumínio e boro em células solares de silício
title_fullStr Desenvolvimento do campo retrodifusor seletivo de alumínio e boro em células solares de silício
title_full_unstemmed Desenvolvimento do campo retrodifusor seletivo de alumínio e boro em células solares de silício
title_sort Desenvolvimento do campo retrodifusor seletivo de alumínio e boro em células solares de silício
author Crestani, Thais
author_facet Crestani, Thais
author_role author
dc.contributor.advisor1.fl_str_mv Zanesco, Izete
dc.contributor.advisor1ID.fl_str_mv 469.034.370-53
dc.contributor.advisor1Lattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4787917H3
dc.contributor.advisor-co1.fl_str_mv Moehlecke, Adriano
dc.contributor.advisor-co1Lattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4787919H0
dc.contributor.authorID.fl_str_mv 013.725.520-90
dc.contributor.authorLattes.fl_str_mv http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K8783497T7
dc.contributor.author.fl_str_mv Crestani, Thais
contributor_str_mv Zanesco, Izete
Moehlecke, Adriano
dc.subject.por.fl_str_mv CÉLULAS SOLARES
SILÍCIO
ENGENHARIA
topic CÉLULAS SOLARES
SILÍCIO
ENGENHARIA
ENGENHARIAS
dc.subject.cnpq.fl_str_mv ENGENHARIAS
description The typical solar cells of the industry are fabricated in p-type crystalline silicon wafers and have a pn junction at one side and, on the other side, the back surface field (BSF). The objective of this work is to develop solar cells with aluminum and boron selective back surface field to enable the passivation on the rear face with an industrial process. Czochralski p-type silicon wafers of solar grade quality were used. The boron diffusion was performed on the whole back side of the silicon wafers and the aluminum was screen-printed to form the selective back surface field under the metal grid. The boron diffusion temperature and time, the firing temperature of the metal pastes, the percentage of the rear area covered with aluminum and the passivation with SiO2 were evaluated in the electrical parameters. The best boron diffusion temperature was 970 ° C for 20 minutes and firing temperature of the metal pastes was 870 ° C. The solar cell with the highest efficiency were obtained for a rear metal grid with 14 % of the area covered by aluminum. The passivation by SiO2 on both surfaces increased the minority charge carrier diffusion length from 490 μm to 665 μm. Consequently, the passivation increased the efficiency from 15.6 % to 16.1 %, as a result of an increasing of the fill factor and the open circuit voltage. The passivation also increased the internal quantum efficiency in the range of violet/blue wavelengths as well as in the near infrared region.
publishDate 2016
dc.date.accessioned.fl_str_mv 2016-10-06T11:11:46Z
dc.date.issued.fl_str_mv 2016-07-07
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://tede2.pucrs.br/tede2/handle/tede/6985
url http://tede2.pucrs.br/tede2/handle/tede/6985
dc.language.iso.fl_str_mv por
language por
dc.relation.program.fl_str_mv -7432719344215120122
dc.relation.confidence.fl_str_mv 600
600
600
dc.relation.department.fl_str_mv -655770572761439785
dc.relation.cnpq.fl_str_mv 4518971056484826825
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.publisher.none.fl_str_mv Pontifícia Universidade Católica do Rio Grande do Sul
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais
dc.publisher.initials.fl_str_mv PUCRS
dc.publisher.country.fl_str_mv Brasil
dc.publisher.department.fl_str_mv Faculdade de Engenharia
publisher.none.fl_str_mv Pontifícia Universidade Católica do Rio Grande do Sul
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS
instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
instacron:PUC_RS
instname_str Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
instacron_str PUC_RS
institution PUC_RS
reponame_str Biblioteca Digital de Teses e Dissertações da PUC_RS
collection Biblioteca Digital de Teses e Dissertações da PUC_RS
bitstream.url.fl_str_mv http://tede2.pucrs.br/tede2/bitstream/tede/6985/5/DIS_THAIS_CRESTANI_COMPLETO.pdf.jpg
http://tede2.pucrs.br/tede2/bitstream/tede/6985/4/DIS_THAIS_CRESTANI_COMPLETO.pdf.txt
http://tede2.pucrs.br/tede2/bitstream/tede/6985/3/license.txt
http://tede2.pucrs.br/tede2/bitstream/tede/6985/2/DIS_THAIS_CRESTANI_COMPLETO.pdf
bitstream.checksum.fl_str_mv 06fbac9bdabbb222df0f073b987b23a7
1cadc55eae0496ddc8659244ecd13c91
5a9d6006225b368ef605ba16b4f6d1be
40503ab7961f50b87d67545be969f402
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
MD5
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
repository.mail.fl_str_mv biblioteca.central@pucrs.br||
_version_ 1799765322306158592