Resistência à fratura de coroas cerâmicas monolíticas fabricadas em CAD/CAM cimentadas sobre diferentes pilares de implante
Autor(a) principal: | |
---|---|
Data de Publicação: | 2019 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da PUC_RS |
Texto Completo: | http://tede2.pucrs.br/tede2/handle/tede/8614 |
Resumo: | Objective: to evaluate the fracture strength of monolithic ceramic unit crowns with different thickness and cemented on solid abutment and tiBase. The hypotheses presented are that (i) the presence of the fixing screw hole decreases the crown fracture strength, (ii) the restoring material influences the fracture resistance, (iii) the restoration thickness influences the fracture resistance of the restorations. Materials and methods: A total of 64 upper second premolar crowns were made for the solid abutment and Variobase C® abutment over the implant analog Straumann Tissue Level. The crowns were made of lithium dissilicate (IPS e.max CAD) and zirconia (Incoris ZI) with 0,5 mm and 1,5 mm thickness in the occlusal, and divided into 8 groups (n = 8): SE05, SE15, SZ05, SZ15, VE05, VE15, VZ05, VZ15. The crowns were cemented with resin cement and the screw access restored with composite resin. After mechanical cycling, the specimens were submitted to the test of fracture resistance in the universal test machine and the maximum force recorded in Newtons (N). The results were submitted to the Shapiro-Wilk test followed by 3-way ANOVA and Tukey (a= 5%). Results: SZ15: 5368,6 N ± 536,74 A; SZ05: 4809,8 N ± 857,55 A; SE15: 2068,8 N ± 359,77 B; SE05: 1887,4N ± 276,94 B; VZ15: 1935,5N ± 274,51 B; VZ05: 1759,4 N ± 334,34 B; VE15: 963,5 N ± 198,92 C; VE05: 924,8 N ± 152,01 C. Conclusions: The presence of the screw access channel reduced in half the fracture strength of the crowns when compared to the crowns cemented on a solid abutment. Incoris ZI showed higher fracture resistance than the IPS e.max CAD independent of the abutment and thickness. The different thicknesses of the restorations had little influence on fracture resistance. |
id |
P_RS_3ea7ae3718e0ad6d0d498067bd9d69d3 |
---|---|
oai_identifier_str |
oai:tede2.pucrs.br:tede/8614 |
network_acronym_str |
P_RS |
network_name_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
repository_id_str |
|
spelling |
Burnett Jr., Luiz Henriquehttp://lattes.cnpq.br/1252685026530007http://lattes.cnpq.br/2752544081968434Meneghetti, Priscila Ceolin2019-05-30T14:41:10Z2019-03-14http://tede2.pucrs.br/tede2/handle/tede/8614Objective: to evaluate the fracture strength of monolithic ceramic unit crowns with different thickness and cemented on solid abutment and tiBase. The hypotheses presented are that (i) the presence of the fixing screw hole decreases the crown fracture strength, (ii) the restoring material influences the fracture resistance, (iii) the restoration thickness influences the fracture resistance of the restorations. Materials and methods: A total of 64 upper second premolar crowns were made for the solid abutment and Variobase C® abutment over the implant analog Straumann Tissue Level. The crowns were made of lithium dissilicate (IPS e.max CAD) and zirconia (Incoris ZI) with 0,5 mm and 1,5 mm thickness in the occlusal, and divided into 8 groups (n = 8): SE05, SE15, SZ05, SZ15, VE05, VE15, VZ05, VZ15. The crowns were cemented with resin cement and the screw access restored with composite resin. After mechanical cycling, the specimens were submitted to the test of fracture resistance in the universal test machine and the maximum force recorded in Newtons (N). The results were submitted to the Shapiro-Wilk test followed by 3-way ANOVA and Tukey (a= 5%). Results: SZ15: 5368,6 N ± 536,74 A; SZ05: 4809,8 N ± 857,55 A; SE15: 2068,8 N ± 359,77 B; SE05: 1887,4N ± 276,94 B; VZ15: 1935,5N ± 274,51 B; VZ05: 1759,4 N ± 334,34 B; VE15: 963,5 N ± 198,92 C; VE05: 924,8 N ± 152,01 C. Conclusions: The presence of the screw access channel reduced in half the fracture strength of the crowns when compared to the crowns cemented on a solid abutment. Incoris ZI showed higher fracture resistance than the IPS e.max CAD independent of the abutment and thickness. The different thicknesses of the restorations had little influence on fracture resistance.Objetivo: avaliar a resistência à fratura de coroas cerâmicas monolíticas com diferentes espessuras e cimentadas sobre pilar sólido e tiBase. As hipóteses apresentadas são que (i) a presença do orifício do parafuso de fixação diminui a resistência à fratura das coroas, (ii) o material restaurador influencia na resistência à fratura, (iii) a espessura da restauração influencia na resistência à fratura das restaurações. Materiais e métodos: Um total de 64 coroas de segundo pré-molar superior foram confeccionadas para os pilares Sólido e Variobase C® (tiBase) sobre o análogo do implante Straumann Tissue Level. As coroas foram confeccionadas em dissilicato de litio (IPS e.max CAD) e zircônia (Incoris ZI) com 0,5 mm e 1,5 mm de espessura na face oclusal, e divididas em 8 grupos (n=8): SE05, SE15, SZ05, SZ15, VE05, VE15, VZ05, VZ15. As coroas foram cimentadas com cimento resinoso e o acesso ao parafuso restaurado com resina composta. Após ciclagem mecânica, os corpos de prova foram submetidos ao ensaio de resistência à fratura na máquina de ensaio universal e a força máxima registrada em Newtons (N). Os resultados obtidos foram submetidos ao teste de Shapiro-Wilk seguido de ANOVA 3-way e Tukey (a= 5%). Resultados: SZ15: 5368,6 N ± 536,74 A; SZ05: 4809,8 N ± 857,55 A; SE15: 2068,8 N ± 359,77 B; SE05: 1887,4N ± 276,94 B; VZ15: 1935,5N ± 274,51 B; VZ05: 1759,4 N ± 334,34 B; VE15: 963,5 N ± 198,92 C; VE05: 924,8 N ± 152,01 C. Conclusões: A presença do canal de acesso ao parafuso reduziu pela metade a resistência à fratura das coroas quando comparados com as coroas cimentadas sobre pilar sólido. A zircônia Incoris ZI apresentou maior resistência à fratura do que o IPS e.max CAD independente do pilar e da espessura. As diferentes espessuras das restaurações tiveram pouca influência na resistência à fratura.Submitted by PPG Odontologia (odontologia-pg@pucrs.br) on 2019-04-30T17:58:30Z No. of bitstreams: 1 PRISCILA_CEOLIN MENEGHETTI_DIS.pdf: 2657075 bytes, checksum: bde96ebb49dd8c1a4fc4ca8f997d1ef1 (MD5)Approved for entry into archive by Sheila Dias (sheila.dias@pucrs.br) on 2019-05-30T14:25:52Z (GMT) No. of bitstreams: 1 PRISCILA_CEOLIN MENEGHETTI_DIS.pdf: 2657075 bytes, checksum: bde96ebb49dd8c1a4fc4ca8f997d1ef1 (MD5)Made available in DSpace on 2019-05-30T14:41:10Z (GMT). No. of bitstreams: 1 PRISCILA_CEOLIN MENEGHETTI_DIS.pdf: 2657075 bytes, checksum: bde96ebb49dd8c1a4fc4ca8f997d1ef1 (MD5) Previous issue date: 2019-03-14Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/175212/DIS_PRISCILA_CEOLIN_MENEGHETTI_CONFIDENCIAL.pdf.jpghttps://tede2.pucrs.br/tede2/retrieve/187823/DIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em OdontologiaPUCRSBrasilEscola de Ciências da SaúdeCerâmica MonolíticaCAD/CAMResistência à FraturaImplante DentáriozircôniaDissilicato de LítioTiBasePilar SólidoMonolitic cCramicsCAD/CAMDental ImplantFracture StrengthIithium DissilicateKirconiaTiBaseSolid AbutmentCIENCIAS DA SAUDE::ODONTOLOGIAResistência à fratura de coroas cerâmicas monolíticas fabricadas em CAD/CAM cimentadas sobre diferentes pilares de implanteinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisTrabalho será publicado como artigo ou livro48 meses30/05/2023-7411869720500764667500500600-20704984698792443493590462550136975366info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSORIGINALDIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdfDIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdfapplication/pdf2657075https://tede2.pucrs.br/tede2/bitstream/tede/8614/5/DIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdfbde96ebb49dd8c1a4fc4ca8f997d1ef1MD55THUMBNAILDIS_PRISCILA_CEOLIN_MENEGHETTI_CONFIDENCIAL.pdf.jpgDIS_PRISCILA_CEOLIN_MENEGHETTI_CONFIDENCIAL.pdf.jpgimage/jpeg4084https://tede2.pucrs.br/tede2/bitstream/tede/8614/4/DIS_PRISCILA_CEOLIN_MENEGHETTI_CONFIDENCIAL.pdf.jpg58c55d8ea300c86ec69197ab0d6510edMD54DIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdf.jpgDIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdf.jpgimage/jpeg5974https://tede2.pucrs.br/tede2/bitstream/tede/8614/7/DIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdf.jpg2cff0be84b219eedc43c7c678ca2a977MD57TEXTDIS_PRISCILA_CEOLIN_MENEGHETTI_CONFIDENCIAL.pdf.txtDIS_PRISCILA_CEOLIN_MENEGHETTI_CONFIDENCIAL.pdf.txttext/plain2303https://tede2.pucrs.br/tede2/bitstream/tede/8614/3/DIS_PRISCILA_CEOLIN_MENEGHETTI_CONFIDENCIAL.pdf.txt9b9d3d68c28a57f2b176cebe9c4b6361MD53DIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdf.txtDIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdf.txttext/plain36057https://tede2.pucrs.br/tede2/bitstream/tede/8614/6/DIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdf.txt0e4c351b280fcce6ab0517aa9d875b6bMD56LICENSElicense.txtlicense.txttext/plain; charset=utf-8590https://tede2.pucrs.br/tede2/bitstream/tede/8614/1/license.txt220e11f2d3ba5354f917c7035aadef24MD51tede/86142023-06-09 12:00:22.197oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2023-06-09T15:00:22Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false |
dc.title.por.fl_str_mv |
Resistência à fratura de coroas cerâmicas monolíticas fabricadas em CAD/CAM cimentadas sobre diferentes pilares de implante |
title |
Resistência à fratura de coroas cerâmicas monolíticas fabricadas em CAD/CAM cimentadas sobre diferentes pilares de implante |
spellingShingle |
Resistência à fratura de coroas cerâmicas monolíticas fabricadas em CAD/CAM cimentadas sobre diferentes pilares de implante Meneghetti, Priscila Ceolin Cerâmica Monolítica CAD/CAM Resistência à Fratura Implante Dentário zircônia Dissilicato de Lítio TiBase Pilar Sólido Monolitic cCramics CAD/CAM Dental Implant Fracture Strength Iithium Dissilicate Kirconia TiBase Solid Abutment CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Resistência à fratura de coroas cerâmicas monolíticas fabricadas em CAD/CAM cimentadas sobre diferentes pilares de implante |
title_full |
Resistência à fratura de coroas cerâmicas monolíticas fabricadas em CAD/CAM cimentadas sobre diferentes pilares de implante |
title_fullStr |
Resistência à fratura de coroas cerâmicas monolíticas fabricadas em CAD/CAM cimentadas sobre diferentes pilares de implante |
title_full_unstemmed |
Resistência à fratura de coroas cerâmicas monolíticas fabricadas em CAD/CAM cimentadas sobre diferentes pilares de implante |
title_sort |
Resistência à fratura de coroas cerâmicas monolíticas fabricadas em CAD/CAM cimentadas sobre diferentes pilares de implante |
author |
Meneghetti, Priscila Ceolin |
author_facet |
Meneghetti, Priscila Ceolin |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Burnett Jr., Luiz Henrique |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/1252685026530007 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/2752544081968434 |
dc.contributor.author.fl_str_mv |
Meneghetti, Priscila Ceolin |
contributor_str_mv |
Burnett Jr., Luiz Henrique |
dc.subject.por.fl_str_mv |
Cerâmica Monolítica CAD/CAM Resistência à Fratura Implante Dentário zircônia Dissilicato de Lítio TiBase Pilar Sólido |
topic |
Cerâmica Monolítica CAD/CAM Resistência à Fratura Implante Dentário zircônia Dissilicato de Lítio TiBase Pilar Sólido Monolitic cCramics CAD/CAM Dental Implant Fracture Strength Iithium Dissilicate Kirconia TiBase Solid Abutment CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.eng.fl_str_mv |
Monolitic cCramics CAD/CAM Dental Implant Fracture Strength Iithium Dissilicate Kirconia TiBase Solid Abutment |
dc.subject.cnpq.fl_str_mv |
CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
Objective: to evaluate the fracture strength of monolithic ceramic unit crowns with different thickness and cemented on solid abutment and tiBase. The hypotheses presented are that (i) the presence of the fixing screw hole decreases the crown fracture strength, (ii) the restoring material influences the fracture resistance, (iii) the restoration thickness influences the fracture resistance of the restorations. Materials and methods: A total of 64 upper second premolar crowns were made for the solid abutment and Variobase C® abutment over the implant analog Straumann Tissue Level. The crowns were made of lithium dissilicate (IPS e.max CAD) and zirconia (Incoris ZI) with 0,5 mm and 1,5 mm thickness in the occlusal, and divided into 8 groups (n = 8): SE05, SE15, SZ05, SZ15, VE05, VE15, VZ05, VZ15. The crowns were cemented with resin cement and the screw access restored with composite resin. After mechanical cycling, the specimens were submitted to the test of fracture resistance in the universal test machine and the maximum force recorded in Newtons (N). The results were submitted to the Shapiro-Wilk test followed by 3-way ANOVA and Tukey (a= 5%). Results: SZ15: 5368,6 N ± 536,74 A; SZ05: 4809,8 N ± 857,55 A; SE15: 2068,8 N ± 359,77 B; SE05: 1887,4N ± 276,94 B; VZ15: 1935,5N ± 274,51 B; VZ05: 1759,4 N ± 334,34 B; VE15: 963,5 N ± 198,92 C; VE05: 924,8 N ± 152,01 C. Conclusions: The presence of the screw access channel reduced in half the fracture strength of the crowns when compared to the crowns cemented on a solid abutment. Incoris ZI showed higher fracture resistance than the IPS e.max CAD independent of the abutment and thickness. The different thicknesses of the restorations had little influence on fracture resistance. |
publishDate |
2019 |
dc.date.accessioned.fl_str_mv |
2019-05-30T14:41:10Z |
dc.date.issued.fl_str_mv |
2019-03-14 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://tede2.pucrs.br/tede2/handle/tede/8614 |
url |
http://tede2.pucrs.br/tede2/handle/tede/8614 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-7411869720500764667 |
dc.relation.confidence.fl_str_mv |
500 500 600 |
dc.relation.cnpq.fl_str_mv |
-2070498469879244349 |
dc.relation.sponsorship.fl_str_mv |
3590462550136975366 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Odontologia |
dc.publisher.initials.fl_str_mv |
PUCRS |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Escola de Ciências da Saúde |
publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) instacron:PUC_RS |
instname_str |
Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
instacron_str |
PUC_RS |
institution |
PUC_RS |
reponame_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
collection |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
bitstream.url.fl_str_mv |
https://tede2.pucrs.br/tede2/bitstream/tede/8614/5/DIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdf https://tede2.pucrs.br/tede2/bitstream/tede/8614/4/DIS_PRISCILA_CEOLIN_MENEGHETTI_CONFIDENCIAL.pdf.jpg https://tede2.pucrs.br/tede2/bitstream/tede/8614/7/DIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdf.jpg https://tede2.pucrs.br/tede2/bitstream/tede/8614/3/DIS_PRISCILA_CEOLIN_MENEGHETTI_CONFIDENCIAL.pdf.txt https://tede2.pucrs.br/tede2/bitstream/tede/8614/6/DIS_PRISCILA_CEOLIN_MENEGHETTI_COMPLETO.pdf.txt https://tede2.pucrs.br/tede2/bitstream/tede/8614/1/license.txt |
bitstream.checksum.fl_str_mv |
bde96ebb49dd8c1a4fc4ca8f997d1ef1 58c55d8ea300c86ec69197ab0d6510ed 2cff0be84b219eedc43c7c678ca2a977 9b9d3d68c28a57f2b176cebe9c4b6361 0e4c351b280fcce6ab0517aa9d875b6b 220e11f2d3ba5354f917c7035aadef24 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
repository.mail.fl_str_mv |
biblioteca.central@pucrs.br|| |
_version_ |
1799765339289944064 |