Avaliação da resistência de união das interfaces de cimentação de onlays em resina composta CAD/CAM
Autor(a) principal: | |
---|---|
Data de Publicação: | 2016 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da PUC_RS |
Texto Completo: | http://tede2.pucrs.br/tede2/handle/tede/6795 |
Resumo: | The aim of the study was to evaluate, in vitro, the weakest bond interface in Lava Ultimate onlays luted to the tooth preparation with Single Bond Universal and RelyX Ultimate. The following variables were tested: a) total-etch or the self-etch technique; b) with and without adhesive application on the internal surface of the onlay; c) with and without cyclic loading. Fifty-six Lava Ultimate onlays were milled and luted to the human tooth preparations according to the variables, being formed eight groups (n = 7): G1 and G2 - Single Bond Universal applied in the total-etch mode; G3 and G4 - Single Bond Universal applied in the self-etch mode; G5 and G6 - Single Bond Universal applied in the total-etch mode + adhesive application on the onlay; G7 and G8 - Single Bond Universal in the self-etch mode + adhesive application on the onlay. The onlays were luted with RelyX Ultimate. After storage in distilled water at 37° C for 24 h, only the samples from G2, G4, G6 and G8 were submitted to cyclic loading at 100 N using 1000,000 cycles. Beams with a cross section area of ~0.80 mm2 from all groups were obtained and submitted to a microtensile bond strength test in a universal testing machine at a crosshead speed of 0.5 mm/min. The types of failure were observed in optical microscope. The microtensile bond strength values were analyzed by three-way ANOVA and post-hoc multiple comparison using Tukey’s test (α=0.05). There was a significant interaction between the three factors (p = 0.006).The means followed by the same letter represent no statistical difference for the microtensile bond strength (MPa): G6 = 34.64 (±34.64)a, G1 = 34.48 (±12.58)a, G2 = 31.94 (±9.18) ab, G5 = 30.88 (±6.85)abc, G7 = 26.66 (±8.25)bc, G8 = 24.03 (±7.65)cd, G4 = 18.81 (±4.14)de, G3 = 14.64 (±5.35)e. Most failures were at the resinous agent-restoration interface. It was concluded that the resinous agent-restoration interface corresponds to the weakest interface in Lava Ultimate onlays luted with Single Bond Universal and RelyX Ultimate. The application of Single Bond Universal on the internal surface of the onlay was not a relevant procedure. |
id |
P_RS_559a98dcf83e65029354dd2257c9f7c9 |
---|---|
oai_identifier_str |
oai:tede2.pucrs.br:tede/6795 |
network_acronym_str |
P_RS |
network_name_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
repository_id_str |
|
spelling |
Spohr, Ana Maria423.932.720-20http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4790497E9916.684.840-72http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4242317Y1Souza, Ivana Agnoletto2016-06-29T19:51:31Z2016-02-29http://tede2.pucrs.br/tede2/handle/tede/6795The aim of the study was to evaluate, in vitro, the weakest bond interface in Lava Ultimate onlays luted to the tooth preparation with Single Bond Universal and RelyX Ultimate. The following variables were tested: a) total-etch or the self-etch technique; b) with and without adhesive application on the internal surface of the onlay; c) with and without cyclic loading. Fifty-six Lava Ultimate onlays were milled and luted to the human tooth preparations according to the variables, being formed eight groups (n = 7): G1 and G2 - Single Bond Universal applied in the total-etch mode; G3 and G4 - Single Bond Universal applied in the self-etch mode; G5 and G6 - Single Bond Universal applied in the total-etch mode + adhesive application on the onlay; G7 and G8 - Single Bond Universal in the self-etch mode + adhesive application on the onlay. The onlays were luted with RelyX Ultimate. After storage in distilled water at 37° C for 24 h, only the samples from G2, G4, G6 and G8 were submitted to cyclic loading at 100 N using 1000,000 cycles. Beams with a cross section area of ~0.80 mm2 from all groups were obtained and submitted to a microtensile bond strength test in a universal testing machine at a crosshead speed of 0.5 mm/min. The types of failure were observed in optical microscope. The microtensile bond strength values were analyzed by three-way ANOVA and post-hoc multiple comparison using Tukey’s test (α=0.05). There was a significant interaction between the three factors (p = 0.006).The means followed by the same letter represent no statistical difference for the microtensile bond strength (MPa): G6 = 34.64 (±34.64)a, G1 = 34.48 (±12.58)a, G2 = 31.94 (±9.18) ab, G5 = 30.88 (±6.85)abc, G7 = 26.66 (±8.25)bc, G8 = 24.03 (±7.65)cd, G4 = 18.81 (±4.14)de, G3 = 14.64 (±5.35)e. Most failures were at the resinous agent-restoration interface. It was concluded that the resinous agent-restoration interface corresponds to the weakest interface in Lava Ultimate onlays luted with Single Bond Universal and RelyX Ultimate. The application of Single Bond Universal on the internal surface of the onlay was not a relevant procedure.Este estudo teve como objetivo avaliar, in vitro, a interface de união menos resistente de onlays em resina composta Lava Ultimate cimentadas ao preparo dentário com Single Bond Universal e RelyX Ultimate, nas seguintes variáveis: a) aplicação do sistema adesivo no modo total-etch e self-etch; b) com e sem aplicação do adesivo na superfície interna da onlay; c) sem e com ciclagem mecânica. Ao total foram fresadas 56 onlays em resina composta Lava Ultimate, sendo cimentadas aos preparos em dentes humanos de acordo com as variáveis empregadas, sendo formados oito grupos (n=7): G1 e G2 - Single Bond Universal na versão total-etch; G3 e G4 - Single Bond Universal na versão self-etch; G5 e G6 - Single Bond Universal na versão total-etch + adesivo na onlay; G7 e G8 - Single Bond Universal na versão self-etch + adesivo na onlay. As onlays foram cimentadas com o cimento resinoso RelyX Ultimate. Após armazenamento em água destilada a 37º C por 24 h, apenas as amostras do G2, G4, G6 e G8 foram submetidas à ciclagem mecânica com carga vertical de 100 N na superfície oclusal das coroas, totalizando 1.000.000 de ciclos. Todas as restaurações, de todos os grupos, foram seccionadas nos eixos x e y para obtenção de corpos de prova em forma de palitos, com aproximadamente 0,80 mm2 de secção transversal. Os corpos de prova foram submetidos ao teste de microtração na máquina de ensaio universal EMIC-DL 2000 com velocidade de 0,5 mm/minuto. Os tipos de falha foram observados em microscópio óptico. Os valores de resistência à microtração foram analisados pela ANOVA de três vias, seguido do teste de Tukey ao nível de significância de 5%. Houve interação significativa entre os três fatores (p=0,006). As médias seguidas de mesma letra não diferem estatisticamente para a resistência à microtração (MPa): G6 = 34,64 (±34,64)a, G1 = 34,48 (±12,58)a, G2 = 31,94 (±9,18) ab, G5 = 30,88 (±6,85)abc, G7 = 26,66 (±8,25)bc, G8 = 24,03 (±7,65)cd, G4 = 18,81 (±4,14)de, G3 = 14,64 (±5,35)e. A maioria das falhas foram na interface agente resinoso-restauração. Conclui-se que a interface agente resinoso/restauração corresponde à interface menos resistente na cimentação de onlays em resina composta Lava Ultimate quando empregado o sistema adesivo Single Bond Universal e o cimento resinoso RelyX Ultimate. A aplicação do adesivo Single Bond Universal na superfície interna da restauração não se mostrou um procedimento relevante.Submitted by Setor de Tratamento da Informação - BC/PUCRS (tede2@pucrs.br) on 2016-06-29T19:51:31Z No. of bitstreams: 1 DIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf: 106952 bytes, checksum: 37ca419440e1901deef7a5328ff06ed2 (MD5)Made available in DSpace on 2016-06-29T19:51:31Z (GMT). No. of bitstreams: 1 DIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf: 106952 bytes, checksum: 37ca419440e1901deef7a5328ff06ed2 (MD5) Previous issue date: 2016-02-29Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/165521/DIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em OdontologiaPUCRSBrasilFaculdade de OdontologiaRESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA)RESTAURAÇÃO DENTÁRIARESINAS COMPOSTASRESINAS (ODONTOLOGIA)ODONTOLOGIACIENCIAS DA SAUDE::ODONTOLOGIAAvaliação da resistência de união das interfaces de cimentação de onlays em resina composta CAD/CAMinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-80965548187336651646006006006004673435736271820140-20704984698792443492075167498588264571info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSTHUMBNAILDIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf.jpgDIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf.jpgimage/jpeg3667http://tede2.pucrs.br/tede2/bitstream/tede/6795/5/DIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf.jpg530da6cca5fedaf1e14d4a1e10f13315MD55TEXTDIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf.txtDIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf.txttext/plain12626http://tede2.pucrs.br/tede2/bitstream/tede/6795/4/DIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf.txte20d5f431495cc8c4ad6999c9068271fMD54LICENSElicense.txtlicense.txttext/plain; charset=utf-8610http://tede2.pucrs.br/tede2/bitstream/tede/6795/3/license.txt5a9d6006225b368ef605ba16b4f6d1beMD53ORIGINALDIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdfDIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdfapplication/pdf106952http://tede2.pucrs.br/tede2/bitstream/tede/6795/2/DIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf37ca419440e1901deef7a5328ff06ed2MD52tede/67952016-06-29 20:00:29.691oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2016-06-29T23:00:29Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false |
dc.title.por.fl_str_mv |
Avaliação da resistência de união das interfaces de cimentação de onlays em resina composta CAD/CAM |
title |
Avaliação da resistência de união das interfaces de cimentação de onlays em resina composta CAD/CAM |
spellingShingle |
Avaliação da resistência de união das interfaces de cimentação de onlays em resina composta CAD/CAM Souza, Ivana Agnoletto RESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA) RESTAURAÇÃO DENTÁRIA RESINAS COMPOSTAS RESINAS (ODONTOLOGIA) ODONTOLOGIA CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Avaliação da resistência de união das interfaces de cimentação de onlays em resina composta CAD/CAM |
title_full |
Avaliação da resistência de união das interfaces de cimentação de onlays em resina composta CAD/CAM |
title_fullStr |
Avaliação da resistência de união das interfaces de cimentação de onlays em resina composta CAD/CAM |
title_full_unstemmed |
Avaliação da resistência de união das interfaces de cimentação de onlays em resina composta CAD/CAM |
title_sort |
Avaliação da resistência de união das interfaces de cimentação de onlays em resina composta CAD/CAM |
author |
Souza, Ivana Agnoletto |
author_facet |
Souza, Ivana Agnoletto |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Spohr, Ana Maria |
dc.contributor.advisor1ID.fl_str_mv |
423.932.720-20 |
dc.contributor.advisor1Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4790497E9 |
dc.contributor.authorID.fl_str_mv |
916.684.840-72 |
dc.contributor.authorLattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4242317Y1 |
dc.contributor.author.fl_str_mv |
Souza, Ivana Agnoletto |
contributor_str_mv |
Spohr, Ana Maria |
dc.subject.por.fl_str_mv |
RESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA) RESTAURAÇÃO DENTÁRIA RESINAS COMPOSTAS RESINAS (ODONTOLOGIA) ODONTOLOGIA |
topic |
RESISTÊNCIA DOS MATERIAIS (ODONTOLOGIA) RESTAURAÇÃO DENTÁRIA RESINAS COMPOSTAS RESINAS (ODONTOLOGIA) ODONTOLOGIA CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.cnpq.fl_str_mv |
CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
The aim of the study was to evaluate, in vitro, the weakest bond interface in Lava Ultimate onlays luted to the tooth preparation with Single Bond Universal and RelyX Ultimate. The following variables were tested: a) total-etch or the self-etch technique; b) with and without adhesive application on the internal surface of the onlay; c) with and without cyclic loading. Fifty-six Lava Ultimate onlays were milled and luted to the human tooth preparations according to the variables, being formed eight groups (n = 7): G1 and G2 - Single Bond Universal applied in the total-etch mode; G3 and G4 - Single Bond Universal applied in the self-etch mode; G5 and G6 - Single Bond Universal applied in the total-etch mode + adhesive application on the onlay; G7 and G8 - Single Bond Universal in the self-etch mode + adhesive application on the onlay. The onlays were luted with RelyX Ultimate. After storage in distilled water at 37° C for 24 h, only the samples from G2, G4, G6 and G8 were submitted to cyclic loading at 100 N using 1000,000 cycles. Beams with a cross section area of ~0.80 mm2 from all groups were obtained and submitted to a microtensile bond strength test in a universal testing machine at a crosshead speed of 0.5 mm/min. The types of failure were observed in optical microscope. The microtensile bond strength values were analyzed by three-way ANOVA and post-hoc multiple comparison using Tukey’s test (α=0.05). There was a significant interaction between the three factors (p = 0.006).The means followed by the same letter represent no statistical difference for the microtensile bond strength (MPa): G6 = 34.64 (±34.64)a, G1 = 34.48 (±12.58)a, G2 = 31.94 (±9.18) ab, G5 = 30.88 (±6.85)abc, G7 = 26.66 (±8.25)bc, G8 = 24.03 (±7.65)cd, G4 = 18.81 (±4.14)de, G3 = 14.64 (±5.35)e. Most failures were at the resinous agent-restoration interface. It was concluded that the resinous agent-restoration interface corresponds to the weakest interface in Lava Ultimate onlays luted with Single Bond Universal and RelyX Ultimate. The application of Single Bond Universal on the internal surface of the onlay was not a relevant procedure. |
publishDate |
2016 |
dc.date.accessioned.fl_str_mv |
2016-06-29T19:51:31Z |
dc.date.issued.fl_str_mv |
2016-02-29 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://tede2.pucrs.br/tede2/handle/tede/6795 |
url |
http://tede2.pucrs.br/tede2/handle/tede/6795 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-8096554818733665164 |
dc.relation.confidence.fl_str_mv |
600 600 600 600 |
dc.relation.department.fl_str_mv |
4673435736271820140 |
dc.relation.cnpq.fl_str_mv |
-2070498469879244349 |
dc.relation.sponsorship.fl_str_mv |
2075167498588264571 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Odontologia |
dc.publisher.initials.fl_str_mv |
PUCRS |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Faculdade de Odontologia |
publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) instacron:PUC_RS |
instname_str |
Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
instacron_str |
PUC_RS |
institution |
PUC_RS |
reponame_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
collection |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
bitstream.url.fl_str_mv |
http://tede2.pucrs.br/tede2/bitstream/tede/6795/5/DIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf.jpg http://tede2.pucrs.br/tede2/bitstream/tede/6795/4/DIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf.txt http://tede2.pucrs.br/tede2/bitstream/tede/6795/3/license.txt http://tede2.pucrs.br/tede2/bitstream/tede/6795/2/DIS_IVANA_AGNOLETTO_SOUZA_PARCIAL.pdf |
bitstream.checksum.fl_str_mv |
530da6cca5fedaf1e14d4a1e10f13315 e20d5f431495cc8c4ad6999c9068271f 5a9d6006225b368ef605ba16b4f6d1be 37ca419440e1901deef7a5328ff06ed2 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
repository.mail.fl_str_mv |
biblioteca.central@pucrs.br|| |
_version_ |
1799765320195375104 |