Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética
Autor(a) principal: | |
---|---|
Data de Publicação: | 2018 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da PUC_RS |
Texto Completo: | http://tede2.pucrs.br/tede2/handle/tede/8637 |
Resumo: | In the present study, some physical characteristics and nuclear magnetic relaxation properties of iron oxide nanoparticles coated with different coatings and synthesized in our laboratories were investigated. Eight nanoparticle systems were obtained, one of these systems being a linked fluorophore group (Cy5.5). Raman spectroscopy and X-rays diffraction have shown that the iron oxide in question is magnetite. The magnetization measurements revealed superparamagnetic behavior of the nanoparticles due to the absence of hysteresis of the nanoparticles and a saturation magnetization ranging from 3.8-61.6 emu/g. The iron concentration of each synthesis was obtained by UV-Vis spectrophotometry and relaxometry and the results obtained ranged from 0.46-11.2 mg/mL. ZFC/FC measurements showed a distribution of the blocking temperature of the nanoparticles not exceeding 50 K. Aqueous solutions with different concentrations of the nanoparticles and the Lumirem commercial contrast agent were prepared to give the relaxation times T1 and T2 and the relaxivities r1 and r2. In these measurements, the nanoparticles showed contrast effects, disturbing the signal intensity, decreasing the relaxation times T1 and T2. The ratio of relaxivities (r2/r1) ranged from 3.13-64.14, which is within the values of the commercially available iron oxide contrast agents. It is concluded that the nanoparticles evaluated in this work are suitable as a T2-type contrast agent. |
id |
P_RS_a1cdab5e5233480f5704e3c78393f936 |
---|---|
oai_identifier_str |
oai:tede2.pucrs.br:tede/8637 |
network_acronym_str |
P_RS |
network_name_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
repository_id_str |
|
spelling |
Papaléo, Ricardo Meurerhttp://lattes.cnpq.br/1933730859000512Rocha, Maximiliano Santos da2019-06-04T14:16:00Z2018-01-26http://tede2.pucrs.br/tede2/handle/tede/8637In the present study, some physical characteristics and nuclear magnetic relaxation properties of iron oxide nanoparticles coated with different coatings and synthesized in our laboratories were investigated. Eight nanoparticle systems were obtained, one of these systems being a linked fluorophore group (Cy5.5). Raman spectroscopy and X-rays diffraction have shown that the iron oxide in question is magnetite. The magnetization measurements revealed superparamagnetic behavior of the nanoparticles due to the absence of hysteresis of the nanoparticles and a saturation magnetization ranging from 3.8-61.6 emu/g. The iron concentration of each synthesis was obtained by UV-Vis spectrophotometry and relaxometry and the results obtained ranged from 0.46-11.2 mg/mL. ZFC/FC measurements showed a distribution of the blocking temperature of the nanoparticles not exceeding 50 K. Aqueous solutions with different concentrations of the nanoparticles and the Lumirem commercial contrast agent were prepared to give the relaxation times T1 and T2 and the relaxivities r1 and r2. In these measurements, the nanoparticles showed contrast effects, disturbing the signal intensity, decreasing the relaxation times T1 and T2. The ratio of relaxivities (r2/r1) ranged from 3.13-64.14, which is within the values of the commercially available iron oxide contrast agents. It is concluded that the nanoparticles evaluated in this work are suitable as a T2-type contrast agent.No presente estudo, algumas características físicas e propriedades de relaxação magnética nuclear de nanopartículas de óxido de ferro revestidas com diferentes recobrimentos e sintetizadas em nossos laboratórios foram investigadas. Obtiveram-se oito sistemas de nanopartículas, sendo um destes sistemas com um grupo fluoróforo ligado (Cy5.5). Análises de espectroscopia Raman e difração de raios-X demonstraram que o óxido de ferro em questão é a magnetita. As medidas de magnetização revelaram comportamento superparamagnético das nanopartículas, devido à ausência de histerese das mesmas, e uma magnetização de saturação variando entre 3,8-61,6 emu/g. A concentração de ferro de cada síntese foi obtida por espectrofotometria UV-Vis e relaxometria. Os resultados obtidos variaram entre 0,46-11,2 mg/mL. Medidas de ZFC/FC demonstraram uma distribuição de temperaturas de bloqueio das nanopartículas não excedendo 50 K. Soluções aquosas com diferentes concentrações das nanopartículas e o agente de contraste comercial Lumirem foram preparadas para se obter os tempos de relaxação T1 e T2 e as relaxividades r1 e r2. Nessas medidas, as nanopartículas mostraram efeitos de contraste, perturbando a intensidade de sinal e diminuindo os tempos de relaxação T1 e T2. A razão entre as relaxividades (r2/r1) variaram entre 3,13-64,14, o que está dentro dos valores dos agentes de contrastes de óxido de ferro comercialmente disponíveis. Conclui-se que as nanopartículas avaliadas nesse trabalho são passíveis de serem utilizadas como agente de contraste do tipo T2.Submitted by PPG Engenharia e Tecnologia de Materiais (engenharia.pg.materiais@pucrs.br) on 2019-05-07T16:38:42Z No. of bitstreams: 1 pgetema.modelos.Dissertacao.Versão para Homologação.pdf: 2201385 bytes, checksum: 14e5c2f95194bd9d5292221095cbadb1 (MD5)Approved for entry into archive by Sarajane Pan (sarajane.pan@pucrs.br) on 2019-06-04T13:57:20Z (GMT) No. of bitstreams: 1 pgetema.modelos.Dissertacao.Versão para Homologação.pdf: 2201385 bytes, checksum: 14e5c2f95194bd9d5292221095cbadb1 (MD5)Made available in DSpace on 2019-06-04T14:16:00Z (GMT). No. of bitstreams: 1 pgetema.modelos.Dissertacao.Versão para Homologação.pdf: 2201385 bytes, checksum: 14e5c2f95194bd9d5292221095cbadb1 (MD5) Previous issue date: 2018-01-26Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/175295/pgetema.modelos.Dissertacao.Vers%c3%a3o%20para%20Homologa%c3%a7%c3%a3o.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em Engenharia e Tecnologia de MateriaisPUCRSBrasilEscola PolitécnicaImagem por Ressonância MagnéticaNanopartículas MagnéticasAgentes de ContrasteRelaxividadeMagnetic Resonance ImagingMagnetic NanoparticlesContrast AgentsRelaxivityENGENHARIASRelaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnéticainfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisTrabalho não apresenta restrição para publicação495391460509391966550050060045189710564848268253590462550136975366info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSTHUMBNAILpgetema.modelos.Dissertacao.Versão para Homologação.pdf.jpgpgetema.modelos.Dissertacao.Versão para Homologação.pdf.jpgimage/jpeg5152http://tede2.pucrs.br/tede2/bitstream/tede/8637/5/pgetema.modelos.Dissertacao.Vers%C3%A3o+para+Homologa%C3%A7%C3%A3o.pdf.jpg3ae434c67de9cda21c8af84a0be08dceMD55TEXTpgetema.modelos.Dissertacao.Versão para Homologação.pdf.txtpgetema.modelos.Dissertacao.Versão para Homologação.pdf.txttext/plain123141http://tede2.pucrs.br/tede2/bitstream/tede/8637/4/pgetema.modelos.Dissertacao.Vers%C3%A3o+para+Homologa%C3%A7%C3%A3o.pdf.txt0925f9a051eeaf78bfeff92a3dd5e0f0MD54LICENSElicense.txtlicense.txttext/plain; charset=utf-8590http://tede2.pucrs.br/tede2/bitstream/tede/8637/3/license.txt220e11f2d3ba5354f917c7035aadef24MD53ORIGINALpgetema.modelos.Dissertacao.Versão para Homologação.pdfpgetema.modelos.Dissertacao.Versão para Homologação.pdfapplication/pdf2201385http://tede2.pucrs.br/tede2/bitstream/tede/8637/2/pgetema.modelos.Dissertacao.Vers%C3%A3o+para+Homologa%C3%A7%C3%A3o.pdf14e5c2f95194bd9d5292221095cbadb1MD52tede/86372019-06-04 12:00:41.646oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2019-06-04T15:00:41Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false |
dc.title.por.fl_str_mv |
Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética |
title |
Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética |
spellingShingle |
Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética Rocha, Maximiliano Santos da Imagem por Ressonância Magnética Nanopartículas Magnéticas Agentes de Contraste Relaxividade Magnetic Resonance Imaging Magnetic Nanoparticles Contrast Agents Relaxivity ENGENHARIAS |
title_short |
Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética |
title_full |
Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética |
title_fullStr |
Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética |
title_full_unstemmed |
Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética |
title_sort |
Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética |
author |
Rocha, Maximiliano Santos da |
author_facet |
Rocha, Maximiliano Santos da |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Papaléo, Ricardo Meurer |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/1933730859000512 |
dc.contributor.author.fl_str_mv |
Rocha, Maximiliano Santos da |
contributor_str_mv |
Papaléo, Ricardo Meurer |
dc.subject.por.fl_str_mv |
Imagem por Ressonância Magnética Nanopartículas Magnéticas Agentes de Contraste Relaxividade |
topic |
Imagem por Ressonância Magnética Nanopartículas Magnéticas Agentes de Contraste Relaxividade Magnetic Resonance Imaging Magnetic Nanoparticles Contrast Agents Relaxivity ENGENHARIAS |
dc.subject.eng.fl_str_mv |
Magnetic Resonance Imaging Magnetic Nanoparticles Contrast Agents Relaxivity |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS |
description |
In the present study, some physical characteristics and nuclear magnetic relaxation properties of iron oxide nanoparticles coated with different coatings and synthesized in our laboratories were investigated. Eight nanoparticle systems were obtained, one of these systems being a linked fluorophore group (Cy5.5). Raman spectroscopy and X-rays diffraction have shown that the iron oxide in question is magnetite. The magnetization measurements revealed superparamagnetic behavior of the nanoparticles due to the absence of hysteresis of the nanoparticles and a saturation magnetization ranging from 3.8-61.6 emu/g. The iron concentration of each synthesis was obtained by UV-Vis spectrophotometry and relaxometry and the results obtained ranged from 0.46-11.2 mg/mL. ZFC/FC measurements showed a distribution of the blocking temperature of the nanoparticles not exceeding 50 K. Aqueous solutions with different concentrations of the nanoparticles and the Lumirem commercial contrast agent were prepared to give the relaxation times T1 and T2 and the relaxivities r1 and r2. In these measurements, the nanoparticles showed contrast effects, disturbing the signal intensity, decreasing the relaxation times T1 and T2. The ratio of relaxivities (r2/r1) ranged from 3.13-64.14, which is within the values of the commercially available iron oxide contrast agents. It is concluded that the nanoparticles evaluated in this work are suitable as a T2-type contrast agent. |
publishDate |
2018 |
dc.date.issued.fl_str_mv |
2018-01-26 |
dc.date.accessioned.fl_str_mv |
2019-06-04T14:16:00Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://tede2.pucrs.br/tede2/handle/tede/8637 |
url |
http://tede2.pucrs.br/tede2/handle/tede/8637 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
4953914605093919665 |
dc.relation.confidence.fl_str_mv |
500 500 600 |
dc.relation.cnpq.fl_str_mv |
4518971056484826825 |
dc.relation.sponsorship.fl_str_mv |
3590462550136975366 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais |
dc.publisher.initials.fl_str_mv |
PUCRS |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Escola Politécnica |
publisher.none.fl_str_mv |
Pontifícia Universidade Católica do Rio Grande do Sul |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) instacron:PUC_RS |
instname_str |
Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
instacron_str |
PUC_RS |
institution |
PUC_RS |
reponame_str |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
collection |
Biblioteca Digital de Teses e Dissertações da PUC_RS |
bitstream.url.fl_str_mv |
http://tede2.pucrs.br/tede2/bitstream/tede/8637/5/pgetema.modelos.Dissertacao.Vers%C3%A3o+para+Homologa%C3%A7%C3%A3o.pdf.jpg http://tede2.pucrs.br/tede2/bitstream/tede/8637/4/pgetema.modelos.Dissertacao.Vers%C3%A3o+para+Homologa%C3%A7%C3%A3o.pdf.txt http://tede2.pucrs.br/tede2/bitstream/tede/8637/3/license.txt http://tede2.pucrs.br/tede2/bitstream/tede/8637/2/pgetema.modelos.Dissertacao.Vers%C3%A3o+para+Homologa%C3%A7%C3%A3o.pdf |
bitstream.checksum.fl_str_mv |
3ae434c67de9cda21c8af84a0be08dce 0925f9a051eeaf78bfeff92a3dd5e0f0 220e11f2d3ba5354f917c7035aadef24 14e5c2f95194bd9d5292221095cbadb1 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS) |
repository.mail.fl_str_mv |
biblioteca.central@pucrs.br|| |
_version_ |
1799765339246952448 |