Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética

Detalhes bibliográficos
Autor(a) principal: Rocha, Maximiliano Santos da
Data de Publicação: 2018
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da PUC_RS
Texto Completo: http://tede2.pucrs.br/tede2/handle/tede/8637
Resumo: In the present study, some physical characteristics and nuclear magnetic relaxation properties of iron oxide nanoparticles coated with different coatings and synthesized in our laboratories were investigated. Eight nanoparticle systems were obtained, one of these systems being a linked fluorophore group (Cy5.5). Raman spectroscopy and X-rays diffraction have shown that the iron oxide in question is magnetite. The magnetization measurements revealed superparamagnetic behavior of the nanoparticles due to the absence of hysteresis of the nanoparticles and a saturation magnetization ranging from 3.8-61.6 emu/g. The iron concentration of each synthesis was obtained by UV-Vis spectrophotometry and relaxometry and the results obtained ranged from 0.46-11.2 mg/mL. ZFC/FC measurements showed a distribution of the blocking temperature of the nanoparticles not exceeding 50 K. Aqueous solutions with different concentrations of the nanoparticles and the Lumirem commercial contrast agent were prepared to give the relaxation times T1 and T2 and the relaxivities r1 and r2. In these measurements, the nanoparticles showed contrast effects, disturbing the signal intensity, decreasing the relaxation times T1 and T2. The ratio of relaxivities (r2/r1) ranged from 3.13-64.14, which is within the values of the commercially available iron oxide contrast agents. It is concluded that the nanoparticles evaluated in this work are suitable as a T2-type contrast agent.
id P_RS_a1cdab5e5233480f5704e3c78393f936
oai_identifier_str oai:tede2.pucrs.br:tede/8637
network_acronym_str P_RS
network_name_str Biblioteca Digital de Teses e Dissertações da PUC_RS
repository_id_str
spelling Papaléo, Ricardo Meurerhttp://lattes.cnpq.br/1933730859000512Rocha, Maximiliano Santos da2019-06-04T14:16:00Z2018-01-26http://tede2.pucrs.br/tede2/handle/tede/8637In the present study, some physical characteristics and nuclear magnetic relaxation properties of iron oxide nanoparticles coated with different coatings and synthesized in our laboratories were investigated. Eight nanoparticle systems were obtained, one of these systems being a linked fluorophore group (Cy5.5). Raman spectroscopy and X-rays diffraction have shown that the iron oxide in question is magnetite. The magnetization measurements revealed superparamagnetic behavior of the nanoparticles due to the absence of hysteresis of the nanoparticles and a saturation magnetization ranging from 3.8-61.6 emu/g. The iron concentration of each synthesis was obtained by UV-Vis spectrophotometry and relaxometry and the results obtained ranged from 0.46-11.2 mg/mL. ZFC/FC measurements showed a distribution of the blocking temperature of the nanoparticles not exceeding 50 K. Aqueous solutions with different concentrations of the nanoparticles and the Lumirem commercial contrast agent were prepared to give the relaxation times T1 and T2 and the relaxivities r1 and r2. In these measurements, the nanoparticles showed contrast effects, disturbing the signal intensity, decreasing the relaxation times T1 and T2. The ratio of relaxivities (r2/r1) ranged from 3.13-64.14, which is within the values of the commercially available iron oxide contrast agents. It is concluded that the nanoparticles evaluated in this work are suitable as a T2-type contrast agent.No presente estudo, algumas características físicas e propriedades de relaxação magnética nuclear de nanopartículas de óxido de ferro revestidas com diferentes recobrimentos e sintetizadas em nossos laboratórios foram investigadas. Obtiveram-se oito sistemas de nanopartículas, sendo um destes sistemas com um grupo fluoróforo ligado (Cy5.5). Análises de espectroscopia Raman e difração de raios-X demonstraram que o óxido de ferro em questão é a magnetita. As medidas de magnetização revelaram comportamento superparamagnético das nanopartículas, devido à ausência de histerese das mesmas, e uma magnetização de saturação variando entre 3,8-61,6 emu/g. A concentração de ferro de cada síntese foi obtida por espectrofotometria UV-Vis e relaxometria. Os resultados obtidos variaram entre 0,46-11,2 mg/mL. Medidas de ZFC/FC demonstraram uma distribuição de temperaturas de bloqueio das nanopartículas não excedendo 50 K. Soluções aquosas com diferentes concentrações das nanopartículas e o agente de contraste comercial Lumirem foram preparadas para se obter os tempos de relaxação T1 e T2 e as relaxividades r1 e r2. Nessas medidas, as nanopartículas mostraram efeitos de contraste, perturbando a intensidade de sinal e diminuindo os tempos de relaxação T1 e T2. A razão entre as relaxividades (r2/r1) variaram entre 3,13-64,14, o que está dentro dos valores dos agentes de contrastes de óxido de ferro comercialmente disponíveis. Conclui-se que as nanopartículas avaliadas nesse trabalho são passíveis de serem utilizadas como agente de contraste do tipo T2.Submitted by PPG Engenharia e Tecnologia de Materiais (engenharia.pg.materiais@pucrs.br) on 2019-05-07T16:38:42Z No. of bitstreams: 1 pgetema.modelos.Dissertacao.Versão para Homologação.pdf: 2201385 bytes, checksum: 14e5c2f95194bd9d5292221095cbadb1 (MD5)Approved for entry into archive by Sarajane Pan (sarajane.pan@pucrs.br) on 2019-06-04T13:57:20Z (GMT) No. of bitstreams: 1 pgetema.modelos.Dissertacao.Versão para Homologação.pdf: 2201385 bytes, checksum: 14e5c2f95194bd9d5292221095cbadb1 (MD5)Made available in DSpace on 2019-06-04T14:16:00Z (GMT). No. of bitstreams: 1 pgetema.modelos.Dissertacao.Versão para Homologação.pdf: 2201385 bytes, checksum: 14e5c2f95194bd9d5292221095cbadb1 (MD5) Previous issue date: 2018-01-26Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://tede2.pucrs.br:80/tede2/retrieve/175295/pgetema.modelos.Dissertacao.Vers%c3%a3o%20para%20Homologa%c3%a7%c3%a3o.pdf.jpgporPontifícia Universidade Católica do Rio Grande do SulPrograma de Pós-Graduação em Engenharia e Tecnologia de MateriaisPUCRSBrasilEscola PolitécnicaImagem por Ressonância MagnéticaNanopartículas MagnéticasAgentes de ContrasteRelaxividadeMagnetic Resonance ImagingMagnetic NanoparticlesContrast AgentsRelaxivityENGENHARIASRelaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnéticainfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisTrabalho não apresenta restrição para publicação495391460509391966550050060045189710564848268253590462550136975366info:eu-repo/semantics/openAccessreponame:Biblioteca Digital de Teses e Dissertações da PUC_RSinstname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)instacron:PUC_RSTHUMBNAILpgetema.modelos.Dissertacao.Versão para Homologação.pdf.jpgpgetema.modelos.Dissertacao.Versão para Homologação.pdf.jpgimage/jpeg5152http://tede2.pucrs.br/tede2/bitstream/tede/8637/5/pgetema.modelos.Dissertacao.Vers%C3%A3o+para+Homologa%C3%A7%C3%A3o.pdf.jpg3ae434c67de9cda21c8af84a0be08dceMD55TEXTpgetema.modelos.Dissertacao.Versão para Homologação.pdf.txtpgetema.modelos.Dissertacao.Versão para Homologação.pdf.txttext/plain123141http://tede2.pucrs.br/tede2/bitstream/tede/8637/4/pgetema.modelos.Dissertacao.Vers%C3%A3o+para+Homologa%C3%A7%C3%A3o.pdf.txt0925f9a051eeaf78bfeff92a3dd5e0f0MD54LICENSElicense.txtlicense.txttext/plain; charset=utf-8590http://tede2.pucrs.br/tede2/bitstream/tede/8637/3/license.txt220e11f2d3ba5354f917c7035aadef24MD53ORIGINALpgetema.modelos.Dissertacao.Versão para Homologação.pdfpgetema.modelos.Dissertacao.Versão para Homologação.pdfapplication/pdf2201385http://tede2.pucrs.br/tede2/bitstream/tede/8637/2/pgetema.modelos.Dissertacao.Vers%C3%A3o+para+Homologa%C3%A7%C3%A3o.pdf14e5c2f95194bd9d5292221095cbadb1MD52tede/86372019-06-04 12:00:41.646oai:tede2.pucrs.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede2.pucrs.br/tede2/PRIhttps://tede2.pucrs.br/oai/requestbiblioteca.central@pucrs.br||opendoar:2019-06-04T15:00:41Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)false
dc.title.por.fl_str_mv Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética
title Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética
spellingShingle Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética
Rocha, Maximiliano Santos da
Imagem por Ressonância Magnética
Nanopartículas Magnéticas
Agentes de Contraste
Relaxividade
Magnetic Resonance Imaging
Magnetic Nanoparticles
Contrast Agents
Relaxivity
ENGENHARIAS
title_short Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética
title_full Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética
title_fullStr Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética
title_full_unstemmed Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética
title_sort Relaxividade de nanopartículas de óxido de ferro com diferentes recobrimentos em equipamentos clínicos de ressonância magnética
author Rocha, Maximiliano Santos da
author_facet Rocha, Maximiliano Santos da
author_role author
dc.contributor.advisor1.fl_str_mv Papaléo, Ricardo Meurer
dc.contributor.advisor1Lattes.fl_str_mv http://lattes.cnpq.br/1933730859000512
dc.contributor.author.fl_str_mv Rocha, Maximiliano Santos da
contributor_str_mv Papaléo, Ricardo Meurer
dc.subject.por.fl_str_mv Imagem por Ressonância Magnética
Nanopartículas Magnéticas
Agentes de Contraste
Relaxividade
topic Imagem por Ressonância Magnética
Nanopartículas Magnéticas
Agentes de Contraste
Relaxividade
Magnetic Resonance Imaging
Magnetic Nanoparticles
Contrast Agents
Relaxivity
ENGENHARIAS
dc.subject.eng.fl_str_mv Magnetic Resonance Imaging
Magnetic Nanoparticles
Contrast Agents
Relaxivity
dc.subject.cnpq.fl_str_mv ENGENHARIAS
description In the present study, some physical characteristics and nuclear magnetic relaxation properties of iron oxide nanoparticles coated with different coatings and synthesized in our laboratories were investigated. Eight nanoparticle systems were obtained, one of these systems being a linked fluorophore group (Cy5.5). Raman spectroscopy and X-rays diffraction have shown that the iron oxide in question is magnetite. The magnetization measurements revealed superparamagnetic behavior of the nanoparticles due to the absence of hysteresis of the nanoparticles and a saturation magnetization ranging from 3.8-61.6 emu/g. The iron concentration of each synthesis was obtained by UV-Vis spectrophotometry and relaxometry and the results obtained ranged from 0.46-11.2 mg/mL. ZFC/FC measurements showed a distribution of the blocking temperature of the nanoparticles not exceeding 50 K. Aqueous solutions with different concentrations of the nanoparticles and the Lumirem commercial contrast agent were prepared to give the relaxation times T1 and T2 and the relaxivities r1 and r2. In these measurements, the nanoparticles showed contrast effects, disturbing the signal intensity, decreasing the relaxation times T1 and T2. The ratio of relaxivities (r2/r1) ranged from 3.13-64.14, which is within the values of the commercially available iron oxide contrast agents. It is concluded that the nanoparticles evaluated in this work are suitable as a T2-type contrast agent.
publishDate 2018
dc.date.issued.fl_str_mv 2018-01-26
dc.date.accessioned.fl_str_mv 2019-06-04T14:16:00Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://tede2.pucrs.br/tede2/handle/tede/8637
url http://tede2.pucrs.br/tede2/handle/tede/8637
dc.language.iso.fl_str_mv por
language por
dc.relation.program.fl_str_mv 4953914605093919665
dc.relation.confidence.fl_str_mv 500
500
600
dc.relation.cnpq.fl_str_mv 4518971056484826825
dc.relation.sponsorship.fl_str_mv 3590462550136975366
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.publisher.none.fl_str_mv Pontifícia Universidade Católica do Rio Grande do Sul
dc.publisher.program.fl_str_mv Programa de Pós-Graduação em Engenharia e Tecnologia de Materiais
dc.publisher.initials.fl_str_mv PUCRS
dc.publisher.country.fl_str_mv Brasil
dc.publisher.department.fl_str_mv Escola Politécnica
publisher.none.fl_str_mv Pontifícia Universidade Católica do Rio Grande do Sul
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS
instname:Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
instacron:PUC_RS
instname_str Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
instacron_str PUC_RS
institution PUC_RS
reponame_str Biblioteca Digital de Teses e Dissertações da PUC_RS
collection Biblioteca Digital de Teses e Dissertações da PUC_RS
bitstream.url.fl_str_mv http://tede2.pucrs.br/tede2/bitstream/tede/8637/5/pgetema.modelos.Dissertacao.Vers%C3%A3o+para+Homologa%C3%A7%C3%A3o.pdf.jpg
http://tede2.pucrs.br/tede2/bitstream/tede/8637/4/pgetema.modelos.Dissertacao.Vers%C3%A3o+para+Homologa%C3%A7%C3%A3o.pdf.txt
http://tede2.pucrs.br/tede2/bitstream/tede/8637/3/license.txt
http://tede2.pucrs.br/tede2/bitstream/tede/8637/2/pgetema.modelos.Dissertacao.Vers%C3%A3o+para+Homologa%C3%A7%C3%A3o.pdf
bitstream.checksum.fl_str_mv 3ae434c67de9cda21c8af84a0be08dce
0925f9a051eeaf78bfeff92a3dd5e0f0
220e11f2d3ba5354f917c7035aadef24
14e5c2f95194bd9d5292221095cbadb1
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
MD5
MD5
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da PUC_RS - Pontifícia Universidade Católica do Rio Grande do Sul (PUCRS)
repository.mail.fl_str_mv biblioteca.central@pucrs.br||
_version_ 1799765339246952448

Registros relacionados