Alkali-activated binary mortar based on natural volcanic pozzolan for repair applications
Autor(a) principal: | |
---|---|
Data de Publicação: | 2019 |
Outros Autores: | , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
Texto Completo: | https://hdl.handle.net/1822/60386 |
Resumo: | The goal of this investigation was evaluate the potential of an alkali-activated binary mortar (AABM), based on a natural volcanic pozzolan (70%) and granulated blast furnace slag (30%), as a repair material. This evaluation focused on its physico-mechanical characterisation (compressive, flexural and splitting tensile strengths; modulus of elasticity; capillary water absorption; and shrinkage) and the measurement of its adherence to three class of OPC concretes (substrates) using pull-off tests. A mixture of NaOH and Na2SiO3 was used as alkaline activator. The compressive and splitting tensile strength of AABM were 34.8?MPa and 2.13?MPa?at 28 days of curing, respectively. Its capillary absorption coefficient and modulus of elasticity were 0.5088?kg/m2h0.5 and 8.66?GPa respectively. The results of the pull-off test demonstrate the adherent nature of the AABM, which was promoted by the strength (quality) of the OPC substrate, with pull-off adherences of 0.75?MPa, 1.14?MPa and 1.24?MPa for class C25/30, C35/45 and C50/60, respectively. According to the results obtained and standard specifications (EN 1504-3), this material can be classified as a class R2-repair mortar. |
id |
RCAP_1fe59d76732004722735fa1fde3c32e9 |
---|---|
oai_identifier_str |
oai:repositorium.sdum.uminho.pt:1822/60386 |
network_acronym_str |
RCAP |
network_name_str |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
repository_id_str |
7160 |
spelling |
Alkali-activated binary mortar based on natural volcanic pozzolan for repair applicationsAlkali-activated materialsCoating mortarNatural volcanic pozzolanPull-offRepair mortarScience & TechnologyThe goal of this investigation was evaluate the potential of an alkali-activated binary mortar (AABM), based on a natural volcanic pozzolan (70%) and granulated blast furnace slag (30%), as a repair material. This evaluation focused on its physico-mechanical characterisation (compressive, flexural and splitting tensile strengths; modulus of elasticity; capillary water absorption; and shrinkage) and the measurement of its adherence to three class of OPC concretes (substrates) using pull-off tests. A mixture of NaOH and Na2SiO3 was used as alkaline activator. The compressive and splitting tensile strength of AABM were 34.8?MPa and 2.13?MPa?at 28 days of curing, respectively. Its capillary absorption coefficient and modulus of elasticity were 0.5088?kg/m2h0.5 and 8.66?GPa respectively. The results of the pull-off test demonstrate the adherent nature of the AABM, which was promoted by the strength (quality) of the OPC substrate, with pull-off adherences of 0.75?MPa, 1.14?MPa and 1.24?MPa for class C25/30, C35/45 and C50/60, respectively. According to the results obtained and standard specifications (EN 1504-3), this material can be classified as a class R2-repair mortar.COLCIENCIAS -Departamento Administrativo de Ciencia, Tecnología e Innovación(undefined)info:eu-repo/semantics/publishedVersionElsevierUniversidade do MinhoRobayo-Salazar, RafaelJesús, CarlosMejía de Gutierrez, RubyPacheco-Torgal, F.20192019-01-01T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/articleapplication/pdfhttps://hdl.handle.net/1822/60386engRobayo-Salazar R., Jesus C., de Gutierrez R., Pacheco-Torgal F. Alkali-activated binary mortar based on natural volcanic pozzolan for repair applications, Journal of Building Engineering, Vol. 25, Issue 1, pp. 1-17, doi:10.1016/j.jobe.2019.100785, 20192352-710210.1016/j.jobe.2019.100785https://www.sciencedirect.com/science/article/pii/S2352710218309410info:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-07-21T12:33:24Zoai:repositorium.sdum.uminho.pt:1822/60386Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T19:28:54.811513Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse |
dc.title.none.fl_str_mv |
Alkali-activated binary mortar based on natural volcanic pozzolan for repair applications |
title |
Alkali-activated binary mortar based on natural volcanic pozzolan for repair applications |
spellingShingle |
Alkali-activated binary mortar based on natural volcanic pozzolan for repair applications Robayo-Salazar, Rafael Alkali-activated materials Coating mortar Natural volcanic pozzolan Pull-off Repair mortar Science & Technology |
title_short |
Alkali-activated binary mortar based on natural volcanic pozzolan for repair applications |
title_full |
Alkali-activated binary mortar based on natural volcanic pozzolan for repair applications |
title_fullStr |
Alkali-activated binary mortar based on natural volcanic pozzolan for repair applications |
title_full_unstemmed |
Alkali-activated binary mortar based on natural volcanic pozzolan for repair applications |
title_sort |
Alkali-activated binary mortar based on natural volcanic pozzolan for repair applications |
author |
Robayo-Salazar, Rafael |
author_facet |
Robayo-Salazar, Rafael Jesús, Carlos Mejía de Gutierrez, Ruby Pacheco-Torgal, F. |
author_role |
author |
author2 |
Jesús, Carlos Mejía de Gutierrez, Ruby Pacheco-Torgal, F. |
author2_role |
author author author |
dc.contributor.none.fl_str_mv |
Universidade do Minho |
dc.contributor.author.fl_str_mv |
Robayo-Salazar, Rafael Jesús, Carlos Mejía de Gutierrez, Ruby Pacheco-Torgal, F. |
dc.subject.por.fl_str_mv |
Alkali-activated materials Coating mortar Natural volcanic pozzolan Pull-off Repair mortar Science & Technology |
topic |
Alkali-activated materials Coating mortar Natural volcanic pozzolan Pull-off Repair mortar Science & Technology |
description |
The goal of this investigation was evaluate the potential of an alkali-activated binary mortar (AABM), based on a natural volcanic pozzolan (70%) and granulated blast furnace slag (30%), as a repair material. This evaluation focused on its physico-mechanical characterisation (compressive, flexural and splitting tensile strengths; modulus of elasticity; capillary water absorption; and shrinkage) and the measurement of its adherence to three class of OPC concretes (substrates) using pull-off tests. A mixture of NaOH and Na2SiO3 was used as alkaline activator. The compressive and splitting tensile strength of AABM were 34.8?MPa and 2.13?MPa?at 28 days of curing, respectively. Its capillary absorption coefficient and modulus of elasticity were 0.5088?kg/m2h0.5 and 8.66?GPa respectively. The results of the pull-off test demonstrate the adherent nature of the AABM, which was promoted by the strength (quality) of the OPC substrate, with pull-off adherences of 0.75?MPa, 1.14?MPa and 1.24?MPa for class C25/30, C35/45 and C50/60, respectively. According to the results obtained and standard specifications (EN 1504-3), this material can be classified as a class R2-repair mortar. |
publishDate |
2019 |
dc.date.none.fl_str_mv |
2019 2019-01-01T00:00:00Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
https://hdl.handle.net/1822/60386 |
url |
https://hdl.handle.net/1822/60386 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
Robayo-Salazar R., Jesus C., de Gutierrez R., Pacheco-Torgal F. Alkali-activated binary mortar based on natural volcanic pozzolan for repair applications, Journal of Building Engineering, Vol. 25, Issue 1, pp. 1-17, doi:10.1016/j.jobe.2019.100785, 2019 2352-7102 10.1016/j.jobe.2019.100785 https://www.sciencedirect.com/science/article/pii/S2352710218309410 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Elsevier |
publisher.none.fl_str_mv |
Elsevier |
dc.source.none.fl_str_mv |
reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação instacron:RCAAP |
instname_str |
Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação |
instacron_str |
RCAAP |
institution |
RCAAP |
reponame_str |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
collection |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) |
repository.name.fl_str_mv |
Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação |
repository.mail.fl_str_mv |
|
_version_ |
1799132787019612160 |