Desenvolvimento de compósitos de biopolímeros e cargas naturais para termoformação de alvéolos de fruta

Detalhes bibliográficos
Autor(a) principal: Barbosa, Sara de Jesus Costa
Data de Publicação: 2023
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: https://hdl.handle.net/1822/82740
Resumo: Dissertação de mestrado em Engenharia de Polímeros
id RCAP_4626b21d8c3fcdb8c9ab69d83ae1e578
oai_identifier_str oai:repositorium.sdum.uminho.pt:1822/82740
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Desenvolvimento de compósitos de biopolímeros e cargas naturais para termoformação de alvéolos de frutaDevelopment of composites of biopolymers and natural fillers for thermoforming fruit alveoliBiocompósitosBiopolímerosCascas de caféTermoformabilideBiocompositesBiopolymersCoffee husksThermoformabiltyEngenharia e Tecnologia::Engenharia dos MateriaisDissertação de mestrado em Engenharia de PolímerosSendo o café uma das bebidas mais consumidas em todo o mundo, engloba um grande mercado mundial, e gera enormes quantidades de resíduos sólidos, como as cacas de café (CC), entre outros. Como estes resíduos são constituídos por compostos orgânicos, podem ser reaproveitados e valorizados. Assim, uma das possíveis utilizações, consiste na produção de materiais compósitos de matriz biopolimérica, com o objetivo de produção de vários produtos que inovam pelo aspeto, textura e até cheiro, ao introduzir as cascas de café nas suas misturas de biopolímeros. O trabalho realizado focou se na produção de compósitos com o biopolímero Inzea F38 da Nurel, um aditivo de acoplamento, Vinnex 8880 da Wacker e cascas de café com diferentes taxas de incorporação, 5%, 10% e 15%. Numa primeira fase, preparam-se dois masterbatch com 50% de carga, um com o F38 e outro o Vinnex. Na segunda fase do trabalho, foram preparadas por extrusão as várias composições em forma de folha, diluindo nas proporções adequadas o masterbatch para se obter composições com 5%, 10% e 15% de carga. Para a caracterização mecânica dos materiais compósitos foram preparados provetes a partir das folhas, cortados no sentido da extrusão e no sentido perpendicular ao da extrusão. Os resultados de tração mostraram que a ductilidade do material aumenta na direção transversal ao fluxo. Os ensaios de distribuição das cargas na folha, observados através da passagem de luz, mostraram uma distribuição homogénea. A adesão carga/matriz foi observada por SEM em amostras cortadas em folhas antes de termoformar e em regiões das peças termoformadas que sofrerem maior deformação. Em ambas as situações, antes e depois de termoformar, os resultados mostraram uma excelente compatibilidade e adesão entre a carga e a matriz polimérica. A presença do aditivo, também identificada nas imagens de SEM como uma fase não miscível e muito bem distribuída, facilita o processo de adesão. A termoformabilidade dos materiais compósitos foi estudada termoformando as folhas obtidas, usando um molde protótipo com diferentes razões de estiramento e a várias temperaturas. Os resultados mostraram um excelente comportamento à termoformabilidade num intervalo de temperaturas de cerca de 20ᵒC. Os testes de resistência à degradação em água e em terra, não mostraram vestígios de degradação nas amostras com aditivo.As coffee is one of the most consumed beverages in the world, includes a large world market, and generates huge amounts of solid waste, such as coffee husks, among others. As these residues are organic, they can be reused and consequently valued. So, one of its possible uses is the production of biopolymer matrix compounds, with the aim of producing various products that innovate in terms of appearance, texture and even smell, by introducing coffee husks into their biopolymer mixtures. The realized work focused on the production of composites with the biopolymer Inzea F38 from Nurel, a cuppling additive, Vinnex 8880 from Wacker, and coffee husks with different incorporation rates, 5%, 10% and 15%. In a first phase, two masterbatch were prepared with 50% filler, one with F38 and the other with Vinnex. In the second phase of the work, the various compositions in sheet form were prepared by extrusion, diluting the masterbatch in the appropriate proportions to obtain compositions with 5%, 10% and 15% filler. For the mechanical characterization of the composite materials, test pieces were prepared from the sheets, cut in the direction of the extrusion and in perpendicular to extrusion direction. The tensile results showed that the ductility of the material increases in the transverse direction to the flow. The tests on the distribution of coffee husk particles on the sheet, observed through the passage of light, showed a homogeneous distribution. Filler/matrix adhesion was observed by SEM in samples cut into sheets before thermoforming and in regions of thermoformed parts that undergo greater deformation. In both situations, before and after thermoforming, the results showed excellent compatibility and adhesion between the filler and the polymer matrix. The presence of the additive, also identified in the SEM images as an immiscible and very well distributed phase, facilitates the adhesion process. The thermoformability of composite materials was studied by thermoforming the obtained sheets, using a prototype mold with diferente strech ratios and at various temperatures. The results showed excellent thermoformability behavior in a temperature range of about 20˚C. Tests of resistance to degradation in water and on land, showed no traces of degradation in samples with additive.Duarte, F. M.Pontes, A. J.Universidade do MinhoBarbosa, Sara de Jesus Costa2023-01-202023-01-20T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttps://hdl.handle.net/1822/82740por203147065info:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-07-21T12:06:51Zoai:repositorium.sdum.uminho.pt:1822/82740Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T18:57:40.317459Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Desenvolvimento de compósitos de biopolímeros e cargas naturais para termoformação de alvéolos de fruta
Development of composites of biopolymers and natural fillers for thermoforming fruit alveoli
title Desenvolvimento de compósitos de biopolímeros e cargas naturais para termoformação de alvéolos de fruta
spellingShingle Desenvolvimento de compósitos de biopolímeros e cargas naturais para termoformação de alvéolos de fruta
Barbosa, Sara de Jesus Costa
Biocompósitos
Biopolímeros
Cascas de café
Termoformabilide
Biocomposites
Biopolymers
Coffee husks
Thermoformabilty
Engenharia e Tecnologia::Engenharia dos Materiais
title_short Desenvolvimento de compósitos de biopolímeros e cargas naturais para termoformação de alvéolos de fruta
title_full Desenvolvimento de compósitos de biopolímeros e cargas naturais para termoformação de alvéolos de fruta
title_fullStr Desenvolvimento de compósitos de biopolímeros e cargas naturais para termoformação de alvéolos de fruta
title_full_unstemmed Desenvolvimento de compósitos de biopolímeros e cargas naturais para termoformação de alvéolos de fruta
title_sort Desenvolvimento de compósitos de biopolímeros e cargas naturais para termoformação de alvéolos de fruta
author Barbosa, Sara de Jesus Costa
author_facet Barbosa, Sara de Jesus Costa
author_role author
dc.contributor.none.fl_str_mv Duarte, F. M.
Pontes, A. J.
Universidade do Minho
dc.contributor.author.fl_str_mv Barbosa, Sara de Jesus Costa
dc.subject.por.fl_str_mv Biocompósitos
Biopolímeros
Cascas de café
Termoformabilide
Biocomposites
Biopolymers
Coffee husks
Thermoformabilty
Engenharia e Tecnologia::Engenharia dos Materiais
topic Biocompósitos
Biopolímeros
Cascas de café
Termoformabilide
Biocomposites
Biopolymers
Coffee husks
Thermoformabilty
Engenharia e Tecnologia::Engenharia dos Materiais
description Dissertação de mestrado em Engenharia de Polímeros
publishDate 2023
dc.date.none.fl_str_mv 2023-01-20
2023-01-20T00:00:00Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/1822/82740
url https://hdl.handle.net/1822/82740
dc.language.iso.fl_str_mv por
language por
dc.relation.none.fl_str_mv 203147065
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799132365505691648

Registros relacionados