Influence of composite restorative materials and light-curing units on diametrical tensile strength
Autor(a) principal: | |
---|---|
Data de Publicação: | 2005 |
Outros Autores: | , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Brazilian Oral Research |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242005000200009 |
Resumo: | The aim of this study was to evaluate the diametrical tensile strength (DTS) of three light-curing photo-activated composites with two different light curing units (LCU). Three types of dental restorative composites were used in this study: micro filled A110 (3M Espe); P60 (3M Espe) for posterior restorations, and micro-hybrid Charisma (Heraeus-Kulzer). The two LCUs were: halogen light (HAL) (Degulux, Degussa) and blue light emitting diode (LED) (Ultrablue, DMC). Resin composite specimens were inserted incrementally into a Teflon split mold meas-uring 3 mm in depth and 6 mm in internal diameter, and cured using either LCU (n = 10). Specimens were placed into a dark bottle containing distilled water at 37°C for 7 days. DTS tests were performed in a Universal Testing Machine (0.5 mm/min). Data were submitted to two-way ANOVA and Tukey's test. Results were (MPa): A110/HAL: 276.50 ± 62.94ª; A110/LED: 306.01 ± 65.16ª; P60/HAL: 568.29 ± 60.77b and P60/LED: 543.01 ± 83.65b; Charisma/HAL: 430.94 ± 67.28c; Charisma/LED: 435.52 ± 105.12c. Results suggested that no significant difference in DTS was obtained with LCUs for the same composite. However, resin composite restorative materials presented different DTS. |
id |
SBPQO-1_fa08e3ea63afacd0fc68c7a98493dac2 |
---|---|
oai_identifier_str |
oai:scielo:S1806-83242005000200009 |
network_acronym_str |
SBPQO-1 |
network_name_str |
Brazilian Oral Research |
repository_id_str |
|
spelling |
Influence of composite restorative materials and light-curing units on diametrical tensile strengthLight emitting diodeComposite resinsDiametrical tensile strengthMechanical propertiesThe aim of this study was to evaluate the diametrical tensile strength (DTS) of three light-curing photo-activated composites with two different light curing units (LCU). Three types of dental restorative composites were used in this study: micro filled A110 (3M Espe); P60 (3M Espe) for posterior restorations, and micro-hybrid Charisma (Heraeus-Kulzer). The two LCUs were: halogen light (HAL) (Degulux, Degussa) and blue light emitting diode (LED) (Ultrablue, DMC). Resin composite specimens were inserted incrementally into a Teflon split mold meas-uring 3 mm in depth and 6 mm in internal diameter, and cured using either LCU (n = 10). Specimens were placed into a dark bottle containing distilled water at 37°C for 7 days. DTS tests were performed in a Universal Testing Machine (0.5 mm/min). Data were submitted to two-way ANOVA and Tukey's test. Results were (MPa): A110/HAL: 276.50 ± 62.94ª; A110/LED: 306.01 ± 65.16ª; P60/HAL: 568.29 ± 60.77b and P60/LED: 543.01 ± 83.65b; Charisma/HAL: 430.94 ± 67.28c; Charisma/LED: 435.52 ± 105.12c. Results suggested that no significant difference in DTS was obtained with LCUs for the same composite. However, resin composite restorative materials presented different DTS.Sociedade Brasileira de Pesquisa Odontológica - SBPqO2005-06-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242005000200009Brazilian Oral Research v.19 n.2 2005reponame:Brazilian Oral Researchinstname:Sociedade Brasileira de Pesquisa Odontológica (SBPqO)instacron:SBPQO10.1590/S1806-83242005000200009info:eu-repo/semantics/openAccessTolosa,Maria Cecília Caldas GiorgiPaulillo,Luís Alexandre Maffei SartiniGiannini,MarceloSantos,Alex José Souza dosDias,Carlos Tadeu dos Santoseng2005-09-08T00:00:00Zoai:scielo:S1806-83242005000200009Revistahttps://www.scielo.br/j/bor/https://old.scielo.br/oai/scielo-oai.phppob@edu.usp.br||bor@sbpqo.org.br1807-31071806-8324opendoar:2005-09-08T00:00Brazilian Oral Research - Sociedade Brasileira de Pesquisa Odontológica (SBPqO)false |
dc.title.none.fl_str_mv |
Influence of composite restorative materials and light-curing units on diametrical tensile strength |
title |
Influence of composite restorative materials and light-curing units on diametrical tensile strength |
spellingShingle |
Influence of composite restorative materials and light-curing units on diametrical tensile strength Tolosa,Maria Cecília Caldas Giorgi Light emitting diode Composite resins Diametrical tensile strength Mechanical properties |
title_short |
Influence of composite restorative materials and light-curing units on diametrical tensile strength |
title_full |
Influence of composite restorative materials and light-curing units on diametrical tensile strength |
title_fullStr |
Influence of composite restorative materials and light-curing units on diametrical tensile strength |
title_full_unstemmed |
Influence of composite restorative materials and light-curing units on diametrical tensile strength |
title_sort |
Influence of composite restorative materials and light-curing units on diametrical tensile strength |
author |
Tolosa,Maria Cecília Caldas Giorgi |
author_facet |
Tolosa,Maria Cecília Caldas Giorgi Paulillo,Luís Alexandre Maffei Sartini Giannini,Marcelo Santos,Alex José Souza dos Dias,Carlos Tadeu dos Santos |
author_role |
author |
author2 |
Paulillo,Luís Alexandre Maffei Sartini Giannini,Marcelo Santos,Alex José Souza dos Dias,Carlos Tadeu dos Santos |
author2_role |
author author author author |
dc.contributor.author.fl_str_mv |
Tolosa,Maria Cecília Caldas Giorgi Paulillo,Luís Alexandre Maffei Sartini Giannini,Marcelo Santos,Alex José Souza dos Dias,Carlos Tadeu dos Santos |
dc.subject.por.fl_str_mv |
Light emitting diode Composite resins Diametrical tensile strength Mechanical properties |
topic |
Light emitting diode Composite resins Diametrical tensile strength Mechanical properties |
description |
The aim of this study was to evaluate the diametrical tensile strength (DTS) of three light-curing photo-activated composites with two different light curing units (LCU). Three types of dental restorative composites were used in this study: micro filled A110 (3M Espe); P60 (3M Espe) for posterior restorations, and micro-hybrid Charisma (Heraeus-Kulzer). The two LCUs were: halogen light (HAL) (Degulux, Degussa) and blue light emitting diode (LED) (Ultrablue, DMC). Resin composite specimens were inserted incrementally into a Teflon split mold meas-uring 3 mm in depth and 6 mm in internal diameter, and cured using either LCU (n = 10). Specimens were placed into a dark bottle containing distilled water at 37°C for 7 days. DTS tests were performed in a Universal Testing Machine (0.5 mm/min). Data were submitted to two-way ANOVA and Tukey's test. Results were (MPa): A110/HAL: 276.50 ± 62.94ª; A110/LED: 306.01 ± 65.16ª; P60/HAL: 568.29 ± 60.77b and P60/LED: 543.01 ± 83.65b; Charisma/HAL: 430.94 ± 67.28c; Charisma/LED: 435.52 ± 105.12c. Results suggested that no significant difference in DTS was obtained with LCUs for the same composite. However, resin composite restorative materials presented different DTS. |
publishDate |
2005 |
dc.date.none.fl_str_mv |
2005-06-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242005000200009 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1806-83242005000200009 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/S1806-83242005000200009 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
Sociedade Brasileira de Pesquisa Odontológica - SBPqO |
publisher.none.fl_str_mv |
Sociedade Brasileira de Pesquisa Odontológica - SBPqO |
dc.source.none.fl_str_mv |
Brazilian Oral Research v.19 n.2 2005 reponame:Brazilian Oral Research instname:Sociedade Brasileira de Pesquisa Odontológica (SBPqO) instacron:SBPQO |
instname_str |
Sociedade Brasileira de Pesquisa Odontológica (SBPqO) |
instacron_str |
SBPQO |
institution |
SBPQO |
reponame_str |
Brazilian Oral Research |
collection |
Brazilian Oral Research |
repository.name.fl_str_mv |
Brazilian Oral Research - Sociedade Brasileira de Pesquisa Odontológica (SBPqO) |
repository.mail.fl_str_mv |
pob@edu.usp.br||bor@sbpqo.org.br |
_version_ |
1750318320382377984 |