Avaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Welding
Autor(a) principal: | |
---|---|
Data de Publicação: | 2007 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFSCAR |
Texto Completo: | https://repositorio.ufscar.br/handle/ufscar/764 |
Resumo: | The corrosion resistance of aluminum alloy can be impaired due to intermetallic precipitation during thermal treatment to improve mechanical properties. This work investigates the corrosion resistance of aluminum alloy 2024-T351 and the joint welded by FSW. Microstructural analysis and microhardness tests were made. Intergranular corrosion tests according to ASTM G110-97, exfoliation corrosion tests according to ASTM G 34-01 and stress corrosion cracking in 3.5% NaCl according to ASTM G 129-00, were carried out. Anodic behavior was evaluated by potentiodynamic polarization measurements in 3.5% NaCl solution. It was not detected intermetallic precipitates by electron and optical microscopy. It was also detected that the joint was more severe attacked than the base metal by intergranular corrosion and exfoliation tests. The welded joint was susceptible to stress corrosion cracking in tests carried out with low nominal strain rate of 10-7 s-1. Base metal and the joint in tests carried out in air and in 3.5% NaCl at strain rate of 10-6 s-1 showed ductile behavior, while the joint with strain rate of 10-7 s-1 showed fragile behavior. The polarization test in chloride medium of aluminum alloys didn t show passive breakdown what make difficult to determinate the pitting potential. Polarization curves indicated that the welded joint had lower current density and higher potential than the base metal. In lower potentials pitting was formed majoritary at grain boundaries |
id |
SCAR_a29ae35a51aee9177f073b4a8c56c139 |
---|---|
oai_identifier_str |
oai:repositorio.ufscar.br:ufscar/764 |
network_acronym_str |
SCAR |
network_name_str |
Repositório Institucional da UFSCAR |
repository_id_str |
4322 |
spelling |
Busquim, Thaís de PaulaKuri, Sebastião Eliashttp://genos.cnpq.br:12010/dwlattes/owa/prc_imp_cv_int?f_cod=K4783423D1http://lattes.cnpq.br/85325731643360756536799b-1dd4-4293-98bc-2f0791c221322016-06-02T19:11:49Z2008-05-302016-06-02T19:11:49Z2007-09-14BUSQUIM, Thaís de Paula. Avaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Welding. 2007. 107 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2007.https://repositorio.ufscar.br/handle/ufscar/764The corrosion resistance of aluminum alloy can be impaired due to intermetallic precipitation during thermal treatment to improve mechanical properties. This work investigates the corrosion resistance of aluminum alloy 2024-T351 and the joint welded by FSW. Microstructural analysis and microhardness tests were made. Intergranular corrosion tests according to ASTM G110-97, exfoliation corrosion tests according to ASTM G 34-01 and stress corrosion cracking in 3.5% NaCl according to ASTM G 129-00, were carried out. Anodic behavior was evaluated by potentiodynamic polarization measurements in 3.5% NaCl solution. It was not detected intermetallic precipitates by electron and optical microscopy. It was also detected that the joint was more severe attacked than the base metal by intergranular corrosion and exfoliation tests. The welded joint was susceptible to stress corrosion cracking in tests carried out with low nominal strain rate of 10-7 s-1. Base metal and the joint in tests carried out in air and in 3.5% NaCl at strain rate of 10-6 s-1 showed ductile behavior, while the joint with strain rate of 10-7 s-1 showed fragile behavior. The polarization test in chloride medium of aluminum alloys didn t show passive breakdown what make difficult to determinate the pitting potential. Polarization curves indicated that the welded joint had lower current density and higher potential than the base metal. In lower potentials pitting was formed majoritary at grain boundariesA resistência à corrosão de ligas de alumínio pode ser degradada devido à precipitação de intermetálicos quando submetidas a tratamentos térmicos para elevar a resistência mecânica. Este trabalho investiga a resistência à corrosão da liga de alumínio 2024-T351 e também da junta soldada por FSW. Foram feitos análise microestrutural e microdureza. Foram realizados ensaios de corrosão intergranular segundo a norma ASTM G110-97, corrosão por esfoliação de acordo com a norma ASTM G34-01 e também ensaio de corrosão sob tensão em solução de NaCl 3,5% com taxa de deformação de 10- 6 e 10-7 s-1, segundo a norma ASTM G129-00. O comportamento anódico foi avaliado por testes potenciodinâmicos em solução de NaCl 3,5%. Os precipitados intermetálicos não foram observados por microscopias ótica e eletrônica. Nos ensaios de corrosão intergranular e esfoliação foi observado que a junta soldada sofreu corrosão mais acentuada do que o metal base. A junta soldada foi suscetível a corrosão sob tensão, somente em ensaios realizados com taxa de deformação baixa, de 10-7 s-1. O metal base e a junta ensaiada ao ar e em NaCl 3,5% com taxa de deformação de 10-6 s-1 apresentaram comportamento dútil, enquanto a junta com taxa de deformação 10-7 s-1, apresentou comportamento frágil. Nos ensaios de polarização em meio de cloretos a liga 2024-T351 não foi observado patamar de passivação o que dificultou a determinação do potencial de pite. As curvas de polarização mostraram que a junta soldada possui densidade de corrente menor e maiores potenciais do que o metal base. Em baixos potenciais os pites foram formados preferencialmente nos contornos dos grãosUniversidade Federal de Sao Carlosapplication/pdfporUniversidade Federal de São CarlosPrograma de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEMUFSCarBRCorrosãoLiga de alumínioFSW - (Friction Stir Welding)MicroestruturaResistência à corrosãoENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICAAvaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Weldinginfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-1-1dd65b32b-27ea-44dd-9f6f-c8b3b548e9bainfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFSCARinstname:Universidade Federal de São Carlos (UFSCAR)instacron:UFSCARORIGINAL1795.pdfapplication/pdf5550885https://repositorio.ufscar.br/bitstream/ufscar/764/1/1795.pdf1be0da6e81e9e84eb153d9eafe8f1116MD51THUMBNAIL1795.pdf.jpg1795.pdf.jpgIM Thumbnailimage/jpeg6126https://repositorio.ufscar.br/bitstream/ufscar/764/2/1795.pdf.jpg7273b593df75708efc8ddd7582e60e3bMD52ufscar/7642023-09-18 18:30:39.906oai:repositorio.ufscar.br:ufscar/764Repositório InstitucionalPUBhttps://repositorio.ufscar.br/oai/requestopendoar:43222023-09-18T18:30:39Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR)false |
dc.title.por.fl_str_mv |
Avaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Welding |
title |
Avaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Welding |
spellingShingle |
Avaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Welding Busquim, Thaís de Paula Corrosão Liga de alumínio FSW - (Friction Stir Welding) Microestrutura Resistência à corrosão ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
title_short |
Avaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Welding |
title_full |
Avaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Welding |
title_fullStr |
Avaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Welding |
title_full_unstemmed |
Avaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Welding |
title_sort |
Avaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Welding |
author |
Busquim, Thaís de Paula |
author_facet |
Busquim, Thaís de Paula |
author_role |
author |
dc.contributor.authorlattes.por.fl_str_mv |
http://lattes.cnpq.br/8532573164336075 |
dc.contributor.author.fl_str_mv |
Busquim, Thaís de Paula |
dc.contributor.advisor1.fl_str_mv |
Kuri, Sebastião Elias |
dc.contributor.advisor1Lattes.fl_str_mv |
http://genos.cnpq.br:12010/dwlattes/owa/prc_imp_cv_int?f_cod=K4783423D1 |
dc.contributor.authorID.fl_str_mv |
6536799b-1dd4-4293-98bc-2f0791c22132 |
contributor_str_mv |
Kuri, Sebastião Elias |
dc.subject.por.fl_str_mv |
Corrosão Liga de alumínio FSW - (Friction Stir Welding) Microestrutura Resistência à corrosão |
topic |
Corrosão Liga de alumínio FSW - (Friction Stir Welding) Microestrutura Resistência à corrosão ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
dc.subject.cnpq.fl_str_mv |
ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
description |
The corrosion resistance of aluminum alloy can be impaired due to intermetallic precipitation during thermal treatment to improve mechanical properties. This work investigates the corrosion resistance of aluminum alloy 2024-T351 and the joint welded by FSW. Microstructural analysis and microhardness tests were made. Intergranular corrosion tests according to ASTM G110-97, exfoliation corrosion tests according to ASTM G 34-01 and stress corrosion cracking in 3.5% NaCl according to ASTM G 129-00, were carried out. Anodic behavior was evaluated by potentiodynamic polarization measurements in 3.5% NaCl solution. It was not detected intermetallic precipitates by electron and optical microscopy. It was also detected that the joint was more severe attacked than the base metal by intergranular corrosion and exfoliation tests. The welded joint was susceptible to stress corrosion cracking in tests carried out with low nominal strain rate of 10-7 s-1. Base metal and the joint in tests carried out in air and in 3.5% NaCl at strain rate of 10-6 s-1 showed ductile behavior, while the joint with strain rate of 10-7 s-1 showed fragile behavior. The polarization test in chloride medium of aluminum alloys didn t show passive breakdown what make difficult to determinate the pitting potential. Polarization curves indicated that the welded joint had lower current density and higher potential than the base metal. In lower potentials pitting was formed majoritary at grain boundaries |
publishDate |
2007 |
dc.date.issued.fl_str_mv |
2007-09-14 |
dc.date.available.fl_str_mv |
2008-05-30 2016-06-02T19:11:49Z |
dc.date.accessioned.fl_str_mv |
2016-06-02T19:11:49Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
BUSQUIM, Thaís de Paula. Avaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Welding. 2007. 107 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2007. |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufscar.br/handle/ufscar/764 |
identifier_str_mv |
BUSQUIM, Thaís de Paula. Avaliação da resistência à corrosão da liga 2024-T351 soldada por FSW Friction Stir Welding. 2007. 107 f. Dissertação (Mestrado em Ciências Exatas e da Terra) - Universidade Federal de São Carlos, São Carlos, 2007. |
url |
https://repositorio.ufscar.br/handle/ufscar/764 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.confidence.fl_str_mv |
-1 -1 |
dc.relation.authority.fl_str_mv |
dd65b32b-27ea-44dd-9f6f-c8b3b548e9ba |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de São Carlos |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciência e Engenharia de Materiais - PPGCEM |
dc.publisher.initials.fl_str_mv |
UFSCar |
dc.publisher.country.fl_str_mv |
BR |
publisher.none.fl_str_mv |
Universidade Federal de São Carlos |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFSCAR instname:Universidade Federal de São Carlos (UFSCAR) instacron:UFSCAR |
instname_str |
Universidade Federal de São Carlos (UFSCAR) |
instacron_str |
UFSCAR |
institution |
UFSCAR |
reponame_str |
Repositório Institucional da UFSCAR |
collection |
Repositório Institucional da UFSCAR |
bitstream.url.fl_str_mv |
https://repositorio.ufscar.br/bitstream/ufscar/764/1/1795.pdf https://repositorio.ufscar.br/bitstream/ufscar/764/2/1795.pdf.jpg |
bitstream.checksum.fl_str_mv |
1be0da6e81e9e84eb153d9eafe8f1116 7273b593df75708efc8ddd7582e60e3b |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFSCAR - Universidade Federal de São Carlos (UFSCAR) |
repository.mail.fl_str_mv |
|
_version_ |
1802136247041261568 |