Efeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentina
Autor(a) principal: | |
---|---|
Data de Publicação: | 2014 |
Tipo de documento: | Tese |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFG |
Texto Completo: | http://repositorio.bc.ufg.br/tede/handle/tede/3874 |
Resumo: | Evaluate bond strength (BS) between leucite glass ceramic and dentin when luted with conventional and self-adhesive resin cements, preheated or not, through a microtensile bond strength test (μTBS) and examine the fracture mode. Materials and Methods: Twenty-four extracted human third molars were sectioned for the removal of the occlusal enamel and root portion, and ramdomly divided into four groups, with four teeth for each group. Twenty-four leucite glass ceramic discs (IPS Empress Esthetic, Ivoclar Vivadent, Schaan, Liechtenstein) were obtained and luted to the teeth, following manufacturers instructions, divided in four (4) groups: GI – RelyX ARC (3M ESPE) + Scotchbond Multi-Purpose Plus (3M ESPE); GII – RelyX ARC preheated 60°C + Scotchbond Multi-Purpose Plus; GIII – RelyX U200; GIV – RelyX U200 preheated 60°C. They were cut into 1 mm2 specimens, stored in destilled water for 24hs at 25±2°C and submitted to the μTBS in a universal testing machine. Each fragment of the specimen was analysed in stereoscopic microscope (45X) to classify the failure mode. SEM images of a representative pair of each failure mode were obtained. Data were statisticaly analysed with Variance Analysis (ANOVA) and Tukey (α=0.05). Results: There were statistical significant differences on BS between the cements RelyX ARC and U200 (p<0.05) in both groups with and without heating. There were no significant differences on BS between groups GI (12.98 MPa) and GII (12.87 MPa) and between GIII (6.81 MPa) and GIV (8.58 MPa) for both cements tested (p>0,05). The most common failure mode observed in all groups was adhesive, followed by mixed and ceramic cohesive failure; no group presented dentin cohesive failure. Conclusion: Preheating of resin cements to 60ºC did not enhance BS for both cements. BS for conventional resin cement was greater than self-adhesive resin cement. Adhesive failure was the most common failure mode. |
id |
UFG-2_1b980ceed4665905dec34aba3fb1ce44 |
---|---|
oai_identifier_str |
oai:repositorio.bc.ufg.br:tede/3874 |
network_acronym_str |
UFG-2 |
network_name_str |
Repositório Institucional da UFG |
repository_id_str |
|
spelling |
Estrela, Carloshttp://lattes.cnpq.br/3611967334176683Souza, João Batista deEstrela, CarlosFreitas, Gersinei Carlos dePécora, Jesus DjalmaSouza, João Batista deReges, Rogério Vieirahttp://lattes.cnpq.br/2325401417593664Castro, Fernanda Maria de2015-01-14T13:39:55Z2014-02-21CASTRO, Fernanda Maria de. Efeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentina. 2014. 80 f. Tese (Doutorado em Ciências da Saúde) - Universidade Federal de Goiás, Goiânia, 2014.http://repositorio.bc.ufg.br/tede/handle/tede/3874Evaluate bond strength (BS) between leucite glass ceramic and dentin when luted with conventional and self-adhesive resin cements, preheated or not, through a microtensile bond strength test (μTBS) and examine the fracture mode. Materials and Methods: Twenty-four extracted human third molars were sectioned for the removal of the occlusal enamel and root portion, and ramdomly divided into four groups, with four teeth for each group. Twenty-four leucite glass ceramic discs (IPS Empress Esthetic, Ivoclar Vivadent, Schaan, Liechtenstein) were obtained and luted to the teeth, following manufacturers instructions, divided in four (4) groups: GI – RelyX ARC (3M ESPE) + Scotchbond Multi-Purpose Plus (3M ESPE); GII – RelyX ARC preheated 60°C + Scotchbond Multi-Purpose Plus; GIII – RelyX U200; GIV – RelyX U200 preheated 60°C. They were cut into 1 mm2 specimens, stored in destilled water for 24hs at 25±2°C and submitted to the μTBS in a universal testing machine. Each fragment of the specimen was analysed in stereoscopic microscope (45X) to classify the failure mode. SEM images of a representative pair of each failure mode were obtained. Data were statisticaly analysed with Variance Analysis (ANOVA) and Tukey (α=0.05). Results: There were statistical significant differences on BS between the cements RelyX ARC and U200 (p<0.05) in both groups with and without heating. There were no significant differences on BS between groups GI (12.98 MPa) and GII (12.87 MPa) and between GIII (6.81 MPa) and GIV (8.58 MPa) for both cements tested (p>0,05). The most common failure mode observed in all groups was adhesive, followed by mixed and ceramic cohesive failure; no group presented dentin cohesive failure. Conclusion: Preheating of resin cements to 60ºC did not enhance BS for both cements. BS for conventional resin cement was greater than self-adhesive resin cement. Adhesive failure was the most common failure mode.Avaliar a resistência de união (RU) entre uma cerâmica vítrea reforçada por leucita e a dentina com a utilização de cimentos resinosos convencional e autoadesivo, com e sem aquecimento, por meio do teste de microtração (μTBS) e verificar o padrão de fratura. Material e métodos: vinte e quatro (24) terceiros molares humanos extraídos foram seccionados para remoção da porção radicular e do esmalte oclusal e aleatoriamente divididos em quatro (4) grupos. Vinte e quatro discos de cerâmica vítrea reforçada por leucita (IPS Empress Esthetic, Ivoclar Vivadent, Schaan, Liechtenstein) foram obtidos e cimentados aos dentes seccionados, de acordo com as especificações do fabricante, obtendo-se quatro (4) grupos: GI – RelyX ARC (3M ESPE) + Scotchbond Multi-Purpose Plus (3M ESPE); GII – RelyX ARC preaquecido 60°C + Scotchbond Multi-Purpose Plus; GIII – RelyX U200 (3M ESPE); GIV – RelyX U200 preaquecido 60°C. As amostras foram cortadas para obtenção de espécimes de 1,0 mm2, armazenadas por 24 h em água destilada a 25±2°C e submetidas ao teste de microtração em máquina de ensaio universal. Cada parte do espécime foi analisada em microscópio estereoscópico (45X) para visualização e classificação do padrão de fratura. Foram realizadas fotomicrografias em microscopia eletrônica de varredura de um par representativo de cada tipo de fratura. Os dados obtidos foram analisados estatísticamente por Análise de Variância (ANOVA) e teste de Tukey (α=0,05). Resultados: houve diferença estatisticamente significante entre a RU dos cimentos RelyX ARC e U200 (p<0,05), com e sem aquecimento. Não houve diferença significante entre a RU dos grupos GI (12,98 MPa) e GII (12,87 MPa) e entre GIII (6,81MPa) e GIV (8,58 MPa) (p>0,05). A falha adesiva foi o tipo de falha mais observado em todos os grupos, seguida pela falha mista e coesiva em cerâmica; nenhum grupo apresentou falhas coesivas em dentina. Conclusão: o preaquecimento dos cimentos resinosos a 60ºC não influenciou significantemente na RU entre a dentina e a cerâmica para ambos os cimentos, sendo a RU do cimento resinoso convencional superior à RU do autoadesivo. O padrão de fratura mais observado foi a falha adesiva.Submitted by Luciana Ferreira (lucgeral@gmail.com) on 2015-01-14T13:38:51Z No. of bitstreams: 2 license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Tese - Fernanda Maria de Castro - 2014.pdf: 1978045 bytes, checksum: bc85b184ec55cdac0ec38892e07c936d (MD5)Approved for entry into archive by Luciana Ferreira (lucgeral@gmail.com) on 2015-01-14T13:39:55Z (GMT) No. of bitstreams: 2 license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Tese - Fernanda Maria de Castro - 2014.pdf: 1978045 bytes, checksum: bc85b184ec55cdac0ec38892e07c936d (MD5)Made available in DSpace on 2015-01-14T13:39:55Z (GMT). No. of bitstreams: 2 license_rdf: 23148 bytes, checksum: 9da0b6dfac957114c6a7714714b86306 (MD5) Tese - Fernanda Maria de Castro - 2014.pdf: 1978045 bytes, checksum: bc85b184ec55cdac0ec38892e07c936d (MD5) Previous issue date: 2014-02-21Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfhttp://repositorio.bc.ufg.br/tede/retrieve/14548/Tese%20-%20Fernanda%20Maria%20de%20Castro%20-%202014.pdf.jpgporUniversidade Federal de GoiásPrograma de Pós-graduação em Ciências da Saúde (FM)UFGBrasilFaculdade de Medicina - FM (RG)http://creativecommons.org/licenses/by-nc-nd/4.0/info:eu-repo/semantics/openAccessPolimerizaçãoAquecimentoCimentos de resinaPorcelana dentáriaAdesivos dentáriosPolymerizationHeatingResin cementsDental porcelainDental cementsCIENCIAS DA SAUDE::ODONTOLOGIAEfeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentinaEffect of resin cements preheating on ceramics bonding to dentininfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis-10068643126177453106006006006001545772475950486338-20704984698792443492075167498588264571reponame:Repositório Institucional da UFGinstname:Universidade Federal de Goiás (UFG)instacron:UFGTEXTTese - Fernanda Maria de Castro - 2014.pdf.txtTese - Fernanda Maria de Castro - 2014.pdf.txtExtracted Texttext/plain104647http://repositorio.bc.ufg.br/tede/bitstreams/c919a8bb-aacb-49e6-a4c3-9e09ca9c2b05/downloadd158c1d10867e167c5e4d0860c3a6d35MD57THUMBNAILTese - Fernanda Maria de Castro - 2014.pdf.jpgTese - Fernanda Maria de Castro - 2014.pdf.jpgGenerated Thumbnailimage/jpeg2710http://repositorio.bc.ufg.br/tede/bitstreams/3d67d1e5-a908-4731-93ea-5220f976b4b3/download1380fbfd275cc4fa395e1d94f01efcc8MD58ORIGINALTese - Fernanda Maria de Castro - 2014.pdfTese - Fernanda Maria de Castro - 2014.pdfapplication/pdf1978045http://repositorio.bc.ufg.br/tede/bitstreams/e0ce87df-a559-48ed-8aa0-66069b47fefb/downloadbc85b184ec55cdac0ec38892e07c936dMD52LICENSElicense.txtlicense.txttext/plain; charset=utf-82165http://repositorio.bc.ufg.br/tede/bitstreams/6711c97b-8962-4f9b-b93b-97391617e85a/downloadbd3efa91386c1718a7f26a329fdcb468MD53CC-LICENSElicense_urllicense_urltext/plain; charset=utf-849http://repositorio.bc.ufg.br/tede/bitstreams/5e480b80-e8b9-4a0e-815f-c1977e10c2fd/download4afdbb8c545fd630ea7db775da747b2fMD54license_textlicense_texttext/html; charset=utf-822901http://repositorio.bc.ufg.br/tede/bitstreams/6f4b6439-e70f-4364-b661-a371b69595e2/download29b9d5e95be03707f9d4a2e110421c11MD55license_rdflicense_rdfapplication/rdf+xml; charset=utf-823148http://repositorio.bc.ufg.br/tede/bitstreams/e724cce6-2f80-4fff-bd60-1237bdd1ed45/download9da0b6dfac957114c6a7714714b86306MD56tede/38742015-01-15 03:01:09.109http://creativecommons.org/licenses/by-nc-nd/4.0/Acesso Abertoopen.accessoai:repositorio.bc.ufg.br:tede/3874http://repositorio.bc.ufg.br/tedeRepositório InstitucionalPUBhttp://repositorio.bc.ufg.br/oai/requesttasesdissertacoes.bc@ufg.bropendoar:2015-01-15T05:01:09Repositório Institucional da UFG - Universidade Federal de Goiás (UFG)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 |
dc.title.por.fl_str_mv |
Efeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentina |
dc.title.alternative.eng.fl_str_mv |
Effect of resin cements preheating on ceramics bonding to dentin |
title |
Efeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentina |
spellingShingle |
Efeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentina Castro, Fernanda Maria de Polimerização Aquecimento Cimentos de resina Porcelana dentária Adesivos dentários Polymerization Heating Resin cements Dental porcelain Dental cements CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Efeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentina |
title_full |
Efeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentina |
title_fullStr |
Efeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentina |
title_full_unstemmed |
Efeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentina |
title_sort |
Efeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentina |
author |
Castro, Fernanda Maria de |
author_facet |
Castro, Fernanda Maria de |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Estrela, Carlos |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/3611967334176683 |
dc.contributor.advisor-co1.fl_str_mv |
Souza, João Batista de |
dc.contributor.referee1.fl_str_mv |
Estrela, Carlos |
dc.contributor.referee2.fl_str_mv |
Freitas, Gersinei Carlos de |
dc.contributor.referee3.fl_str_mv |
Pécora, Jesus Djalma |
dc.contributor.referee4.fl_str_mv |
Souza, João Batista de |
dc.contributor.referee5.fl_str_mv |
Reges, Rogério Vieira |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/2325401417593664 |
dc.contributor.author.fl_str_mv |
Castro, Fernanda Maria de |
contributor_str_mv |
Estrela, Carlos Souza, João Batista de Estrela, Carlos Freitas, Gersinei Carlos de Pécora, Jesus Djalma Souza, João Batista de Reges, Rogério Vieira |
dc.subject.por.fl_str_mv |
Polimerização Aquecimento Cimentos de resina Porcelana dentária Adesivos dentários |
topic |
Polimerização Aquecimento Cimentos de resina Porcelana dentária Adesivos dentários Polymerization Heating Resin cements Dental porcelain Dental cements CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.eng.fl_str_mv |
Polymerization Heating Resin cements Dental porcelain Dental cements |
dc.subject.cnpq.fl_str_mv |
CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
Evaluate bond strength (BS) between leucite glass ceramic and dentin when luted with conventional and self-adhesive resin cements, preheated or not, through a microtensile bond strength test (μTBS) and examine the fracture mode. Materials and Methods: Twenty-four extracted human third molars were sectioned for the removal of the occlusal enamel and root portion, and ramdomly divided into four groups, with four teeth for each group. Twenty-four leucite glass ceramic discs (IPS Empress Esthetic, Ivoclar Vivadent, Schaan, Liechtenstein) were obtained and luted to the teeth, following manufacturers instructions, divided in four (4) groups: GI – RelyX ARC (3M ESPE) + Scotchbond Multi-Purpose Plus (3M ESPE); GII – RelyX ARC preheated 60°C + Scotchbond Multi-Purpose Plus; GIII – RelyX U200; GIV – RelyX U200 preheated 60°C. They were cut into 1 mm2 specimens, stored in destilled water for 24hs at 25±2°C and submitted to the μTBS in a universal testing machine. Each fragment of the specimen was analysed in stereoscopic microscope (45X) to classify the failure mode. SEM images of a representative pair of each failure mode were obtained. Data were statisticaly analysed with Variance Analysis (ANOVA) and Tukey (α=0.05). Results: There were statistical significant differences on BS between the cements RelyX ARC and U200 (p<0.05) in both groups with and without heating. There were no significant differences on BS between groups GI (12.98 MPa) and GII (12.87 MPa) and between GIII (6.81 MPa) and GIV (8.58 MPa) for both cements tested (p>0,05). The most common failure mode observed in all groups was adhesive, followed by mixed and ceramic cohesive failure; no group presented dentin cohesive failure. Conclusion: Preheating of resin cements to 60ºC did not enhance BS for both cements. BS for conventional resin cement was greater than self-adhesive resin cement. Adhesive failure was the most common failure mode. |
publishDate |
2014 |
dc.date.issued.fl_str_mv |
2014-02-21 |
dc.date.accessioned.fl_str_mv |
2015-01-14T13:39:55Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/doctoralThesis |
format |
doctoralThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
CASTRO, Fernanda Maria de. Efeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentina. 2014. 80 f. Tese (Doutorado em Ciências da Saúde) - Universidade Federal de Goiás, Goiânia, 2014. |
dc.identifier.uri.fl_str_mv |
http://repositorio.bc.ufg.br/tede/handle/tede/3874 |
identifier_str_mv |
CASTRO, Fernanda Maria de. Efeito do preaquecimento de cimentos resinosos na resistência de união de cerâmica à dentina. 2014. 80 f. Tese (Doutorado em Ciências da Saúde) - Universidade Federal de Goiás, Goiânia, 2014. |
url |
http://repositorio.bc.ufg.br/tede/handle/tede/3874 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-1006864312617745310 |
dc.relation.confidence.fl_str_mv |
600 600 600 600 |
dc.relation.department.fl_str_mv |
1545772475950486338 |
dc.relation.cnpq.fl_str_mv |
-2070498469879244349 |
dc.relation.sponsorship.fl_str_mv |
2075167498588264571 |
dc.rights.driver.fl_str_mv |
http://creativecommons.org/licenses/by-nc-nd/4.0/ info:eu-repo/semantics/openAccess |
rights_invalid_str_mv |
http://creativecommons.org/licenses/by-nc-nd/4.0/ |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de Goiás |
dc.publisher.program.fl_str_mv |
Programa de Pós-graduação em Ciências da Saúde (FM) |
dc.publisher.initials.fl_str_mv |
UFG |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Faculdade de Medicina - FM (RG) |
publisher.none.fl_str_mv |
Universidade Federal de Goiás |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFG instname:Universidade Federal de Goiás (UFG) instacron:UFG |
instname_str |
Universidade Federal de Goiás (UFG) |
instacron_str |
UFG |
institution |
UFG |
reponame_str |
Repositório Institucional da UFG |
collection |
Repositório Institucional da UFG |
bitstream.url.fl_str_mv |
http://repositorio.bc.ufg.br/tede/bitstreams/c919a8bb-aacb-49e6-a4c3-9e09ca9c2b05/download http://repositorio.bc.ufg.br/tede/bitstreams/3d67d1e5-a908-4731-93ea-5220f976b4b3/download http://repositorio.bc.ufg.br/tede/bitstreams/e0ce87df-a559-48ed-8aa0-66069b47fefb/download http://repositorio.bc.ufg.br/tede/bitstreams/6711c97b-8962-4f9b-b93b-97391617e85a/download http://repositorio.bc.ufg.br/tede/bitstreams/5e480b80-e8b9-4a0e-815f-c1977e10c2fd/download http://repositorio.bc.ufg.br/tede/bitstreams/6f4b6439-e70f-4364-b661-a371b69595e2/download http://repositorio.bc.ufg.br/tede/bitstreams/e724cce6-2f80-4fff-bd60-1237bdd1ed45/download |
bitstream.checksum.fl_str_mv |
d158c1d10867e167c5e4d0860c3a6d35 1380fbfd275cc4fa395e1d94f01efcc8 bc85b184ec55cdac0ec38892e07c936d bd3efa91386c1718a7f26a329fdcb468 4afdbb8c545fd630ea7db775da747b2f 29b9d5e95be03707f9d4a2e110421c11 9da0b6dfac957114c6a7714714b86306 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFG - Universidade Federal de Goiás (UFG) |
repository.mail.fl_str_mv |
tasesdissertacoes.bc@ufg.br |
_version_ |
1798044321311621120 |