Fase aquosa do bio-óleo de pirólise rápida incorporada com bentonita como agente protetor contra fungos e para hidrorepelência da madeira

Detalhes bibliográficos
Autor(a) principal: Sanson, Caio Silvestre Lima
Data de Publicação: 2021
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFPR
Texto Completo: https://hdl.handle.net/1884/74009
Resumo: Orientador: Prof. Dr Pedro Henrique Gonzalez de Cademartori
id UFPR_38fe5d707e6ca6008b5bf41335333125
oai_identifier_str oai:acervodigital.ufpr.br:1884/74009
network_acronym_str UFPR
network_name_str Repositório Institucional da UFPR
repository_id_str 308
spelling Helm, Cristiane VieiraMagalhães, Washington Luiz EstevesUniversidade Federal do Paraná. Setor de Ciências Agrárias. Programa de Pós-Graduação em Engenharia FlorestalCademartori, Pedro Henrique Gonzalez de, 1987-Sanson, Caio Silvestre Lima2022-11-17T11:46:34Z2022-11-17T11:46:34Z2021https://hdl.handle.net/1884/74009Orientador: Prof. Dr Pedro Henrique Gonzalez de CademartoriCoorientadores: Profª. Drª. Cristiane Vieira Helm, Prof. Dr. Washington Luiz Esteves MagalhãesDissertação (mestrado) - Universidade Federal do Paraná, Setor de Ciências Agrárias, Programa de Pós-Graduação em Engenharia Florestal. Defesa : Curitiba, 27/08/2021Inclui referências: p. 73-85Área de concentração: Tecnologia e Utilização de Produtos FlorestaisResumo: O estudo teve como principal objetivo desenvolver um agente protetor para madeira a ataques de fungos e aumentar a hidrorepelência da superfície da madeira, através do fracionamento líquido-líquido do bio-óleo de pirólise rápida de Eucalyptus sp. e incorporação de nanoestruturas do argilomineral bentonita. A motivação do presente estudo foi produzir uma alternativa de origem renovável com caráter protetor para madeira com menor potencial danoso para o meio ambiente, em comparação por exemplo a produtos derivados do cromo, cobre e arsênio. O bio-óleo foi fracionado pelo método de separação física por agitação vigorosa utilizando água destilada como meio líquido. Ajustou-se a proporção água:óleo, para obter os melhores rendimentos da fração aquoso (WS) (em torno de 60%), optando-se pelas proporções 1:50 (WS50) e 1:100 (WS100). A bentonita foi esfoliada em meio aquoso via agitação vigorosa e magnética, formando a suspensão de nanoestruturas de bentonita (NB), e em seguida incorporada com as WS. Um total de cinco tratamentos contendo com as WS e/ou NB (WS100+NB, WS100, WS50+NB, WS50 e NB) foram caracterizados essas suspensões antes (na sua forma líquida e os sólidos de cada suspensão quando secos) e depois de quando impregnados na madeira de Pinus taeda quanto a morfologia, atividade antifúngica, resistência biológica, molhabilidade superficial, comportamento térmico por análise termogravimétrica e ensaios de lixiviação. Morfologicamente por MEV e MET foi utilizado para caracterização das nanoestruturas de bentonita dispersas em escala nanométrica, e quando impregnadas na madeira com ou sem a WS, formou um filme sob a superfície da madeira. Os sólidos das suspensões de WS incorporadas com NB, quando analisadas por termogravimetria, apresentaram maior estabilidade térmica, suponha-se que pelo fato da presença dos compostos inorgânicos. As madeiras tratadas com WS e NB aumentaram substancialmente a hidrorrepelência, apresentando maior estabilidade cinética do ângulo de contato. Os tratamentos WS100, WS50 e WS50+NB inibiram totalmente o crescimento dos fungosTrametes versicolor e Gloeophyllum trabeum em ensaio de potencial antagonista por disco-difusão. Estas inibições foram confirmadas no teste de biodeterioração acelerada da madeira com os mesmos fungos. De maneira geral, os tratamentos com WS e NB resultaram em menor perda de massa se comparado a madeira não-tratada, ressaltando-se o tratamento com NB e WS50+NB com os melhores resultados. Na lixiviação foi verificado a quantidade material de lixiviado para os materiais analisados. Portanto, ao serem analisados em caráter físico, químico e biológico, as suspensões provenientes do fracionamento do bio-óleo de pirólise rápida com ou sem as nanoestruturas de bentonita, demonstraram ser uma alternativa eficaz como agente protetor de materiais lignocelulósicos, e que a junção desses dois materiais resultou em uma sinergia positiva.Abstract: This study was to develop a protective agent for wood, through the liquid-liquid fractionation of the fast pyrolysis bio-oil of Eucalyptus sp. and incorporation of bentonite clay mineral nanostructures. The motivation of this study was to produce an alternative with a protective character for wood with less harmful potential for the environment and adding value to materials of renewable origin. Bio-oil was fractionated by physical separation method by vigorous stirring using distilled water as liquid medium. The water:oil ratio was adjusted to obtain the best WS yields (around 60%), opting for the ratios 1:50 (WS50) and 1:100 (WS100). The bentonite was exfoliated in an aqueous medium via vigorous and magnetic stirring, forming a suspension of bentonite nanostructures (NB), and then incorporated with the WS. A total of five treatments containing WS and/or NB (WS100+NB, WS100, WS50+NB, WS50 and NB) were characterized before (in its liquid form and its solids when dry) and after impregnation in Pinus taeda wood as morphology, antifungal activity, biological resistance, surface wettability, thermal behavior by thermogravimetric analysis and leaching tests. Morphologically, by SEM and TEM, the nanostructures of bentonite dispersed at a nanometric scale were verified, and when impregnated in the wood with or without WS, it formed a film under the surface of the wood. The solids of WS suspensions incorporated with NB, when analyzed by thermogravimetry, showed greater thermal stability due to the presence of inorganic compounds. Woods treated with WS and NB substantially increased water repellency, showing greater kinetic stability of the contact angle. Treatments WS100, WS50 and WS50+NB totally inhibited the growth of the fungi Trametes versicolor and Gloeophyllum trabeum in a disk-diffusion test of antagonist potential. These inhibitions were confirmed in the accelerated wood biodeterioration test with the same fungi. In general, the treatments with WS and NB resulted in less mass loss compared to untreated wood, highlighting the treatment with NB and WS50+NB. And when analyzing the leaching of the wood impregnated with WS and/or NB suspensions, a low level of leaching was verified for both materials. Therefore, when analyzed on a physical, chemical, and biological basis, the suspensions from the fractionation of rapid pyrolysis bio-oil with or without bentonite nanostructures, proved to be an effective alternative as a protective agent for lignocellulosic materials, and that the combination of these two materials resulted in a positive synergy.1 recurso online : PDF.application/pdfMadeira - PreservativosMadeira - ConservaçãoFungos apodrecedores da madeiraBiocombustíveisPiroliseFase aquosa do bio-óleo de pirólise rápida incorporada com bentonita como agente protetor contra fungos e para hidrorepelência da madeirainfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisporreponame:Repositório Institucional da UFPRinstname:Universidade Federal do Paraná (UFPR)instacron:UFPRinfo:eu-repo/semantics/openAccessORIGINALR - D - CAIO SILVESTRE LIMA SANSON.pdfapplication/pdf3544220https://acervodigital.ufpr.br/bitstream/1884/74009/1/R%20-%20D%20-%20CAIO%20SILVESTRE%20LIMA%20SANSON.pdf05d414722b242956eec6fdfbb7ec9dafMD51open access1884/740092022-11-17 08:46:34.327open accessoai:acervodigital.ufpr.br:1884/74009Repositório de PublicaçõesPUBhttp://acervodigital.ufpr.br/oai/requestopendoar:3082022-11-17T11:46:34Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)false
dc.title.pt_BR.fl_str_mv Fase aquosa do bio-óleo de pirólise rápida incorporada com bentonita como agente protetor contra fungos e para hidrorepelência da madeira
title Fase aquosa do bio-óleo de pirólise rápida incorporada com bentonita como agente protetor contra fungos e para hidrorepelência da madeira
spellingShingle Fase aquosa do bio-óleo de pirólise rápida incorporada com bentonita como agente protetor contra fungos e para hidrorepelência da madeira
Sanson, Caio Silvestre Lima
Madeira - Preservativos
Madeira - Conservação
Fungos apodrecedores da madeira
Biocombustíveis
Pirolise
title_short Fase aquosa do bio-óleo de pirólise rápida incorporada com bentonita como agente protetor contra fungos e para hidrorepelência da madeira
title_full Fase aquosa do bio-óleo de pirólise rápida incorporada com bentonita como agente protetor contra fungos e para hidrorepelência da madeira
title_fullStr Fase aquosa do bio-óleo de pirólise rápida incorporada com bentonita como agente protetor contra fungos e para hidrorepelência da madeira
title_full_unstemmed Fase aquosa do bio-óleo de pirólise rápida incorporada com bentonita como agente protetor contra fungos e para hidrorepelência da madeira
title_sort Fase aquosa do bio-óleo de pirólise rápida incorporada com bentonita como agente protetor contra fungos e para hidrorepelência da madeira
author Sanson, Caio Silvestre Lima
author_facet Sanson, Caio Silvestre Lima
author_role author
dc.contributor.other.pt_BR.fl_str_mv Helm, Cristiane Vieira
Magalhães, Washington Luiz Esteves
Universidade Federal do Paraná. Setor de Ciências Agrárias. Programa de Pós-Graduação em Engenharia Florestal
dc.contributor.advisor1.fl_str_mv Cademartori, Pedro Henrique Gonzalez de, 1987-
dc.contributor.author.fl_str_mv Sanson, Caio Silvestre Lima
contributor_str_mv Cademartori, Pedro Henrique Gonzalez de, 1987-
dc.subject.por.fl_str_mv Madeira - Preservativos
Madeira - Conservação
Fungos apodrecedores da madeira
Biocombustíveis
Pirolise
topic Madeira - Preservativos
Madeira - Conservação
Fungos apodrecedores da madeira
Biocombustíveis
Pirolise
description Orientador: Prof. Dr Pedro Henrique Gonzalez de Cademartori
publishDate 2021
dc.date.issued.fl_str_mv 2021
dc.date.accessioned.fl_str_mv 2022-11-17T11:46:34Z
dc.date.available.fl_str_mv 2022-11-17T11:46:34Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/1884/74009
url https://hdl.handle.net/1884/74009
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 1 recurso online : PDF.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFPR
instname:Universidade Federal do Paraná (UFPR)
instacron:UFPR
instname_str Universidade Federal do Paraná (UFPR)
instacron_str UFPR
institution UFPR
reponame_str Repositório Institucional da UFPR
collection Repositório Institucional da UFPR
bitstream.url.fl_str_mv https://acervodigital.ufpr.br/bitstream/1884/74009/1/R%20-%20D%20-%20CAIO%20SILVESTRE%20LIMA%20SANSON.pdf
bitstream.checksum.fl_str_mv 05d414722b242956eec6fdfbb7ec9daf
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFPR - Universidade Federal do Paraná (UFPR)
repository.mail.fl_str_mv
_version_ 1801860835928178688

Registros relacionados