Produção de monofilamentos a base de alginato e nanocristais de celulose obtidos de resíduos de algodão

Detalhes bibliográficos
Autor(a) principal: Kreutzfeld, Victor
Data de Publicação: 2023
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/249913
Resumo: Dissertação (mestrado profissional) - Universidade Federal de Santa Catarina, Campus Blumenau, Programa de Pós-Graduação em Engenharia Têxtil, Blumenau, 2023.
id UFSC_10a07663b98fa88cbd4b969c9208f104
oai_identifier_str oai:repositorio.ufsc.br:123456789/249913
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Produção de monofilamentos a base de alginato e nanocristais de celulose obtidos de resíduos de algodãoIndústria têxtilCeluloseHidróliseFiaçãoResíduos industriaisDissertação (mestrado profissional) - Universidade Federal de Santa Catarina, Campus Blumenau, Programa de Pós-Graduação em Engenharia Têxtil, Blumenau, 2023.A celulose é o polímero renovável mais abundante na natureza, sendo um dos principais constituintes das paredes celulares das plantas. Recentemente, o isolamento da nanocelulose, na forma de fribrilas ou bastonetes, tem despertado crescente atenção para diversas aplicações pelas propriedades de elevada área superficial, elevada rigidez e cristalinidade, baixa densidade e biodegradabilidade. Dentre as fontes de celulose que podem ser utilizadas para a obtenção da nanocelulose, destaca-se as fibras de algodão, que apresentam em sua composição entre 88 e 96% de celulose. Associado a isso, o algodão é uma das principais matérias-primas da indústria têxtil, gerando massivas quantidades de resíduos em diversas etapas do processamento, constituindo um problema ambiental. Portanto, os resíduos industriais de algodão são uma fonte promissora e sustentável para a obtenção de nanocelulose, os quais podem ser utilizados para a produção de filamentos como agentes de reforço com outros polímeros. Neste estudo, resíduos de algodão alvejado e tingido foram utilizados como matéria-prima para a obtenção de nanocristais de celulose (NCCs), os quais foram utilizados como agentes de reforço em filamentos de alginato produzidos pela técnica de fiação a úmido. Os NCCs foram obtidos por meio da hidrólise com solução aquosa de ácido sulfúrico a 60 % (m/m) em reação a 45 °C e 45 minutos. Os materiais resultantes da hidrólise apresentaram a cor do algodão original, formato de bastonetes e dimensões típicas de NCCs, com boa estabilidade de suspensão, rendimentos de reação superiores a 80 % e índices de cristalinidade de 87 %. Os filamentos nanocompósitos foram obtidos utilizando solução de alginato de sódio 2 % (m/v) contendo diferentes proporções mássicas de NCC (1, 3, 5, 10 e 20 %). Após a extrusão, a solidificação ocorreu em um banho aquoso de CaCl2 a 10 % (m/v). Foi verificado que a coloração dos filamentos foi alterada de forma gradativa com maiores concentrações de NCC. Os ensaios de resistência mecânica indicaram que a tensão de ruptura dos filamentos aumentou com a incorporação dos NCCs até a concentração de 5 %, com aumento de 400 %, sendo reduzida nas concentrações superiores. Os filamentos com NCC tingido apresentaram maiores resistências, o que pode ser atribuído à melhor dispersão destes devido ao menor tamanho. O grau de intumescimento em água dos filamentos em períodos de até 14 dias foi baixo (máximo de 42 %) e similar entre as diferentes amostras. A perda de massa máxima foi de 45 % em 14 dias e os filamentos permaneceram fisicamente estáveis. Em geral, o estudo permitiu concluir que é possível obter filamentos de alginato intrinsecamente coloridos e que a adição de NCC obtido de resíduo de algodão em até 5 % é capaz de formar estruturas com resistência mecânica muito superior à do filamento de alginato puro.Abstract: Cellulose is the most abundant renewable polymer in nature, being one of the main constituents of plant cell walls. Recently, the isolation of nanocellulose, in the form of fibrils or rods, has attracted increasing attention for several applications due to the properties of high surface area, high rigidity and crystallinity, low density, and biodegradability. Among the sources of cellulose that can be used to obtain nanocellulose, cotton fibers stand out, which present in their composition between 88 and 96% of cellulose. In addition, cotton is one of the main raw materials of the textile industry, generating massive amounts of waste in different processing stages, constituting an environmental problem. Therefore, industrial cotton waste is a promising and sustainable source for obtaining nanocellulose, which can be used to produce filaments as reinforcing agents with other polymers. In this study, bleached and dyed cotton residues were used as raw material to obtain cellulose nanocrystals (NCCs), which were used as reinforcing agents in alginate filaments produced by the wet spinning technique. The NCCs were obtained by hydrolysis with an aqueous sulfuric acid solution at 60% (w/w) in reaction at 45 °C and 45 minutes. The materials resulting from hydrolysis showed the color of the original cotton, rod shape and dimensions typical of NCCs, with good suspension stability, reaction yields greater than 80%, and crystallinity indexes of 87%. The nanocomposite filaments were obtained using a 2% (w/v) sodium alginate solution containing different mass proportions of NCC (1, 3, 5, 10, and 20 %). After extrusion, solidification took place in a 10% (w/v) CaCl2 aqueous bath. It was verified that the coloration of the filaments was gradually altered with higher concentrations of NCC. The results of mechanical properties indicated that the tensile strength of the filaments increased with the incorporation of NCCs up to a concentration of 5%, with an increase of 400%, being reduced in higher concentrations. Filaments with colored NCC showed greater resistance, which can be attributed to their better dispersion in the alginate matrix due to their smaller size. The degree of swelling in water of the filaments in periods of 14 days was low (maximum 42%) and similar between the different samples. The maximum mass loss was 45% at 14 days and the filaments remained physically stable. In general, it was concluded that it is possible to obtain intrinsically colored alginate filaments and that the addition of NCC obtained from cotton waste in up to 5% is capable of forming structures with mechanical strength much higher than that of the pure alginate filament.Bierhalz, Andrea Cristiane KrauseValle, Rita de Cássia Siqueira CurtoUniversidade Federal de Santa CatarinaKreutzfeld, Victor2023-09-01T13:05:24Z2023-09-01T13:05:24Z2023info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis91 p.| il., gráfs., tabs.application/pdf382863https://repositorio.ufsc.br/handle/123456789/249913porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2023-09-15T12:08:24Zoai:repositorio.ufsc.br:123456789/249913Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732023-09-15T12:08:24Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Produção de monofilamentos a base de alginato e nanocristais de celulose obtidos de resíduos de algodão
title Produção de monofilamentos a base de alginato e nanocristais de celulose obtidos de resíduos de algodão
spellingShingle Produção de monofilamentos a base de alginato e nanocristais de celulose obtidos de resíduos de algodão
Kreutzfeld, Victor
Indústria têxtil
Celulose
Hidrólise
Fiação
Resíduos industriais
title_short Produção de monofilamentos a base de alginato e nanocristais de celulose obtidos de resíduos de algodão
title_full Produção de monofilamentos a base de alginato e nanocristais de celulose obtidos de resíduos de algodão
title_fullStr Produção de monofilamentos a base de alginato e nanocristais de celulose obtidos de resíduos de algodão
title_full_unstemmed Produção de monofilamentos a base de alginato e nanocristais de celulose obtidos de resíduos de algodão
title_sort Produção de monofilamentos a base de alginato e nanocristais de celulose obtidos de resíduos de algodão
author Kreutzfeld, Victor
author_facet Kreutzfeld, Victor
author_role author
dc.contributor.none.fl_str_mv Bierhalz, Andrea Cristiane Krause
Valle, Rita de Cássia Siqueira Curto
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Kreutzfeld, Victor
dc.subject.por.fl_str_mv Indústria têxtil
Celulose
Hidrólise
Fiação
Resíduos industriais
topic Indústria têxtil
Celulose
Hidrólise
Fiação
Resíduos industriais
description Dissertação (mestrado profissional) - Universidade Federal de Santa Catarina, Campus Blumenau, Programa de Pós-Graduação em Engenharia Têxtil, Blumenau, 2023.
publishDate 2023
dc.date.none.fl_str_mv 2023-09-01T13:05:24Z
2023-09-01T13:05:24Z
2023
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 382863
https://repositorio.ufsc.br/handle/123456789/249913
identifier_str_mv 382863
url https://repositorio.ufsc.br/handle/123456789/249913
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 91 p.| il., gráfs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652190603018241

Registros relacionados