Estudo do efeito de sucessivas despolimerizações sobre as propriedades térmicas e mecânicas da espuma rígida de poliuretano

Detalhes bibliográficos
Autor(a) principal: Mielke, Solange
Data de Publicação: 2012
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: http://repositorio.ufsc.br/xmlui/handle/123456789/99275
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Ciência e Engenharia de Materiais.
id UFSC_48df20339786d07a4d52aac6c9344c58
oai_identifier_str oai:repositorio.ufsc.br:123456789/99275
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Estudo do efeito de sucessivas despolimerizações sobre as propriedades térmicas e mecânicas da espuma rígida de poliuretanoCiencia dos materiaisEngenharia de materiaisPoliuretanasEspumaPolimerizaçãoPolimerosDissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Ciência e Engenharia de Materiais.Os poliuretanos representam uma classe de polímeros que se destacam devido à sua grande versatilidade. Como espumas rígidas ganham mercado na indústria de refrigeração doméstica, sendo utilizadas com a finalidade de conferir propriedades de isolamento térmico e de dar estruturação mecânica às portas e gabinetes. Apesar da indústria, ter alcançado um alto índice de eficiência é inevitável à geração de resíduos oriundos de sobras, "tray out" de máquinas e do retorno de produtos ao fim da vida útil. Diversos pesquisadores propuseram rotas de reciclagem química e mostraram que é possível produzir uma espuma com qualidade e destina - lá à mesma aplicação, porém em nenhum destes estudos é verificado quantas vezes será possível repetir este ciclo com um percentual de polímero decomposto "sem purificação" por até quatro vezes, sem que suas propriedades sejam comprometidas. O objetivo deste trabalho é analisar a influência de sucessivas despolimerizações e expansões, nas propriedades térmicas e mecânicas da espuma rígida de poliuretano. Foi realizada a despolimerização via glicólise utilizando dietilenoglicol e o acetato de potássio como solvente e catalisador respectivamente, mantendo#se as proporções mássicas resíduo solvente 1:1 PUR/DEG e resíduo catalisador 1:0,02 PUR/ KAc, que se mostraram mais eficientes para tratar os resíduos deste segmento. O produto da despolimerização foi caracterizado para que a qualidade do polímero decomposto fosse acompanhada. O polímero decomposto, produto da reação de despolimerização foi utilizado como parte da matéria-prima na formação da nova espuma, em um percentual de 10% que se mostrou adequado para satisfazer às necessidades da indústria de refrigeração doméstica, sem comprometimento de suas propriedades. As expansões foram realizadas mantendo os padrões de uma indústria fabricante de refrigeradores. As propriedades mecânicas e térmicas foram analisadas por ensaio de densidade, compressão, "creep test", condutividade térmica, calorimetria exploratória diferencial (DSC) e termogravimetria (TGA), conforme as normas estabelecidas para este segmento. Após quatro ciclos de despolimerizações e expansões consecutivas não foram observadas alterações significativas nas propriedades mecânicas e térmicas da espuma. Os resultados validam a repetitibilidade do ciclo de reciclagem para as espumas produzidas com um percentual de polímero decomposto "sem purificação" em até quatro ciclos.The polyurethanes represent a class of polymers that stand out because of its great versatility. As the market make rigid foams in domestic refrigeration industry and are used in order to provide thermal insulation properties and give structure to the mechanical ports and offices. Although the industry has achieved a high level of efficiency is the inevitable generation of waste from leftovers, "tray out" machines and return the product end of life. Several researchers have proposed chemical recycling routes and showed that it is possible to produce a foam with quality and designed - there the same application, but in none of these studies is checked how many times you can repeat this cycle as a percentage of polymer decomposed "without purification" by up to four times, without their properties being compromised. The aim of this paper is to analyze the influence of successive depolymerization and expansions in thermal and mechanical properties of rigid polyurethane foam. Depolymerization was carried out via glycolysis using potassium acetate and diethylene glycol as solvent and catalyst respectively, keeping the mass ratios 1:1 PUR residue solvent / catalyst residue DEG and 1:0,02 PUR / KAC, which are more efficient for treat the waste in this segment. The product of depolymerization was characterized for the quality of the recovered polymer was accompanied decomposed. The recovered polymer decomposed, the reaction product of glycolysis was used as part of the raw material in the formation of new foam, on a percentage of 10% which is adequate to meet the needs of the domestic refrigeration industry without compromising its properties. The expansions were carried out maintaining the standards of an industry manufacturer of refrigerators. The mechanical and thermal properties were analyzed by testing the density, compressibility, "creep test", thermal conductivity, differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA), in accordance with standards established for this segment. After four cycles of consecutive expansions depolymezation and there were no significant changes in mechanical and thermal properties of the foam. The results validate the repeatability of the cycle of recycling for the foams produced with a percentage of recovered polymer decomposed to four cycles.FlorianópolisMachado, Ricardo Antonio FranciscoBecker, DanielaUniversidade Federal de Santa CatarinaMielke, Solange2013-03-04T18:29:20Z2013-03-04T18:29:20Z20122012info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis103 p.| il., tabs., grafs.application/pdf304957http://repositorio.ufsc.br/xmlui/handle/123456789/99275porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2016-03-07T18:55:20Zoai:repositorio.ufsc.br:123456789/99275Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732016-03-07T18:55:20Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Estudo do efeito de sucessivas despolimerizações sobre as propriedades térmicas e mecânicas da espuma rígida de poliuretano
title Estudo do efeito de sucessivas despolimerizações sobre as propriedades térmicas e mecânicas da espuma rígida de poliuretano
spellingShingle Estudo do efeito de sucessivas despolimerizações sobre as propriedades térmicas e mecânicas da espuma rígida de poliuretano
Mielke, Solange
Ciencia dos materiais
Engenharia de materiais
Poliuretanas
Espuma
Polimerização
Polimeros
title_short Estudo do efeito de sucessivas despolimerizações sobre as propriedades térmicas e mecânicas da espuma rígida de poliuretano
title_full Estudo do efeito de sucessivas despolimerizações sobre as propriedades térmicas e mecânicas da espuma rígida de poliuretano
title_fullStr Estudo do efeito de sucessivas despolimerizações sobre as propriedades térmicas e mecânicas da espuma rígida de poliuretano
title_full_unstemmed Estudo do efeito de sucessivas despolimerizações sobre as propriedades térmicas e mecânicas da espuma rígida de poliuretano
title_sort Estudo do efeito de sucessivas despolimerizações sobre as propriedades térmicas e mecânicas da espuma rígida de poliuretano
author Mielke, Solange
author_facet Mielke, Solange
author_role author
dc.contributor.none.fl_str_mv Machado, Ricardo Antonio Francisco
Becker, Daniela
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Mielke, Solange
dc.subject.por.fl_str_mv Ciencia dos materiais
Engenharia de materiais
Poliuretanas
Espuma
Polimerização
Polimeros
topic Ciencia dos materiais
Engenharia de materiais
Poliuretanas
Espuma
Polimerização
Polimeros
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-Graduação em Ciência e Engenharia de Materiais.
publishDate 2012
dc.date.none.fl_str_mv 2012
2012
2013-03-04T18:29:20Z
2013-03-04T18:29:20Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 304957
http://repositorio.ufsc.br/xmlui/handle/123456789/99275
identifier_str_mv 304957
url http://repositorio.ufsc.br/xmlui/handle/123456789/99275
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 103 p.| il., tabs., grafs.
application/pdf
dc.publisher.none.fl_str_mv Florianópolis
publisher.none.fl_str_mv Florianópolis
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652137847062528

Registros relacionados