Estudo do desenvolvimento de tensões residuais macroscópicas e do comportamento à fratura de porcelanatos

Detalhes bibliográficos
Autor(a) principal: Delavi, Deyse Gonzaga Gomes
Data de Publicação: 2016
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/xmlui/handle/123456789/167731
Resumo: Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia dos Materiais, Florianópolis, 2016.
id UFSC_d26cc126f3e151e7cd42d568511c5dae
oai_identifier_str oai:repositorio.ufsc.br:123456789/167731
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Universidade Federal de Santa CatarinaDelavi, Deyse Gonzaga GomesHotza, DachamirNoni Junior, Agenor de2016-09-20T04:14:56Z2016-09-20T04:14:56Z2016341126https://repositorio.ufsc.br/xmlui/handle/123456789/167731Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia dos Materiais, Florianópolis, 2016.Este trabalho tem como objetivo estudar a geração das tensões residuais macroscópicas e sua influência sobre a resistência mecânica e o comportamento à fratura de revestimentos cerâmicos tipo porcelanato.Para os porcelanatos laboratoriais, foi empregada uma composição de 52,8% feldspato, 31% de caulim e 16,2% de quartzo (% mássico). As tensões residuais foram medida pelo método Strain Relaxation Slotting Method (SRSM). O presente trabalho foi dividido em três partes. Na primeira parte, o desenvolvimento de tensões residuais em diferentes velocidades de resfriamentos foi estudado para porcelanatos laboratoriais. Mostrou-se que a velocidade de resfriamento, em altas temperaturas, influencia fortemente as tensões residuais geradas na superfície. As maiores tensões residuais de compressão foram encontradas para os resfriamentos rápidos realizados a T máx de 800ºC. Temperaturas inferiores, como a de transformação alotrópica do quartzo, não apresentaram influências significativas no desenvolvimento das tensões residuais. Na segunda parte, estudou-se a influência das propriedades do material na geração de tensões residuais em porcelanatos laboratoriais. Dentre as propriedades estudadas, o tamanho de partícula do quartzo e a espessura do corpo de prova foram as que apresentaram maior influência sobre o incremento nas tensões residuais e na resistência mecânica à flexão. Para a variação do tamanho de partícula do quartzo, foi encontrado que as partículas menores desenvolvem maior compressão na superfície do material incrementando a resistência mecânica. Para a variação da espessura do material, corpos de prova com maiores espessuras, na etapa do resfriamento, apresentam maior gradiente térmico entre a superfície e o centro da peça, comprimindo a superfície e aumentando a resistência mecânica. Com as demais propriedades, porosidade e tamanho do poro,coeficiente de expansão térmica e fase vítrea, constatou-se que o aumento da tensão de compressão na superfície do material nem sempre é convertido em aumento na resistência mecânica. Na terceira parte, foi realizado um estudo sobre a influência das tensões residuais macroscópicas no comportamento à fratura de porcelanatos industriais.As peças, provenientes de diferentes empresas, foram submetidas a ensaios de flexão e seu comportamento à fratura foi analisado. Os resultados mostraram que peças que apresentaram perfis de tensões não parabólicos e assimétricos desenvolveram comportamento inadequado à fratura. Para essas peças, o ajuste das deformações experimentais, no ensaio de medidas de tensões residuais, exige a utilização de polinômios de Legendre maior que grau 2. Ainda nesse capítulo, verificou-se que as peças tensionadas com resfriamento rápido apresentaram fratura não retilínea, enquanto que as peças provenientes de resfriamento lento (não tensionadas) mostraram fratura linear.<br>Abstract: This work aims to study the generation of macroscopic residual stresses and their influence on mechanical strength and cutting behaviorin Porcelain stoneware tiles. For laboratory porcelain a composition of 52.8% feldspar, 31% kaolin and 16.2% quartz was used (by mass). The residual stress was measured by SRSM method. This study was divided into three parts. In the first part, the development of residual stresses at different cooling rates was studied for laboratory porcelain. It was shown that the cooling rate at high temperature strongly influences theresidual stresses generated on the surface. The highest residual compressive stresses were found for rapid cooling performed around T max 800ºC. Lower temperatures, such as the allotropic transformation of quartz, had no significant influence on the development of residual stresses. In the second part, the influence of the material properties onthe generation of residual stresses in laboratory porcelain was studied.Among the properties analyzed, the particle size of quartz and the thickness of the specimen showed the greatest influence on the increasein residual stresses and mechanical strength. For the variation of the particle size of quartz, it was found that the smaller particles develophigher compression on the material surface increasing the mechanical strength. Regarding thickness variation of the material, samples withlarger thickness in the cooling step have a higher thermal gradientbetween the surface and the center of the piece, compressing the surfaceand increasing the mechanical strength. For other properties, porosityand pore size, coefficient of thermal expansion and glass phase, it wasfound that increased compressive stress on the surface of the material isnot always converted into increased mechanical strength. The third partwas a study about the influence of macroscopic residual stresses on thefracture behavior of industrial porcelain. Pieces from different industrieswere submitted to a bending test and the fracture behavior was analyzed. The results showed that pieces with a non-parabolic andasymmetrical stress developed an inadequate fracture behavior. Forthose pieces, the fit of the experimental deformation, in the residual stress measures, require the use of Legendre polynomials of degree greater than 2. Still in this chapter, it was found that the stressed pieceswith rapid cooling showed no rectilinear fracture whereas the (nonstressed)pieces from slow cooling showed a linear fracture.129 p.| il., grafs., tabs.porEngenharia de materiaisResistência de materiaisPorcelanatosEstudo do desenvolvimento de tensões residuais macroscópicas e do comportamento à fratura de porcelanatosinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccessORIGINAL341126.pdfapplication/pdf12928859https://repositorio.ufsc.br/bitstream/123456789/167731/1/341126.pdf6b2a57ac5c8a3bdccab4f089b8b52310MD51123456789/1677312016-09-20 01:14:56.396oai:repositorio.ufsc.br:123456789/167731Repositório de PublicaçõesPUBhttp://150.162.242.35/oai/requestopendoar:23732016-09-20T04:14:56Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.pt_BR.fl_str_mv Estudo do desenvolvimento de tensões residuais macroscópicas e do comportamento à fratura de porcelanatos
title Estudo do desenvolvimento de tensões residuais macroscópicas e do comportamento à fratura de porcelanatos
spellingShingle Estudo do desenvolvimento de tensões residuais macroscópicas e do comportamento à fratura de porcelanatos
Delavi, Deyse Gonzaga Gomes
Engenharia de materiais
Resistência de materiais
Porcelanatos
title_short Estudo do desenvolvimento de tensões residuais macroscópicas e do comportamento à fratura de porcelanatos
title_full Estudo do desenvolvimento de tensões residuais macroscópicas e do comportamento à fratura de porcelanatos
title_fullStr Estudo do desenvolvimento de tensões residuais macroscópicas e do comportamento à fratura de porcelanatos
title_full_unstemmed Estudo do desenvolvimento de tensões residuais macroscópicas e do comportamento à fratura de porcelanatos
title_sort Estudo do desenvolvimento de tensões residuais macroscópicas e do comportamento à fratura de porcelanatos
author Delavi, Deyse Gonzaga Gomes
author_facet Delavi, Deyse Gonzaga Gomes
author_role author
dc.contributor.pt_BR.fl_str_mv Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Delavi, Deyse Gonzaga Gomes
dc.contributor.advisor1.fl_str_mv Hotza, Dachamir
dc.contributor.advisor-co1.fl_str_mv Noni Junior, Agenor de
contributor_str_mv Hotza, Dachamir
Noni Junior, Agenor de
dc.subject.classification.pt_BR.fl_str_mv Engenharia de materiais
Resistência de materiais
Porcelanatos
topic Engenharia de materiais
Resistência de materiais
Porcelanatos
description Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia dos Materiais, Florianópolis, 2016.
publishDate 2016
dc.date.accessioned.fl_str_mv 2016-09-20T04:14:56Z
dc.date.available.fl_str_mv 2016-09-20T04:14:56Z
dc.date.issued.fl_str_mv 2016
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://repositorio.ufsc.br/xmlui/handle/123456789/167731
dc.identifier.other.pt_BR.fl_str_mv 341126
identifier_str_mv 341126
url https://repositorio.ufsc.br/xmlui/handle/123456789/167731
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 129 p.| il., grafs., tabs.
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
bitstream.url.fl_str_mv https://repositorio.ufsc.br/bitstream/123456789/167731/1/341126.pdf
bitstream.checksum.fl_str_mv 6b2a57ac5c8a3bdccab4f089b8b52310
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1766805228865191936

Registros relacionados