Chemical, morphological, rheological and thermal properties of Solanum lycocarpum phosphorylated starches

• Autor(a) principal: Ascheri,Diego Palmiro Ramirez
• Data de Publicação: 2014
• Outros Autores: Pereira,Luciane Dias, Bastos,Suely Miranda Cavalcante
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Revista Ceres
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0034-737X2014000400003
• topic: Solanum lycocarpum Saint Hillaire; wolf's fruit; modified starch; viscosity

The increasing need for starches with specific characteristics makes it important to study unconventional starches and their modifications in order to meet consumer demands. The aim of this work was to study physicochemical characteristics of native starch and phosphate starch of S. lycocarpum. Native starch was phosphated with sodium tripolyphosphate (5-11%) added with stirring. Chemical composition, morphology, density, binding ability to cold water, swelling power and solubility index, turbidity and syneresis, rheological and calorimetric properties were determined. Phosphorus was not detected in the native sample, but the phosphating process produced modified starches with phosphorus contents of 0.015, 0.092 and 0.397%, with the capacity of absorbing more water, either cold or hot. Rheological data showed the strong influence of phosphorus content on viscosity of phosphate starch, with lower pasting temperature and peak viscosity higher than those of native starch. Enthalpy was negatively correlated with the phosphorus content, requiring 9.7; 8.5; 8.1 and 6.4 kJ g-1 of energy for the transition from the amorphous to the crystalline state for the starch granules with phosphorus contents of 0; 0.015; 0.092 and 0.397%, respectively. Cluster analysis and principal component analysis showed that starches with 0.015 and 0.092% phosphorus have similar characteristics and are different from the others. Our results show that the characteristics of phosphate modified S. lycocarpum starch have optimal conditions to meet the demands of raw materials, which require greater consistency in stickiness, combined with low rates of retrogradation and syneresis.