Effects of erosive challenge on the morphology and surface properties of luting cements

• Autor(a) principal: GONDIM,Brenna Louise Cavalcanti
• Data de Publicação: 2016
• Outros Autores: MEDEIROS,Isabella Cavalcante, COSTA,Bruna Palmeira, CARLO,Hugo Lemes, SANTOS,Rogério Lacerda dos, CARVALHO,Fabíola Galbiatti de
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Revista de Odontologia da UNESP
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1807-25772016000200103
• topic: Tooth erosion; resin cements; glass ionomer cements; hardness tests

Abstract Introduction Few studies investigated the surface properties of luting cements after erosive challenge. Objective To evaluate the surface roughness (Ra), Vickers hardness (VHN) and morphology of 4 luting cements after erosive challenge. Material and method Twenty specimens of each cement were prepared (4×2mm) and divided into experimental (erosive challenge) and control (artificial saliva) groups (n=10): Rely X U200 (U200); Rely X ARC (ARC); Ketac Cem Easy Mix (Ketac) and Zinc phosphate (ZnP). The erosive challenge was performed by four daily erosive cycles (90s) in a cola drink and 2 h in artificial saliva over 7 days. Ra and VHN readings were performed before and after erosion. The percentage of hardness loss (%VHN) was obtained after erosion. The surface morphology was analyzed by scanning electron microscopy (SEM). ANOVA, Tukey and Student-T tests were used (α=0.05). Result After erosion, all luting cements had increase in Ra values and U200 and ZnP groups had the highest %VHN. After saliva immersion, only U200 and ZnP groups had significant increases in Ra values and there were no significant differences among the groups in %VHN. SEM analysis showed that Ketac and ZnP groups had rough and porous surfaces, and U200 group had higher resin matrix degradation than ARC group. Conclusion Erosive challenge with a cola drink affected the surface properties of all luting cements.