Effect of zirconia substructure thickness on the mechanical properties and adhesion of veneering porcelain
Autor(a) principal: | |
---|---|
Data de Publicação: | 2019 |
Outros Autores: | , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Brazilian journal of oral sciences (Online) |
Texto Completo: | https://periodicos.sbu.unicamp.br/ojs/index.php/bjos/article/view/8655139 |
Resumo: | Aim: This study investigated the influence of yttrium-stabilized tetragonal zirconia polycrystals (Y-TZP) thickness on fracture load of porcelain-veneered crowns (FL), fracture toughness of porcelain (FT), and the shear bond strength zirconia/porcelain (SBS). Methods: Artificial first molar was prepared for full crown (N=45) with different occlusal reduction. Y-TZP cores were made with different thickness at the occlusal face (1mm, 2mm and 3mm) (n=15). The cores were veneered with VM9 – Vita porcelain with 1.0 mm layer. For FL testing, axial load was applied to the mesiolingual cusp of the crowns. For FT testing, flat Y-TZP plates (5X5 mm) with 1, 2 or 3 mm thickness were veneered with 1.0 mm porcelain layer (n=10). FT by indentation fracture technique was measured close to the interface and at the top surface. For SBS by knife-edge shearing rod, cylindrical porcelain with 5 mm in diameter and 3 mm was applied on flat Y-TZP plates (1, 2 and 3 mm thickness) (n = 10). Results: Data analyzed by 1-Way ANOVA for FL of crowns and SBS between Y-TZP and porcelain were not significant. Two-way ANOVA for FT was significant for zirconia thickness and measurement area. The post-hoc test showed higher values for the groups with 2 and 3mm, and higher values at the interface, irrespectively of Y-TZP thickness. Conclusion: The zirconia thickness did not affect the FL of veneered crowns and the SBS between the ceramics, but FT of porcelain was lower in thinner zirconia substructure and close to the interface Y-TZP/Porcelain. |
id |
UNICAMP-8_a05153c0210e580c682b006f35da09ca |
---|---|
oai_identifier_str |
oai:ojs.periodicos.sbu.unicamp.br:article/8655139 |
network_acronym_str |
UNICAMP-8 |
network_name_str |
Brazilian journal of oral sciences (Online) |
repository_id_str |
|
spelling |
Effect of zirconia substructure thickness on the mechanical properties and adhesion of veneering porcelainZirconiumDental porcelainFracture toughness.Aim: This study investigated the influence of yttrium-stabilized tetragonal zirconia polycrystals (Y-TZP) thickness on fracture load of porcelain-veneered crowns (FL), fracture toughness of porcelain (FT), and the shear bond strength zirconia/porcelain (SBS). Methods: Artificial first molar was prepared for full crown (N=45) with different occlusal reduction. Y-TZP cores were made with different thickness at the occlusal face (1mm, 2mm and 3mm) (n=15). The cores were veneered with VM9 – Vita porcelain with 1.0 mm layer. For FL testing, axial load was applied to the mesiolingual cusp of the crowns. For FT testing, flat Y-TZP plates (5X5 mm) with 1, 2 or 3 mm thickness were veneered with 1.0 mm porcelain layer (n=10). FT by indentation fracture technique was measured close to the interface and at the top surface. For SBS by knife-edge shearing rod, cylindrical porcelain with 5 mm in diameter and 3 mm was applied on flat Y-TZP plates (1, 2 and 3 mm thickness) (n = 10). Results: Data analyzed by 1-Way ANOVA for FL of crowns and SBS between Y-TZP and porcelain were not significant. Two-way ANOVA for FT was significant for zirconia thickness and measurement area. The post-hoc test showed higher values for the groups with 2 and 3mm, and higher values at the interface, irrespectively of Y-TZP thickness. Conclusion: The zirconia thickness did not affect the FL of veneered crowns and the SBS between the ceramics, but FT of porcelain was lower in thinner zirconia substructure and close to the interface Y-TZP/Porcelain.Universidade Estadual de Campinas2019-04-08info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersionOriginal articleapplication/pdfhttps://periodicos.sbu.unicamp.br/ojs/index.php/bjos/article/view/865513910.20396/bjos.v18i0.8655139Brazilian Journal of Oral Sciences; v. 18 (2019): Continuous Publication; e190919Brazilian Journal of Oral Sciences; Vol. 18 (2019): Continuous Publication; e1909191677-3225reponame:Brazilian journal of oral sciences (Online)instname:Universidade Estadual de Campinas (UNICAMP)instacron:UNICAMPenghttps://periodicos.sbu.unicamp.br/ojs/index.php/bjos/article/view/8655139/208172019Lungareze, DanielCunha, GiovanniMariscal Muñoz, EduardoFonseca, Renata GarciaAdabo, Gelsoninfo:eu-repo/semantics/openAccess2020-12-22T01:33:53Zoai:ojs.periodicos.sbu.unicamp.br:article/8655139Revistahttps://periodicos.sbu.unicamp.br/ojs/index.php/bjos/PUBhttps://periodicos.sbu.unicamp.br/ojs/index.php/bjos/oaibrjorals@fop.unicamp.br||brjorals@fop.unicamp.br1677-32251677-3217opendoar:2020-12-22T01:33:53Brazilian journal of oral sciences (Online) - Universidade Estadual de Campinas (UNICAMP)false |
dc.title.none.fl_str_mv |
Effect of zirconia substructure thickness on the mechanical properties and adhesion of veneering porcelain |
title |
Effect of zirconia substructure thickness on the mechanical properties and adhesion of veneering porcelain |
spellingShingle |
Effect of zirconia substructure thickness on the mechanical properties and adhesion of veneering porcelain Lungareze, Daniel Zirconium Dental porcelain Fracture toughness. |
title_short |
Effect of zirconia substructure thickness on the mechanical properties and adhesion of veneering porcelain |
title_full |
Effect of zirconia substructure thickness on the mechanical properties and adhesion of veneering porcelain |
title_fullStr |
Effect of zirconia substructure thickness on the mechanical properties and adhesion of veneering porcelain |
title_full_unstemmed |
Effect of zirconia substructure thickness on the mechanical properties and adhesion of veneering porcelain |
title_sort |
Effect of zirconia substructure thickness on the mechanical properties and adhesion of veneering porcelain |
author |
Lungareze, Daniel |
author_facet |
Lungareze, Daniel Cunha, Giovanni Mariscal Muñoz, Eduardo Fonseca, Renata Garcia Adabo, Gelson |
author_role |
author |
author2 |
Cunha, Giovanni Mariscal Muñoz, Eduardo Fonseca, Renata Garcia Adabo, Gelson |
author2_role |
author author author author |
dc.contributor.author.fl_str_mv |
Lungareze, Daniel Cunha, Giovanni Mariscal Muñoz, Eduardo Fonseca, Renata Garcia Adabo, Gelson |
dc.subject.por.fl_str_mv |
Zirconium Dental porcelain Fracture toughness. |
topic |
Zirconium Dental porcelain Fracture toughness. |
description |
Aim: This study investigated the influence of yttrium-stabilized tetragonal zirconia polycrystals (Y-TZP) thickness on fracture load of porcelain-veneered crowns (FL), fracture toughness of porcelain (FT), and the shear bond strength zirconia/porcelain (SBS). Methods: Artificial first molar was prepared for full crown (N=45) with different occlusal reduction. Y-TZP cores were made with different thickness at the occlusal face (1mm, 2mm and 3mm) (n=15). The cores were veneered with VM9 – Vita porcelain with 1.0 mm layer. For FL testing, axial load was applied to the mesiolingual cusp of the crowns. For FT testing, flat Y-TZP plates (5X5 mm) with 1, 2 or 3 mm thickness were veneered with 1.0 mm porcelain layer (n=10). FT by indentation fracture technique was measured close to the interface and at the top surface. For SBS by knife-edge shearing rod, cylindrical porcelain with 5 mm in diameter and 3 mm was applied on flat Y-TZP plates (1, 2 and 3 mm thickness) (n = 10). Results: Data analyzed by 1-Way ANOVA for FL of crowns and SBS between Y-TZP and porcelain were not significant. Two-way ANOVA for FT was significant for zirconia thickness and measurement area. The post-hoc test showed higher values for the groups with 2 and 3mm, and higher values at the interface, irrespectively of Y-TZP thickness. Conclusion: The zirconia thickness did not affect the FL of veneered crowns and the SBS between the ceramics, but FT of porcelain was lower in thinner zirconia substructure and close to the interface Y-TZP/Porcelain. |
publishDate |
2019 |
dc.date.none.fl_str_mv |
2019-04-08 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article info:eu-repo/semantics/publishedVersion Original article |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
https://periodicos.sbu.unicamp.br/ojs/index.php/bjos/article/view/8655139 10.20396/bjos.v18i0.8655139 |
url |
https://periodicos.sbu.unicamp.br/ojs/index.php/bjos/article/view/8655139 |
identifier_str_mv |
10.20396/bjos.v18i0.8655139 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
https://periodicos.sbu.unicamp.br/ojs/index.php/bjos/article/view/8655139/20817 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.coverage.none.fl_str_mv |
2019 |
dc.publisher.none.fl_str_mv |
Universidade Estadual de Campinas |
publisher.none.fl_str_mv |
Universidade Estadual de Campinas |
dc.source.none.fl_str_mv |
Brazilian Journal of Oral Sciences; v. 18 (2019): Continuous Publication; e190919 Brazilian Journal of Oral Sciences; Vol. 18 (2019): Continuous Publication; e190919 1677-3225 reponame:Brazilian journal of oral sciences (Online) instname:Universidade Estadual de Campinas (UNICAMP) instacron:UNICAMP |
instname_str |
Universidade Estadual de Campinas (UNICAMP) |
instacron_str |
UNICAMP |
institution |
UNICAMP |
reponame_str |
Brazilian journal of oral sciences (Online) |
collection |
Brazilian journal of oral sciences (Online) |
repository.name.fl_str_mv |
Brazilian journal of oral sciences (Online) - Universidade Estadual de Campinas (UNICAMP) |
repository.mail.fl_str_mv |
brjorals@fop.unicamp.br||brjorals@fop.unicamp.br |
_version_ |
1800216402349522944 |