Dentin permeability after pretreatment with titanium tetrafluoride and self-etching or universal adhesive systems

• Autor(a) principal: Franco, Gabriel Greco
• Data de Publicação: 2023
• Outros Autores: Cardoso, Ruthinea Faria de Moraes, Carlos, Natália Russo, Turssi, Cecilia Pedroso, Amaral, Flávia Lucisano Botelho do, França, Fabiana Mantovani Gomes, Basting, Roberta Tarkany
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Brazilian journal of oral sciences (Online)
• Texto Completo: https://periodicos.sbu.unicamp.br/ojs/index.php/bjos/article/view/8667545
• topic: Dentin permeability; Dentin-bonding agents; Titanium; Fluorides

Aim: To evaluate dentin permeability after pretreatment with 2.5% aqueous solution of titanium tetrafluoride (TiF4), followed by a self-etching universal adhesive system. Methods: Forty dentin discs (1.5 mm thick) were randomly divided into groups according to the application or non-application of a pretreatment, and the type of adhesive system to be tested (two-step self-etching/ Clearfil SE Bond/ Kuraray Medical, or universal adhesive system/ Single Bond Universal/ 3M ESPE). Both sides of the discs were conditioned with 37% phosphoric acid to remove the smear layer. The first hydraulic conductivity measurement (L1) was performed in a permeability machine, under 5 PSI pressure. The samples were sanded again to form a standardized smear layer. The teeth designated for pre-treatment with TiF4 received the TiF4 solutions applied actively for 60 seconds, and the adhesive systems were applied according to the manufacturer’s instructions. Then, a new hydraulic conductivity measurement (L2) was performed for the purpose of calculating the hydraulic conductance at a later time, considering the water viscosity and the thickness of the specimen. The percentage (L) of dentin permeability after application of the adhesive system was obtained (L (%) = [(L1-L2) x100] / L1). The Mann-Whitney non-parametric test was applied. Results: There was no difference between the two adhesive systems, or between the groups with or without pretreatment, as regards dentin permeability (p>0.05). Conclusion: Pretreatment with 2.5% TiF4 did not influence dentin permeability, irrespective of the adhesive system used.