Efeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescência
Autor(a) principal: | |
---|---|
Data de Publicação: | 2017 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações do UNIOESTE |
Texto Completo: | http://tede.unioeste.br/handle/tede/3774 |
Resumo: | The aim of this research was to compare the behavior of different thicknesses of bulk fill composite resins by analyzing the microhardness at the top and bottom of specimens (SP), the effect of aging with acid solution (ethanol / water) and fluorescence evaluation. 135 SP were fabricated with thicknesses of 2, 3 and 4 mm subdivided into 5 groups (n = 27): Z35; Aura; Tetric; SureFil; Filtek Bulk Fill (FBF). Each SP was photoactivated by LED light for 20 seconds. The microhardness test was performed after 24 hours and 30 days (ethanol / water solution) on both top and bottom surfaces. Fluorescence analysis was performed with the aid of a dark chamber by three calibrators: low, medium and high. The microhardness data were submitted to the factorial ANOVA test for Repeated Measures, followed by the LSD-Fisher follow-up test. Fluorescence by the LSD-Fisher Test. After 24h the microhardness was higher at the top in the thickness of 2mm: TETRIC and FBF, 3mm: Z350, TETRIC and FBF, 4mm: Z350, AURA, TETRIC and FBF. After aging the highest values in the bottom: 2mm: TETRIC and FBF, 3mm: AURA and TETRIC, in the 4mm: AURA was significantly higher than the first average. (p <0.05). It was possible to close that the larger the thickness, the greater the difference of the microhardness between the top and bottom surfaces. With regard to fluorescence, TETRIC (BF) was the only composite resin that did not have significantly altered values with increasing thickness. Aging in ethanol / water solution increased the microhardness values of some TETRIC, FBF and AURA composite resins. |
id |
UNIOESTE-1_f1dfe53b38d6491be76c20bb3256e0e6 |
---|---|
oai_identifier_str |
oai:tede.unioeste.br:tede/3774 |
network_acronym_str |
UNIOESTE-1 |
network_name_str |
Biblioteca Digital de Teses e Dissertações do UNIOESTE |
repository_id_str |
|
spelling |
Camilotti, Veridianahttp://lattes.cnpq.br/9340494276264996Busato, Mauro Carlos Agnerhttp://lattes.cnpq.br/1189765186576000Camilotti, Veridianahttp://lattes.cnpq.br/9340494276264996Pini, Núbia Inocencya Pavesihttp://lattes.cnpq.br/0798226450922503http://lattes.cnpq.br/8403282070630908Ferreira, Lyvia Karla Cerci2018-06-25T18:13:37Z2017-02-10FERREIRA, Lyvia Karla Cerci. Efeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescência. 2017. 35 f. Dissertação( Mestrado em Odontologia) - Universidade Estadual do Oeste do Paraná, Cascavel, 2017.http://tede.unioeste.br/handle/tede/3774The aim of this research was to compare the behavior of different thicknesses of bulk fill composite resins by analyzing the microhardness at the top and bottom of specimens (SP), the effect of aging with acid solution (ethanol / water) and fluorescence evaluation. 135 SP were fabricated with thicknesses of 2, 3 and 4 mm subdivided into 5 groups (n = 27): Z35; Aura; Tetric; SureFil; Filtek Bulk Fill (FBF). Each SP was photoactivated by LED light for 20 seconds. The microhardness test was performed after 24 hours and 30 days (ethanol / water solution) on both top and bottom surfaces. Fluorescence analysis was performed with the aid of a dark chamber by three calibrators: low, medium and high. The microhardness data were submitted to the factorial ANOVA test for Repeated Measures, followed by the LSD-Fisher follow-up test. Fluorescence by the LSD-Fisher Test. After 24h the microhardness was higher at the top in the thickness of 2mm: TETRIC and FBF, 3mm: Z350, TETRIC and FBF, 4mm: Z350, AURA, TETRIC and FBF. After aging the highest values in the bottom: 2mm: TETRIC and FBF, 3mm: AURA and TETRIC, in the 4mm: AURA was significantly higher than the first average. (p <0.05). It was possible to close that the larger the thickness, the greater the difference of the microhardness between the top and bottom surfaces. With regard to fluorescence, TETRIC (BF) was the only composite resin that did not have significantly altered values with increasing thickness. Aging in ethanol / water solution increased the microhardness values of some TETRIC, FBF and AURA composite resins.O objetivo desta pesquisa foi de comparar o comportamento de diferentes espessuras de incrementos das resinas compostas tipo bulk fill, por meio da análise da microdureza no topo e na base de corpos-de-prova (CP), efeito do envelhecimento com solução ácida (etanol/água) e a avaliação da fluorescência Foram confeccionados 135 CP com espessuras de 2, 3, e 4mm subdivididos em 5 grupos (n=27): resina Z350;Aura bulk fill (AURA); Tetric bulk fill (TETRIC); SureFil bulk fill (SDR). ; Filtek bulk fill (FBF). Cada CP foi fotoativado por aparelho de luz Led durante 20 segundos. O teste de microdureza foi realizado após 24 horas e 30 dias (solução etanol/água) tanto na superfície do topo como na base. A análise da fluorescência foi realizada com auxílio de uma câmara escura por três avaliadores calibrados como: baixa, média e alta. Os dados de microdureza foram submetidos ao teste ANOVA fatorial para Medidas Repetidas, seguido pelo teste de acompanhamento de LSD-Fisher. A fluorescência pelo teste Teste LSD-Fisher. Após 24hs a microdureza foi maior no topo na espessura de 2mm: TBF e FBF, 3mm: Z350, TBF e FBF, 4mm: Z350, ABF, TBF e FBF. Após o envelhecimento os maiores valores na base: 2mm: TBF e FBF, 3mm: ABF e TBF, na de 4mm: ABF foi significativamente maior do que a média inicial. (p<0,05). Foi possível concluir que quanto maior a espessura, maior a diferença da microdureza entre a superfície de topo e base. Com relação a fluorescência a TBF foi a única resina composta que não teve os valores alterados de forma significativa com o aumento da espessura. O envelhecimento em solução etanol/água aumentou os valores de microdureza de algumas resinas compostas TBF, FBF e ABF.Submitted by Rosangela Silva (rosangela.silva3@unioeste.br) on 2018-06-25T18:13:37Z No. of bitstreams: 2 Lyvia Karla Cerci Ferreira Bertacchini.pdf: 1676300 bytes, checksum: a3dc364eb9c66a1393c6417ee5dfd749 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5)Made available in DSpace on 2018-06-25T18:13:37Z (GMT). No. of bitstreams: 2 Lyvia Karla Cerci Ferreira Bertacchini.pdf: 1676300 bytes, checksum: a3dc364eb9c66a1393c6417ee5dfd749 (MD5) license_rdf: 0 bytes, checksum: d41d8cd98f00b204e9800998ecf8427e (MD5) Previous issue date: 2017-02-10Fundação Araucária de Apoio ao Desenvolvimento Científico e Tecnológico do Estado do Paraná (FA)Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfpor6588633818200016417500Universidade Estadual do Oeste do ParanáCascavelPrograma de Pós-Graduação em OdontologiaUNIOESTEBrasilCentro de Ciências Biológicas e da Saúdehttp://creativecommons.org/licenses/by-nc-nd/4.0/info:eu-repo/semantics/openAccessResina Bulk fillMicrodurezaFluorescênciaBulk fill resinsMicrohardnessFluorescenceCIENCIAS DA SAUDE::ODONTOLOGIAEfeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescênciaEffect of resin thickness, solvent storage on the micro-hardness and fluorescence of bulk-fill resin compositesinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-80965548187336651646006006006006001458059979463924370-34391788430682021616231349731063126642075167498588264571reponame:Biblioteca Digital de Teses e Dissertações do UNIOESTEinstname:Universidade Estadual do Oeste do Paraná (UNIOESTE)instacron:UNIOESTEORIGINALLyvia Karla Cerci Ferreira Bertacchini.pdfLyvia Karla Cerci Ferreira Bertacchini.pdfapplication/pdf1676300http://tede.unioeste.br:8080/tede/bitstream/tede/3774/5/Lyvia+Karla+Cerci+Ferreira+Bertacchini.pdfa3dc364eb9c66a1393c6417ee5dfd749MD55CC-LICENSElicense_urllicense_urltext/plain; charset=utf-849http://tede.unioeste.br:8080/tede/bitstream/tede/3774/2/license_url4afdbb8c545fd630ea7db775da747b2fMD52license_textlicense_texttext/html; charset=utf-80http://tede.unioeste.br:8080/tede/bitstream/tede/3774/3/license_textd41d8cd98f00b204e9800998ecf8427eMD53license_rdflicense_rdfapplication/rdf+xml; charset=utf-80http://tede.unioeste.br:8080/tede/bitstream/tede/3774/4/license_rdfd41d8cd98f00b204e9800998ecf8427eMD54LICENSElicense.txtlicense.txttext/plain; charset=utf-82165http://tede.unioeste.br:8080/tede/bitstream/tede/3774/1/license.txtbd3efa91386c1718a7f26a329fdcb468MD51tede/37742018-06-25 17:37:18.129oai:tede.unioeste.br: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Biblioteca Digital de Teses e Dissertaçõeshttp://tede.unioeste.br/PUBhttp://tede.unioeste.br/oai/requestbiblioteca.repositorio@unioeste.bropendoar:2018-06-25T20:37:18Biblioteca Digital de Teses e Dissertações do UNIOESTE - Universidade Estadual do Oeste do Paraná (UNIOESTE)false |
dc.title.por.fl_str_mv |
Efeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescência |
dc.title.alternative.eng.fl_str_mv |
Effect of resin thickness, solvent storage on the micro-hardness and fluorescence of bulk-fill resin composites |
title |
Efeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescência |
spellingShingle |
Efeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescência Ferreira, Lyvia Karla Cerci Resina Bulk fill Microdureza Fluorescência Bulk fill resins Microhardness Fluorescence CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Efeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescência |
title_full |
Efeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescência |
title_fullStr |
Efeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescência |
title_full_unstemmed |
Efeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescência |
title_sort |
Efeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescência |
author |
Ferreira, Lyvia Karla Cerci |
author_facet |
Ferreira, Lyvia Karla Cerci |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Camilotti, Veridiana |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/9340494276264996 |
dc.contributor.referee1.fl_str_mv |
Busato, Mauro Carlos Agner |
dc.contributor.referee1Lattes.fl_str_mv |
http://lattes.cnpq.br/1189765186576000 |
dc.contributor.referee2.fl_str_mv |
Camilotti, Veridiana |
dc.contributor.referee2Lattes.fl_str_mv |
http://lattes.cnpq.br/9340494276264996 |
dc.contributor.referee3.fl_str_mv |
Pini, Núbia Inocencya Pavesi |
dc.contributor.referee3Lattes.fl_str_mv |
http://lattes.cnpq.br/0798226450922503 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/8403282070630908 |
dc.contributor.author.fl_str_mv |
Ferreira, Lyvia Karla Cerci |
contributor_str_mv |
Camilotti, Veridiana Busato, Mauro Carlos Agner Camilotti, Veridiana Pini, Núbia Inocencya Pavesi |
dc.subject.por.fl_str_mv |
Resina Bulk fill Microdureza Fluorescência |
topic |
Resina Bulk fill Microdureza Fluorescência Bulk fill resins Microhardness Fluorescence CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.eng.fl_str_mv |
Bulk fill resins Microhardness Fluorescence |
dc.subject.cnpq.fl_str_mv |
CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
The aim of this research was to compare the behavior of different thicknesses of bulk fill composite resins by analyzing the microhardness at the top and bottom of specimens (SP), the effect of aging with acid solution (ethanol / water) and fluorescence evaluation. 135 SP were fabricated with thicknesses of 2, 3 and 4 mm subdivided into 5 groups (n = 27): Z35; Aura; Tetric; SureFil; Filtek Bulk Fill (FBF). Each SP was photoactivated by LED light for 20 seconds. The microhardness test was performed after 24 hours and 30 days (ethanol / water solution) on both top and bottom surfaces. Fluorescence analysis was performed with the aid of a dark chamber by three calibrators: low, medium and high. The microhardness data were submitted to the factorial ANOVA test for Repeated Measures, followed by the LSD-Fisher follow-up test. Fluorescence by the LSD-Fisher Test. After 24h the microhardness was higher at the top in the thickness of 2mm: TETRIC and FBF, 3mm: Z350, TETRIC and FBF, 4mm: Z350, AURA, TETRIC and FBF. After aging the highest values in the bottom: 2mm: TETRIC and FBF, 3mm: AURA and TETRIC, in the 4mm: AURA was significantly higher than the first average. (p <0.05). It was possible to close that the larger the thickness, the greater the difference of the microhardness between the top and bottom surfaces. With regard to fluorescence, TETRIC (BF) was the only composite resin that did not have significantly altered values with increasing thickness. Aging in ethanol / water solution increased the microhardness values of some TETRIC, FBF and AURA composite resins. |
publishDate |
2017 |
dc.date.issued.fl_str_mv |
2017-02-10 |
dc.date.accessioned.fl_str_mv |
2018-06-25T18:13:37Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
FERREIRA, Lyvia Karla Cerci. Efeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescência. 2017. 35 f. Dissertação( Mestrado em Odontologia) - Universidade Estadual do Oeste do Paraná, Cascavel, 2017. |
dc.identifier.uri.fl_str_mv |
http://tede.unioeste.br/handle/tede/3774 |
identifier_str_mv |
FERREIRA, Lyvia Karla Cerci. Efeito da espessura e do envelhecimento por solução ácida de diferentes resinas compostas bulk fill nas propriedades de microdureza superficial e fluorescência. 2017. 35 f. Dissertação( Mestrado em Odontologia) - Universidade Estadual do Oeste do Paraná, Cascavel, 2017. |
url |
http://tede.unioeste.br/handle/tede/3774 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-8096554818733665164 |
dc.relation.confidence.fl_str_mv |
600 600 600 600 600 |
dc.relation.department.fl_str_mv |
1458059979463924370 |
dc.relation.cnpq.fl_str_mv |
-3439178843068202161 |
dc.relation.sponsorship.fl_str_mv |
623134973106312664 2075167498588264571 |
dc.rights.driver.fl_str_mv |
http://creativecommons.org/licenses/by-nc-nd/4.0/ info:eu-repo/semantics/openAccess |
rights_invalid_str_mv |
http://creativecommons.org/licenses/by-nc-nd/4.0/ |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Estadual do Oeste do Paraná Cascavel |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Odontologia |
dc.publisher.initials.fl_str_mv |
UNIOESTE |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Centro de Ciências Biológicas e da Saúde |
publisher.none.fl_str_mv |
Universidade Estadual do Oeste do Paraná Cascavel |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações do UNIOESTE instname:Universidade Estadual do Oeste do Paraná (UNIOESTE) instacron:UNIOESTE |
instname_str |
Universidade Estadual do Oeste do Paraná (UNIOESTE) |
instacron_str |
UNIOESTE |
institution |
UNIOESTE |
reponame_str |
Biblioteca Digital de Teses e Dissertações do UNIOESTE |
collection |
Biblioteca Digital de Teses e Dissertações do UNIOESTE |
bitstream.url.fl_str_mv |
http://tede.unioeste.br:8080/tede/bitstream/tede/3774/5/Lyvia+Karla+Cerci+Ferreira+Bertacchini.pdf http://tede.unioeste.br:8080/tede/bitstream/tede/3774/2/license_url http://tede.unioeste.br:8080/tede/bitstream/tede/3774/3/license_text http://tede.unioeste.br:8080/tede/bitstream/tede/3774/4/license_rdf http://tede.unioeste.br:8080/tede/bitstream/tede/3774/1/license.txt |
bitstream.checksum.fl_str_mv |
a3dc364eb9c66a1393c6417ee5dfd749 4afdbb8c545fd630ea7db775da747b2f d41d8cd98f00b204e9800998ecf8427e d41d8cd98f00b204e9800998ecf8427e bd3efa91386c1718a7f26a329fdcb468 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações do UNIOESTE - Universidade Estadual do Oeste do Paraná (UNIOESTE) |
repository.mail.fl_str_mv |
biblioteca.repositorio@unioeste.br |
_version_ |
1811723398728908800 |