Capacidade de termoplastificação da guta-percha com diferentes conicidades

• Autor(a) principal: Nascimento, Camila Almeida [UNESP]
• Data de Publicação: 2010
• Outros Autores: Tanomaru-Filho, Mário [UNESP], Bosso, Roberta [UNESP], Kuga, Milton Carlos [UNESP], Guerreiro-Tanomaru, Juliane Maria [UNESP]
• Tipo de documento: Artigo
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://www.revodontolunesp.com.br/article/51ae4aa61ef1faca3d003614?languageSelector=en&; http://hdl.handle.net/11449/126100
• topic: Endodontics; Root canal obturation; Gutta-percha; Guta-percha; Material Obturador de Canal Radicular; Termoplastificação

jObjective: The objective of this study was to evaluate the thermoplasticity of the gutta-percha cones used for root canal obturation: Dentsply convencional (Dentsply Ind. e Com., Petrópolis, RJ, Brazil), Dentsply 0.04, (Dentsply Ind. e Com., Petrópolis, RJ, Brazil), Antaeos 0.04 (VDW GmbH, Munich, Germany), ProTaper (Dentsply Ind. e Com., Petrópolis, RJ, Brazil) and Alfa 0.06 (VDW GmbH, Munich, Germany). Material and method: Specimens of each material (n = 10) were prepared after heating. After 24 hours were again heated to 70 °C and placed between two glass plates and subjected to a compression of 5 kg for 2 minutes. The scanned image of the groups before and after the compression was analyzed with the software Image Tool (UTHSCSA Image Tool for Windows version 3.0, San Antonio, TX, USA). The flow capacity of the different materials was determined by the difference between the initial and final area of each specimen. The results were submitted to ANOVA and Tukey test with significance level of 5%. Result: Among the material evaluated, the gutta-percha cones Alpha 0.06 and ProTaper presented more thermoplasticity than other groups (p < 0.05). The Dentsply gutta-percha presented thermoplasticity intermediate. The groups Dentsply 0.04 and 0.04 showed lower thermoplasticity after heating (p > 0.05). Conclusion: The gutta-percha present different property of thermoplasticity, which is important to selection of thermoplastic obturation techniques.