Avaliação da termociclagem sobre a estabilidade de cor de diferentes matizes de resina composta

• Autor(a) principal: Okida, Ricardo Coelho [UNESP]
• Data de Publicação: 2014
• Outros Autores: Santos, Daniela Micheline dos [UNESP], Okida, Daniela Secches da Silveira [UNESP], Machado, Lucas Silveira [UNESP]
• Tipo de documento: Artigo
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://apcdaracatuba.com.br/revista/2014/10/v35n122014.htm; http://hdl.handle.net/11449/133486
• topic: Composite Resin; Color; Comparative study; Resina composta; Cor; Estudo comparativo

The objective was to evaluate the effect of thermocycling on the color variation of three different composite resins . We studied was Resin Enamel on 3 levels : ( Esthetic X , Opallis and Venus ) ; Resin Dentin in three levels : ( Esthetic X , Opallis and Venus ) and Thermocycling on level 1 : ( 3,000 cycles ) ; variable was the change of color gauged by spectrophotometry . 60 specimens , subdivided into 6 groups were made : GI - Esthetic X Enamel ; GII - Esthetic X dentin ; GIII - Opallis Enamel ; GIV - Opallis dentin ; GV - Enamel and GVI Venus - Venus dentin . The specimens were prepared with a matrix to standardize samples . The inserts of incrementally resins and polymerized with a halogen light Ultralux unit ( Dabi Atlante , Brazil ) with a power of 450mW / cm ² . After fabrication , underwent color reading with a UV Visible Spectrophotometer reflection , UV -2450 ( Shimadzu , Kyoto , Japan ) , with the changes calculated by the system CIE L * a * b * . Then isolates were stored in artificial saliva at 35 ° C ± 2 ° C during 3 months containers being subjected to the effects of thermal cycling for 3000 cycles over the range of 5C to 55C . Again subjected to chromatic evaluation. For the analysis of the results of color change of the studied resins was applied ANOVA two factors at 5 % . The results showed a statistically equal resins enamel GI and GV ( p = 0.79 ) ; the same was not observed for GI and G III resins , where the color change was higher for resin G III ( p = 0.0000002 ) . The same was observed between G III and GV , where the resin enamel G III showed a statistically superior to the color change ( p = 0.0000005 ) Average . Resins to dentin was there a statistical equality between the materials studied . We conclude that the resins studied change in color and resin enamel G III was the most suffered major color changes after aging by thermocycling .