Effect of thermocycling on the bond strength of a glass-infiltrated ceramic and a resin luting cement

• Autor(a) principal: Andreatta Filho, Osvaldo Daniel [UNESP]
• Data de Publicação: 2003
• Outros Autores: Bottino, Marco Antonio [UNESP], Nishioka, Renato Sussumu [UNESP], Valandro, Luiz Felipe, Leite, Fabíola Pessoa Pereira [UNESP]
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://dx.doi.org/10.1590/S1678-77572003000100011; http://hdl.handle.net/11449/213045
• topic: Dental ceramics; Resin cements; Air abrasion; Cerâmica dental; Cimentos resinosos; Abrasão dental por ar

The aim of the present study was to evaluate the effect of thermocycling on the bond strength between the surface of the glass-infiltrated alumina ceramic In-Ceram (VITA) and the Panavia F resin cement (Kuraray CO.). Four 5x6x6mm In-Ceram blocks were obtained. One of the 6x6mm faces of each block was conditioned with Cojet - System (tribochemical silica coating, ESPE-3M) and then luted under a constant 750g pressure with Panavia F cement to another identical face of a resin composit block (Clearfil AP-X, Kuraray) obtained by reproduction of the ceramic one from Express (3M) addition curing silicone impressions. The four sets so formed by ceramic, luting cement and resin have been each one serially sectioned in 20 sticks so that the adhesive surface in each presented 1mm² of area. The samples were divided in 2 groups (n=10): G1- stored for 7 days in deionized water at 36 ± 2ºC; G2 - thermocycled 1500 times between 5 and 55ºC dwell times. The microtensile tests were accomplished in an universal testing machine (EMIC) at a crosshead speed of 0,5 mm/min. The results showed that the mean tensile bond strength values (MPa) for the group G2: (22,815 ± 5,254) had not statistically differ of the values of group G1: (25,628 ± 3,353) (t = 1,427; gl = 18; p-value = 0,171), at the level of a= 5%. It can be concluded that the thermocycling technique used in the present experiment had not produced statistically significant differences between the bond strength results of the specimens obtained by the two used techniques.