Pre-sintered Y-TZP sandblasting: effect on surface roughness, phase transformation, and Y-TZP/veneer bond strength

• Autor(a) principal: Ramos-Tonello, Carla Muller
• Data de Publicação: 2017
• Outros Autores: Trevizo, Bruno Freitas, Rodrigues, Raphaela Farias, Rodrigues Magalhaes, Ana Paula, Furuse, Adilson Yoshio, Lisboa-Filho, Paulo Noronha [UNESP], Tabata, Americo Sheitiro [UNESP], Sanches Borges, Ana Flavia
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://dx.doi.org/10.1590/1678-7757-2017-0131; http://hdl.handle.net/11449/163571
• topic: Zirconium; Ceramics; Surface properties; Shear strength

Sandblasting is a common method to try to improve the Y-TZP/veneer bond strength of dental prostheses, however, it may put stress on zirconia surfaces and could accelerate the t -> m phase transformation. Y-TZP sandblasting before sintering could be an alternative to improve surface roughness and bonding strength of veneering ceramic. Objectives. The aim of this study was to analyze the effect of Y-TZP pre-sintering sandblasting on surface roughness, phase transformation, and the Y-TZP/veneer shear bond strength. Material and Methods. The Y-TZP specimen surface underwent sandblasting with aluminum oxide (50 mu m) pre-sintering (Z-PRE) and post sintering (Z-POS). Z-CTR was not subjected to surface treatment. After ceramic veneer application, the specimens were subjected to shear bond testing. Surface roughness was analyzed by confocal microscopy. Y-TZP monoclinic and tetragonal phases were evaluated by micro-Raman spectroscopy. Shear bond strength and surface roughness data were analyzed by One-way ANOVA and Tukey tests (alpha=0.05). Differences in the wave numbers and the broadening bands of the Raman spectra were compared among groups. Results. Z-POS (9.73 +/- 5.36 MPa) and Z-PRE (7.94 +/- 2.52 MPa) showed the highest bond strength, significantly higher than that of Z-CTR (5.54 +/- 2.14 MPa). The Ra of Z-PRE (1.59 +/- 0.23 mu m) was much greater and significantly different from that of Z-CTR (0.29 +/- 0.05 mu m) and Z-POS (0.77 +/- 0.13 mu m). All groups showed bands typical of the tetragonal (T) and monoclinic (M) phases. Y-TZP sandblasting before sintering resulted in rougher surfaces but did not increase the shear bond strength compared to post-sintering and increased surface defects. Conclusions. Surface treatment with Al3O2, regardless of the moment and application, improves the results of Y-TZP/veneer bonding and is not a specific cause of t -> m transformation.