Tratamento de modificação de eutético da liga AA356

• Autor(a) principal: Coluci, Marcelo Araujo Pinto [UNESP]
• Data de Publicação: 2011
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/118707
• topic: Fundição; Ligas de aluminio; Microestrutura; Eutectic Structure; Microstructure

Alloy Al-7%Si-0,3Mg (AA356), having an excellent combination of properties such as low solidification shrinkage and good fluidity, good weldability, high wear resistance, high strength to weight particularly in the automotive and aerospace engineering. The refinement of the structure aluminum silicon eutectic alloy is a fairly common practice in the casting, through the treatment knows as modification. You can get the modification for the addition of chemicals and rare earths, these have the ability to modify the structure of the eutectic, but only sodium and strontium produce a strong action modifier when used in low concentrations. The modifying effect of silicon grain turns into a fibrous form branched and enveloped by the metal matrix in the form of a composite structure that has the highest limit of tensile strength, ductility and machinability. This work will be obtained AA356 alloy ingots using two different types of molds: metal mold and sand mold. Macrographs will be made in ingots obtained for observation of the macrostructures obtained in both types of ingots. Will be sampled at strategic locations of the ingots to correlate microstructure and cooling rate. The results showed that the material of the ingot has a strong influence on the resulting micro-andmacrostructure