Efeito do Estrôncio (Sr) no tratamento de modificação do eutético da liga Al-1%Si

• Autor(a) principal: Pêcego, Felipe Pinto [UNESP]
• Data de Publicação: 2013
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/120458
• topic: Ligas de aluminio; Resfriamento; Microestrutura; Fundição; Solidificação; Aluminum alloys

This study aimed to analyze the cooling curves, micro and macrograph alloy Al-1 %Si without the addition of strontium modifier and with the addition of the same. One of the ways of improving mechanical properties of alloy Al -Si is through the modification process. For the experiments two billets of the alloy Al-1%Si cast iron mold in a billet with addition of 0.02% strontium by weight, and the other billet without the addition of modifier were fused. In the solidification process of billet temperature was monitored and recorded every second for later plotting in Origin 8 program and analyzes the cooling curves obtained. The billets were cut and passed by grinding and polishing to perform the macrograph and micrographs. The results concerning the macrograph indicated that billet without the addition of Strontium particle size obtained was more refined than the billet where the strontium modifier was added. Regarding the micrograph, photos stemmed from the optical microscope didn´t show the expected modification effect by the addition of Strontium. This suggests that the low amount of silicon (1 %) present in the alloy used in this study interfered in the change process, because according to the literature review, Strontium 0.022 % by weight is sufficient to fully modify an alloy with 7% Silicon. The results from the cooling curve showed that both the eutectic temperature and the solidification time remained unchanged with the addition of strontium