Emprego de carvão ativado e resinas de troca ionica na remoção de substâncias orgânicas contaminantes do alcool etílico

• Autor(a) principal: Salata, Cristiane da Cunha
• Data de Publicação: 2010
• Outros Autores: Cabello, Claudio [UNESP]
• Tipo de documento: Artigo
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://dx.doi.org/10.17766/1808-981X.2010v6n1p83-91; http://hdl.handle.net/11449/134418
• topic: Cassava ethanol; Adsorption; Purification; Neutral alcohol; Etanol de mandioca; Adsorção; Purificação; Álcool neutro

This work had with objective to characterize and evaluate the performance of the combined system, involving activated charcoal and ionic exchange resins in the removal of substances organic contaminating of the ethyl alcohol from the fermentation of the cassava starch. To testing was used ethyl alcohol PA 96 oGL, conductivity of 0.90 μS/cm at 25 oC, acidity of 60 mg/L and Barbet test of 43 minutes at 15 oC. The contaminated alcohol was composed of ethyl alcohol additive of higher alcohols, organic acids, ester, diol, aldehydes, ketone and ether. Contaminated alcohol was added 2% activated charcoal and after the adsorption isotherm in ionic exchange resins was tested. The adsorption with activated charcoal was performed in a Water Bath at 30 oC for one hour and a half and shaking. Already adsorption ionic exchange columns occurred at room temperature on columns of 93,4 cm in filling height and diameter of 2.29 cm, for flows of 180 mL/min and 90 mL/min. Samples were collected in the tests with charcoal and with each one of the resins and the following analyses were performed: conductivity, acidity and Barbet test. The medium values for conductivity, acidity and Barbet test after the adsorption in charcoal and cation and anion resins were respectively: conductivity was 240; 354 and 465 μS/cm to 25 oC; acidity of 1.081; 1.103 and 1.062 mg/L and the Barbet test was 21; 20 and 9 minutes to 15 oC. It was observed that the addition of 2% of activated charcoal and the permanence in the columns of adsorption was not sufficient to remove the organic substances contaminating of the ethyl alcohol.