Obtenção e caracterização de filmes finos de Bi3NbO7 pelo método dos precursores poliméricos

• Autor(a) principal: Gonçalves, Lucas Fabrício [UNESP]
• Data de Publicação: 2014
• Tipo de documento: Dissertação
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/111062
• topic: Filmes finos; Dieletricos; Viscosidade; Analise termica; Microscopia eletronica de varredura; Thin films

The central objective of this study was to obtain thin films of Bi3NbO7 with good dielectric properties at high frequency using organic citrate solution , metal salt and ethylene glycol as the precursor and the spin -coating deposition . The resin is obtained by the polymeric precursor method because the facilities of the process as inexpensive precursors , control of stoichiometry and low -temperature synthesis . After obtaining the precursor , polyester solution with controlled viscosity films were heat treated and characterized by X- ray diffraction , Scanning Electron Microscopy Field Emission Microscope Atomic Force , Transmission Electron Microscope , Thermogravimetric Analysis and Differential Thermal Analysis . The morphology of the films was correlated with viscosity, excess bismuth and annealing temperature used in calcination. To establish the best condition for heat treatment to obtain the crystalline phase , prepared in three different cycles films which were characterized by X-ray diffraction . The best course of treatment was the film treated at 700 ı C , 800 º C and 850 ı C for 2 hours or 3 cycle . Solutions with viscosity around 8.0 cps were used to deposit films on Si substrates coated with platinum and LaNiO3 on alumina by spin-coating method. A comparative study was conducted on heat treated in cycle 3 . Films are observed with low porosity and homogeneous with distinct morphologies . We observed the formation of Bi3NbO7 growth phase with the plane ( 111 ) for films deposited on Si substrates coated ... (Complete abstract click eletronic access below)