Sealing ability of retrograde obturation materials containing calcium hydroxide or MTA

Detalhes bibliográficos
Autor(a) principal: Tanomaru-Filho, Mário
Data de Publicação: 2011
Outros Autores: Faleiros, Frederico B C, Silva, Guilherme F, Bosso, Roberta, Guerreiro-Tanomaru, Juliane M
Tipo de documento: Artigo
Idioma: eng
Título da fonte: Repositório Institucional da UNESP
Texto Completo: http://www.actaodontologicalat.com/archivo/v24n1/fulltext/articulo18.pdf
http://hdl.handle.net/11449/72961
Resumo: Newly available materials for retrograde obturation should have their sealing properties evaluated. The goal of this study was to evaluate the sealing ability of Endo CPM sealer, an MTA-based endodontic cement. Single-rooted extracted human teeth were endodontically treated. After apical sectioning, retrograde cavities were prepared. Teeth were divided into five experimental groups (n=12), in which the following materials were used: Sealer 26 (S26), white Mineral Trioxide Aggregate (MTA), Endo CPM Sealer (CPM1), Endo CPM Sealer in thicker consistency (CPM 2), and zinc oxide and eugenol cement (ZOE), and two control groups (n=3). After retrograde obturation, the teeth were immersed in 0.2% rhodamine B dye for 48 hours in a vacuum chamber Marginal leakage data were subjected to ANOVA and Tukey tests at 5% significance level. S26 presented greater sealing ability (p<0.05) than ZOE, MTA, CPM1, and CPM2, all of which had similar results (p>0.05). We concluded that Sealer 26 has the greatest sealing ability. Endo CPM Sealer, with sealing ability similar to MTA, could be used as a retrograde obturation material.
id UNSP_dcde342ba17ab0a3ebe0ff6e1b4846cd
oai_identifier_str oai:repositorio.unesp.br:11449/72961
network_acronym_str UNSP
network_name_str Repositório Institucional da UNESP
repository_id_str 2946
spelling Sealing ability of retrograde obturation materials containing calcium hydroxide or MTAaluminum derivativebone cementcalcium derivativecalcium hydroxidemineral trioxide aggregateoxideroot canal filling materialsilicatedrug combinationendodonticshumanin vitro studymaterials testingAluminum CompoundsBone CementsCalcium CompoundsCalcium HydroxideDrug CombinationsHumansMaterials TestingOxidesRetrograde ObturationRoot Canal Filling MaterialsSilicatesNewly available materials for retrograde obturation should have their sealing properties evaluated. The goal of this study was to evaluate the sealing ability of Endo CPM sealer, an MTA-based endodontic cement. Single-rooted extracted human teeth were endodontically treated. After apical sectioning, retrograde cavities were prepared. Teeth were divided into five experimental groups (n=12), in which the following materials were used: Sealer 26 (S26), white Mineral Trioxide Aggregate (MTA), Endo CPM Sealer (CPM1), Endo CPM Sealer in thicker consistency (CPM 2), and zinc oxide and eugenol cement (ZOE), and two control groups (n=3). After retrograde obturation, the teeth were immersed in 0.2% rhodamine B dye for 48 hours in a vacuum chamber Marginal leakage data were subjected to ANOVA and Tukey tests at 5% significance level. S26 presented greater sealing ability (p<0.05) than ZOE, MTA, CPM1, and CPM2, all of which had similar results (p>0.05). We concluded that Sealer 26 has the greatest sealing ability. Endo CPM Sealer, with sealing ability similar to MTA, could be used as a retrograde obturation material.Universidade Estadual Paulista (Unesp)Tanomaru-Filho, MárioFaleiros, Frederico B CSilva, Guilherme FBosso, RobertaGuerreiro-Tanomaru, Juliane M2014-05-27T11:26:17Z2014-05-27T11:26:17Z2011-12-01info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/article110-114http://www.actaodontologicalat.com/archivo/v24n1/fulltext/articulo18.pdfActa odontológica latinoamericana : AOL, v. 24, n. 1, p. 110-114, 2011.0326-4815http://hdl.handle.net/11449/729612-s2.0-84856166011Scopusreponame:Repositório Institucional da UNESPinstname:Universidade Estadual Paulista (UNESP)instacron:UNESPengActa Odontológica Latinoamericana (AOL)0,264info:eu-repo/semantics/openAccess2024-09-27T18:03:43Zoai:repositorio.unesp.br:11449/72961Repositório InstitucionalPUBhttp://repositorio.unesp.br/oai/requestrepositoriounesp@unesp.bropendoar:29462024-09-27T18:03:43Repositório Institucional da UNESP - Universidade Estadual Paulista (UNESP)false
dc.title.none.fl_str_mv Sealing ability of retrograde obturation materials containing calcium hydroxide or MTA
title Sealing ability of retrograde obturation materials containing calcium hydroxide or MTA
spellingShingle Sealing ability of retrograde obturation materials containing calcium hydroxide or MTA
Tanomaru-Filho, Mário
aluminum derivative
bone cement
calcium derivative
calcium hydroxide
mineral trioxide aggregate
oxide
root canal filling material
silicate
drug combination
endodontics
human
in vitro study
materials testing
Aluminum Compounds
Bone Cements
Calcium Compounds
Calcium Hydroxide
Drug Combinations
Humans
Materials Testing
Oxides
Retrograde Obturation
Root Canal Filling Materials
Silicates
title_short Sealing ability of retrograde obturation materials containing calcium hydroxide or MTA
title_full Sealing ability of retrograde obturation materials containing calcium hydroxide or MTA
title_fullStr Sealing ability of retrograde obturation materials containing calcium hydroxide or MTA
title_full_unstemmed Sealing ability of retrograde obturation materials containing calcium hydroxide or MTA
title_sort Sealing ability of retrograde obturation materials containing calcium hydroxide or MTA
author Tanomaru-Filho, Mário
author_facet Tanomaru-Filho, Mário
Faleiros, Frederico B C
Silva, Guilherme F
Bosso, Roberta
Guerreiro-Tanomaru, Juliane M
author_role author
author2 Faleiros, Frederico B C
Silva, Guilherme F
Bosso, Roberta
Guerreiro-Tanomaru, Juliane M
author2_role author
author
author
author
dc.contributor.none.fl_str_mv Universidade Estadual Paulista (Unesp)
dc.contributor.author.fl_str_mv Tanomaru-Filho, Mário
Faleiros, Frederico B C
Silva, Guilherme F
Bosso, Roberta
Guerreiro-Tanomaru, Juliane M
dc.subject.por.fl_str_mv aluminum derivative
bone cement
calcium derivative
calcium hydroxide
mineral trioxide aggregate
oxide
root canal filling material
silicate
drug combination
endodontics
human
in vitro study
materials testing
Aluminum Compounds
Bone Cements
Calcium Compounds
Calcium Hydroxide
Drug Combinations
Humans
Materials Testing
Oxides
Retrograde Obturation
Root Canal Filling Materials
Silicates
topic aluminum derivative
bone cement
calcium derivative
calcium hydroxide
mineral trioxide aggregate
oxide
root canal filling material
silicate
drug combination
endodontics
human
in vitro study
materials testing
Aluminum Compounds
Bone Cements
Calcium Compounds
Calcium Hydroxide
Drug Combinations
Humans
Materials Testing
Oxides
Retrograde Obturation
Root Canal Filling Materials
Silicates
description Newly available materials for retrograde obturation should have their sealing properties evaluated. The goal of this study was to evaluate the sealing ability of Endo CPM sealer, an MTA-based endodontic cement. Single-rooted extracted human teeth were endodontically treated. After apical sectioning, retrograde cavities were prepared. Teeth were divided into five experimental groups (n=12), in which the following materials were used: Sealer 26 (S26), white Mineral Trioxide Aggregate (MTA), Endo CPM Sealer (CPM1), Endo CPM Sealer in thicker consistency (CPM 2), and zinc oxide and eugenol cement (ZOE), and two control groups (n=3). After retrograde obturation, the teeth were immersed in 0.2% rhodamine B dye for 48 hours in a vacuum chamber Marginal leakage data were subjected to ANOVA and Tukey tests at 5% significance level. S26 presented greater sealing ability (p<0.05) than ZOE, MTA, CPM1, and CPM2, all of which had similar results (p>0.05). We concluded that Sealer 26 has the greatest sealing ability. Endo CPM Sealer, with sealing ability similar to MTA, could be used as a retrograde obturation material.
publishDate 2011
dc.date.none.fl_str_mv 2011-12-01
2014-05-27T11:26:17Z
2014-05-27T11:26:17Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/article
format article
status_str publishedVersion
dc.identifier.uri.fl_str_mv http://www.actaodontologicalat.com/archivo/v24n1/fulltext/articulo18.pdf
Acta odontológica latinoamericana : AOL, v. 24, n. 1, p. 110-114, 2011.
0326-4815
http://hdl.handle.net/11449/72961
2-s2.0-84856166011
url http://www.actaodontologicalat.com/archivo/v24n1/fulltext/articulo18.pdf
http://hdl.handle.net/11449/72961
identifier_str_mv Acta odontológica latinoamericana : AOL, v. 24, n. 1, p. 110-114, 2011.
0326-4815
2-s2.0-84856166011
dc.language.iso.fl_str_mv eng
language eng
dc.relation.none.fl_str_mv Acta Odontológica Latinoamericana (AOL)
0,264
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 110-114
dc.source.none.fl_str_mv Scopus
reponame:Repositório Institucional da UNESP
instname:Universidade Estadual Paulista (UNESP)
instacron:UNESP
instname_str Universidade Estadual Paulista (UNESP)
instacron_str UNESP
institution UNESP
reponame_str Repositório Institucional da UNESP
collection Repositório Institucional da UNESP
repository.name.fl_str_mv Repositório Institucional da UNESP - Universidade Estadual Paulista (UNESP)
repository.mail.fl_str_mv repositoriounesp@unesp.br
_version_ 1813546416926097408