Resistência à fratura por lascamento de cerâmicas monolíticas
Autor(a) principal: | |
---|---|
Data de Publicação: | 2017 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) |
Texto Completo: | http://tede.upf.br/jspui/handle/tede/1471 |
Resumo: | This study estimated the chipping resistance (ReA) of two ceramics (GC-IPS e.max CAD and YZ- Zenostar Zr Translucent) using the edge chipping test, evaluating (1) if the edge distance (d) influences on the load to produce the chipping (F) and on ReA and (2) if the adhesion to a dentine analogue substrate (G10) influences on ReA. Bar-shaped specimens of 2 mm and 5mm in thickness were fabricated from GC and YZ. Specimens were adhesively cemented (C) to G10 or just fixed to the universal testing machine (NC). Chippings (n=25) were produced from preset d (0.1 mm – 0.6 mm) in all specimens (YZ-C; YZ-NC; GC-C and GC-NC) using a Vickers indenter connected to a universal testing machine with crosshead speed of 1 mm/min. F and d were recorded and ReA (F/d) was calculated. The data were statistically analyzed using Weibull distribution, Pearson correlation, Student t, ANOVA and Turkey (α =0.05). A strong positive correlation was found between F and d for all groups (R≥0.98). The ReAvalues showed a tendency to increased as the d increases, especially for NC ceramics. Such trend was confirmed for the C ceramics. ReAdepends on the material/condition evaluated. |
id |
UPF-1_c125cde27fc8070cee449e40565fdda1 |
---|---|
oai_identifier_str |
oai:tede.upf.br:tede/1471 |
network_acronym_str |
UPF-1 |
network_name_str |
Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) |
repository_id_str |
|
spelling |
Bona, Álvaro Della42784263053http://lattes.cnpq.br/706457979223775002537918045http://lattes.cnpq.br/6282840617115803Taufer, Cristiano2018-08-23T18:06:19Z2017-03-31TAUFER, Cristiano. Resistência à fratura por lascamento de cerâmicas monolíticas. 2017. 149 f. Dissertação (Mestrado em Odontologia) - Universidade de Passo Fundo, Passo Fundo, RS, 2017.http://tede.upf.br/jspui/handle/tede/1471This study estimated the chipping resistance (ReA) of two ceramics (GC-IPS e.max CAD and YZ- Zenostar Zr Translucent) using the edge chipping test, evaluating (1) if the edge distance (d) influences on the load to produce the chipping (F) and on ReA and (2) if the adhesion to a dentine analogue substrate (G10) influences on ReA. Bar-shaped specimens of 2 mm and 5mm in thickness were fabricated from GC and YZ. Specimens were adhesively cemented (C) to G10 or just fixed to the universal testing machine (NC). Chippings (n=25) were produced from preset d (0.1 mm – 0.6 mm) in all specimens (YZ-C; YZ-NC; GC-C and GC-NC) using a Vickers indenter connected to a universal testing machine with crosshead speed of 1 mm/min. F and d were recorded and ReA (F/d) was calculated. The data were statistically analyzed using Weibull distribution, Pearson correlation, Student t, ANOVA and Turkey (α =0.05). A strong positive correlation was found between F and d for all groups (R≥0.98). The ReAvalues showed a tendency to increased as the d increases, especially for NC ceramics. Such trend was confirmed for the C ceramics. ReAdepends on the material/condition evaluated.Este estudo estimou a resistência à fratura por lascamento (ReA) de duas cerâmicas (GC- IPS e.max CAD e YZ- Zenostar Zr Translucent) indicadas para restaurações monolíticas utilizando o teste edge chipping, avaliando (1) se a distância da borda (d) influencia na força para produzir o lascamento (F) e na ReA e (2) se a cimentação em material análogo da dentina (G10) influencia a ReA. Foram fabricados corpos de prova (CP) em forma de barras com 2 e 5 mm de espessura das cerâmicas GC e YZ. Metade dos CP foram cimentados (C) em G10 e os restantes foram apenas fixado na máquina de ensaio universal (NC). Lascamentos (n=25) em determinadas d (0,1 - 0,6 mm) foram produzidos nos CP (YZ-C; YZ-NC; GC-C e GC-NC) usando penetrador Vickers conectado a máquina de ensaio com velocidade de 1 mm/min. F e d foram registradas e ReA (F/d) foi calculada. Os resultados foram avaliados estatisticamente usando distribuição de Weibull, correlação de Pearson, Student t, ANOVA e Tukey (¿=0,05). Forte correlação positiva foi encontrada entre F e d para todos os grupos (R¿0,98). Os valores de ReA mostraram uma tendência de aumento conforme o aumento de d, especialmente para cerâmicas NC. Entretanto, essa tendência não se confirma para cerâmicas C. A ReA depende do material/condição avaliado.Submitted by Mariana Freitas (marianafreitas@upf.br) on 2018-08-23T18:06:19Z No. of bitstreams: 1 2017CristianoTaufer.pdf: 1034579 bytes, checksum: 0cb56244fe8106a9bb77dc1dc046a361 (MD5)Made available in DSpace on 2018-08-23T18:06:19Z (GMT). No. of bitstreams: 1 2017CristianoTaufer.pdf: 1034579 bytes, checksum: 0cb56244fe8106a9bb77dc1dc046a361 (MD5) Previous issue date: 2017-03-31Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESapplication/pdfporUniversidade de Passo FundoPrograma de Pós-Graduação em OdontologiaUPFBrasilFaculdade de Odontologia – FOCerâmica odontológicaDentesFerimentos e lesõesRestauraçãoCIENCIAS DA SAUDE::ODONTOLOGIAResistência à fratura por lascamento de cerâmicas monolíticasResistance to fracture by chipping of monolithic ceramicsinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-80965548187336651645005006006008090167142064557236-20704984698792443492075167498588264571info:eu-repo/semantics/openAccessreponame:Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF)instname:Universidade de Passo Fundo (UPF)instacron:UPFLICENSElicense.txtlicense.txttext/plain; charset=utf-81940http://tede.upf.br:8080/jspui/bitstream/tede/1471/1/license.txte0faded76e3df80302a4a0fb3f2bb5f3MD51ORIGINAL2017CristianoTaufer.pdf2017CristianoTaufer.pdfapplication/pdf1034579http://tede.upf.br:8080/jspui/bitstream/tede/1471/2/2017CristianoTaufer.pdf0cb56244fe8106a9bb77dc1dc046a361MD52tede/14712018-08-23 15:06:19.695oai:tede.upf.br: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Biblioteca Digital de Teses e DissertaçõesPUBhttp://tede.upf.br/oai/requestbiblio@upf.br || bio@upf.br || cas@upf.br || car@upf.br || lve@upf.br || sar@upf.br || sol@upf.br || upfmundi@upf.br || jucelei@upf.bropendoar:2018-08-23T18:06:19Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) - Universidade de Passo Fundo (UPF)false |
dc.title.por.fl_str_mv |
Resistência à fratura por lascamento de cerâmicas monolíticas |
dc.title.alternative.eng.fl_str_mv |
Resistance to fracture by chipping of monolithic ceramics |
title |
Resistência à fratura por lascamento de cerâmicas monolíticas |
spellingShingle |
Resistência à fratura por lascamento de cerâmicas monolíticas Taufer, Cristiano Cerâmica odontológica Dentes Ferimentos e lesões Restauração CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Resistência à fratura por lascamento de cerâmicas monolíticas |
title_full |
Resistência à fratura por lascamento de cerâmicas monolíticas |
title_fullStr |
Resistência à fratura por lascamento de cerâmicas monolíticas |
title_full_unstemmed |
Resistência à fratura por lascamento de cerâmicas monolíticas |
title_sort |
Resistência à fratura por lascamento de cerâmicas monolíticas |
author |
Taufer, Cristiano |
author_facet |
Taufer, Cristiano |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Bona, Álvaro Della |
dc.contributor.advisor1ID.fl_str_mv |
42784263053 |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/7064579792237750 |
dc.contributor.authorID.fl_str_mv |
02537918045 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/6282840617115803 |
dc.contributor.author.fl_str_mv |
Taufer, Cristiano |
contributor_str_mv |
Bona, Álvaro Della |
dc.subject.por.fl_str_mv |
Cerâmica odontológica Dentes Ferimentos e lesões Restauração |
topic |
Cerâmica odontológica Dentes Ferimentos e lesões Restauração CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.cnpq.fl_str_mv |
CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
This study estimated the chipping resistance (ReA) of two ceramics (GC-IPS e.max CAD and YZ- Zenostar Zr Translucent) using the edge chipping test, evaluating (1) if the edge distance (d) influences on the load to produce the chipping (F) and on ReA and (2) if the adhesion to a dentine analogue substrate (G10) influences on ReA. Bar-shaped specimens of 2 mm and 5mm in thickness were fabricated from GC and YZ. Specimens were adhesively cemented (C) to G10 or just fixed to the universal testing machine (NC). Chippings (n=25) were produced from preset d (0.1 mm – 0.6 mm) in all specimens (YZ-C; YZ-NC; GC-C and GC-NC) using a Vickers indenter connected to a universal testing machine with crosshead speed of 1 mm/min. F and d were recorded and ReA (F/d) was calculated. The data were statistically analyzed using Weibull distribution, Pearson correlation, Student t, ANOVA and Turkey (α =0.05). A strong positive correlation was found between F and d for all groups (R≥0.98). The ReAvalues showed a tendency to increased as the d increases, especially for NC ceramics. Such trend was confirmed for the C ceramics. ReAdepends on the material/condition evaluated. |
publishDate |
2017 |
dc.date.issued.fl_str_mv |
2017-03-31 |
dc.date.accessioned.fl_str_mv |
2018-08-23T18:06:19Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
TAUFER, Cristiano. Resistência à fratura por lascamento de cerâmicas monolíticas. 2017. 149 f. Dissertação (Mestrado em Odontologia) - Universidade de Passo Fundo, Passo Fundo, RS, 2017. |
dc.identifier.uri.fl_str_mv |
http://tede.upf.br/jspui/handle/tede/1471 |
identifier_str_mv |
TAUFER, Cristiano. Resistência à fratura por lascamento de cerâmicas monolíticas. 2017. 149 f. Dissertação (Mestrado em Odontologia) - Universidade de Passo Fundo, Passo Fundo, RS, 2017. |
url |
http://tede.upf.br/jspui/handle/tede/1471 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-8096554818733665164 |
dc.relation.confidence.fl_str_mv |
500 500 600 600 |
dc.relation.department.fl_str_mv |
8090167142064557236 |
dc.relation.cnpq.fl_str_mv |
-2070498469879244349 |
dc.relation.sponsorship.fl_str_mv |
2075167498588264571 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade de Passo Fundo |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Odontologia |
dc.publisher.initials.fl_str_mv |
UPF |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Faculdade de Odontologia – FO |
publisher.none.fl_str_mv |
Universidade de Passo Fundo |
dc.source.none.fl_str_mv |
reponame:Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) instname:Universidade de Passo Fundo (UPF) instacron:UPF |
instname_str |
Universidade de Passo Fundo (UPF) |
instacron_str |
UPF |
institution |
UPF |
reponame_str |
Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) |
collection |
Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) |
bitstream.url.fl_str_mv |
http://tede.upf.br:8080/jspui/bitstream/tede/1471/1/license.txt http://tede.upf.br:8080/jspui/bitstream/tede/1471/2/2017CristianoTaufer.pdf |
bitstream.checksum.fl_str_mv |
e0faded76e3df80302a4a0fb3f2bb5f3 0cb56244fe8106a9bb77dc1dc046a361 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) - Universidade de Passo Fundo (UPF) |
repository.mail.fl_str_mv |
biblio@upf.br || bio@upf.br || cas@upf.br || car@upf.br || lve@upf.br || sar@upf.br || sol@upf.br || upfmundi@upf.br || jucelei@upf.br |
_version_ |
1809092291404496896 |