Effect of storage period on the accuracy of elastomeric impressions

• Autor(a) principal: Franco, Eduardo Batista
• Data de Publicação: 2007
• Outros Autores: Cunha, Leonardo Fernandes da, Benetti, Ana Raquel
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Journal of applied oral science (Online)
• Texto Completo: https://www.revistas.usp.br/jaos/article/view/3461
• topic: Dental impression materials; Vinyl polysiloxane; Polyether

AIMS: To investigate the effect of the storage period on the accuracy of recently developed elastomeric materials. METHODS: Simultaneous impressions of a steel die were taken using a polyether (I: Impregum Soft Heavy and Light body, 3M ESPE) and vinyl polysiloxane (P: Perfectim Blue Velvet and Flexi-Velvet, J.Morita). The trays were loaded with the heavy-bodied impression materials while the light-bodied impression materials were simultaneously spread on the steel die. The impressions were poured after 2 hours, 24 hours, and 7 days. Impressions were stored at approximately 55% relative humidity and room temperature. Ten replicas were produced for each experimental condition (n=60). Accuracy of the stone dies was assessed with a depth-measuring microscope. The difference in height between the surface of the stone die and a standard metallic ring was recorded in micrometers at four demarcated points, by two independent examiners. Data were submitted to two-way ANOVA and Tukey test (a = 0.05). RESULTS: Significant differences were found among the groups. Smaller discrepancies were observed when pouring was performed up to 24 hours (I-2h= 65.0 ± 15.68 µm; I-24h= 81.6 ± 11.13 µm) for the polyether, and up to 7 days for the vinyl polysiloxane (P-2h= 79.1 ± 13.82 µm; P-24h= 96.8 ± 6.02 µm; P-7d= 81.4 ± 4.3 µm). Significant dimensional discrepancies, however, were observed when polyether was stored for 7 days (I-7d= 295.3 ± 17.4 µm). CONCLUSION: Storage may significantly affect the dimensional accuracy of impressions and, thus, a maximum period and storage condition should be specified for the recently developed materials.