Flexural strength of acrylic resins polymerized by different cycles
Autor(a) principal: | |
---|---|
Data de Publicação: | 2007 |
Outros Autores: | , , , |
Tipo de documento: | Artigo |
Idioma: | eng |
Título da fonte: | Journal of applied oral science (Online) |
Texto Completo: | http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1678-77572007000500010 |
Resumo: | Despite the large number of studies addressing the effect of microwave polymerization on the properties of acrylic resin, this method has received limited clinical acceptance. This study evaluated the influence of microwave polymerization on the flexural strength of a denture base resin. A conventional heat-polymerized (Clássico), a microwave-polymerized (Onda-Cryl) and a autopolymerizing acrylic (Jet) resins were used. Five groups were established, according to polymerization cycles: A, B and C (Onda-Cryl, short cycle - 500W/3 min, long - 90W/13 min + 500W/90 sec, and manufacturing microwave cycle - 320W/3 min + 0W/3 min + 720W/3 min); T (Clássico, water bath cycle - 74ºC/9h) and Q (Jet, press chamber cycle - 50ºC/15 min at 2 bar). Ten specimens (65 x 10 x 3.3mm) were prepared for each cycle. The flexural strength of the five groups was measured using a three-point bending test at a cross-head speed of 5 mm/min. Flexural strength values were analyzed by one-way ANOVA and the Tukey's test was performed to identify the groups that were significantly different at 5% level. The microwave-polymerized groups showed the highest means (p<0.05) for flexural strength (MPa) (A = 106.97 ± 5.31; B = 107.57 ± 3.99; C = 109.63 ± 5.19), and there were no significant differences among them. The heat-polymerized group (T) showed the lowest flexural strength means (84.40 ± 1.68), and differ significantly from all groups. The specimens of a microwavable denture base resin could be polymerized by different microwave cycles without risk of decreasing the flexural strength. |
id |
USP-17_b7e9a5784220fc582ef30c73f3c8c2d3 |
---|---|
oai_identifier_str |
oai:scielo:S1678-77572007000500010 |
network_acronym_str |
USP-17 |
network_name_str |
Journal of applied oral science (Online) |
repository_id_str |
|
spelling |
Flexural strength of acrylic resins polymerized by different cyclesDenturesAcrylic resinsMicrowavesPhysical propertiesStrengthDespite the large number of studies addressing the effect of microwave polymerization on the properties of acrylic resin, this method has received limited clinical acceptance. This study evaluated the influence of microwave polymerization on the flexural strength of a denture base resin. A conventional heat-polymerized (Clássico), a microwave-polymerized (Onda-Cryl) and a autopolymerizing acrylic (Jet) resins were used. Five groups were established, according to polymerization cycles: A, B and C (Onda-Cryl, short cycle - 500W/3 min, long - 90W/13 min + 500W/90 sec, and manufacturing microwave cycle - 320W/3 min + 0W/3 min + 720W/3 min); T (Clássico, water bath cycle - 74ºC/9h) and Q (Jet, press chamber cycle - 50ºC/15 min at 2 bar). Ten specimens (65 x 10 x 3.3mm) were prepared for each cycle. The flexural strength of the five groups was measured using a three-point bending test at a cross-head speed of 5 mm/min. Flexural strength values were analyzed by one-way ANOVA and the Tukey's test was performed to identify the groups that were significantly different at 5% level. The microwave-polymerized groups showed the highest means (p<0.05) for flexural strength (MPa) (A = 106.97 ± 5.31; B = 107.57 ± 3.99; C = 109.63 ± 5.19), and there were no significant differences among them. The heat-polymerized group (T) showed the lowest flexural strength means (84.40 ± 1.68), and differ significantly from all groups. The specimens of a microwavable denture base resin could be polymerized by different microwave cycles without risk of decreasing the flexural strength.Faculdade De Odontologia De Bauru - USP2007-10-01info:eu-repo/semantics/articleinfo:eu-repo/semantics/publishedVersiontext/htmlhttp://old.scielo.br/scielo.php?script=sci_arttext&pid=S1678-77572007000500010Journal of Applied Oral Science v.15 n.5 2007reponame:Journal of applied oral science (Online)instname:Universidade de São Paulo (USP)instacron:USP10.1590/S1678-77572007000500010info:eu-repo/semantics/openAccessBarbosa,Débora BarrosSouza,Raphael Freitas dePero,Ana CarolinaMarra,JuliêCompagnoni,Marco Antonioeng2007-11-06T00:00:00Zoai:scielo:S1678-77572007000500010Revistahttp://www.scielo.br/jaosPUBhttps://old.scielo.br/oai/scielo-oai.php||jaos@usp.br1678-77651678-7757opendoar:2007-11-06T00:00Journal of applied oral science (Online) - Universidade de São Paulo (USP)false |
dc.title.none.fl_str_mv |
Flexural strength of acrylic resins polymerized by different cycles |
title |
Flexural strength of acrylic resins polymerized by different cycles |
spellingShingle |
Flexural strength of acrylic resins polymerized by different cycles Barbosa,Débora Barros Dentures Acrylic resins Microwaves Physical properties Strength |
title_short |
Flexural strength of acrylic resins polymerized by different cycles |
title_full |
Flexural strength of acrylic resins polymerized by different cycles |
title_fullStr |
Flexural strength of acrylic resins polymerized by different cycles |
title_full_unstemmed |
Flexural strength of acrylic resins polymerized by different cycles |
title_sort |
Flexural strength of acrylic resins polymerized by different cycles |
author |
Barbosa,Débora Barros |
author_facet |
Barbosa,Débora Barros Souza,Raphael Freitas de Pero,Ana Carolina Marra,Juliê Compagnoni,Marco Antonio |
author_role |
author |
author2 |
Souza,Raphael Freitas de Pero,Ana Carolina Marra,Juliê Compagnoni,Marco Antonio |
author2_role |
author author author author |
dc.contributor.author.fl_str_mv |
Barbosa,Débora Barros Souza,Raphael Freitas de Pero,Ana Carolina Marra,Juliê Compagnoni,Marco Antonio |
dc.subject.por.fl_str_mv |
Dentures Acrylic resins Microwaves Physical properties Strength |
topic |
Dentures Acrylic resins Microwaves Physical properties Strength |
description |
Despite the large number of studies addressing the effect of microwave polymerization on the properties of acrylic resin, this method has received limited clinical acceptance. This study evaluated the influence of microwave polymerization on the flexural strength of a denture base resin. A conventional heat-polymerized (Clássico), a microwave-polymerized (Onda-Cryl) and a autopolymerizing acrylic (Jet) resins were used. Five groups were established, according to polymerization cycles: A, B and C (Onda-Cryl, short cycle - 500W/3 min, long - 90W/13 min + 500W/90 sec, and manufacturing microwave cycle - 320W/3 min + 0W/3 min + 720W/3 min); T (Clássico, water bath cycle - 74ºC/9h) and Q (Jet, press chamber cycle - 50ºC/15 min at 2 bar). Ten specimens (65 x 10 x 3.3mm) were prepared for each cycle. The flexural strength of the five groups was measured using a three-point bending test at a cross-head speed of 5 mm/min. Flexural strength values were analyzed by one-way ANOVA and the Tukey's test was performed to identify the groups that were significantly different at 5% level. The microwave-polymerized groups showed the highest means (p<0.05) for flexural strength (MPa) (A = 106.97 ± 5.31; B = 107.57 ± 3.99; C = 109.63 ± 5.19), and there were no significant differences among them. The heat-polymerized group (T) showed the lowest flexural strength means (84.40 ± 1.68), and differ significantly from all groups. The specimens of a microwavable denture base resin could be polymerized by different microwave cycles without risk of decreasing the flexural strength. |
publishDate |
2007 |
dc.date.none.fl_str_mv |
2007-10-01 |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/article |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
format |
article |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1678-77572007000500010 |
url |
http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1678-77572007000500010 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
10.1590/S1678-77572007000500010 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
text/html |
dc.publisher.none.fl_str_mv |
Faculdade De Odontologia De Bauru - USP |
publisher.none.fl_str_mv |
Faculdade De Odontologia De Bauru - USP |
dc.source.none.fl_str_mv |
Journal of Applied Oral Science v.15 n.5 2007 reponame:Journal of applied oral science (Online) instname:Universidade de São Paulo (USP) instacron:USP |
instname_str |
Universidade de São Paulo (USP) |
instacron_str |
USP |
institution |
USP |
reponame_str |
Journal of applied oral science (Online) |
collection |
Journal of applied oral science (Online) |
repository.name.fl_str_mv |
Journal of applied oral science (Online) - Universidade de São Paulo (USP) |
repository.mail.fl_str_mv |
||jaos@usp.br |
_version_ |
1748936434770771968 |