In vitro evaluation of marginal microleakage of class II bonded amalgam restorations using a dentin adhesive and a glass ionomer cement

• Autor(a) principal: PEREIRA JÚNIOR,Edmêr Silvestre
• Data de Publicação: 1999
• Outros Autores: BIJELLA,Maria Francisca Thereza Borro, SILVA,Salete Moura Bonifácio da, VONO,Bernardo Gonzales
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Revista de Odontologia da Universidade de São Paulo
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S0103-06631999000200002
• topic: Dental amalgam; Dental leakage

The purpose of this study was to evaluate in vitro the effectiveness of the dentin bonding system All Bond 2 associated with Resinomer (Bisco), and of Vitrebond (3M) glass ionomer cement fresh-mixed, both used in the bonded amalgam technique, to prevent short-term microleakage in class II cavities restored with Dispersalloy (Dentsply), an admixed alloy. The control group utilized the Copalite (Cooley & Cooley) varnish. Forty five sound human extracted premolars were used. Class II cavity preparations were made on the mesial and distal surfaces of non-carious teeth, with the gingival margins wall established 1mm under the cementum enamel junction. The specimens were divided randomly into three groups with thirty cavities in each group. The teeth were stored in distilled water for 24 hours and were thermocyled through 500 cycles in distilled water between 5°C and 55°C with a dwell time of 15 seconds. The apices and roots of the teeth were sealed. They were placed in a 37°C bath of 0.5% basic fuchsin dye for 24 hours. The teeth were washed in tap water for 24 hours and cut. The microleakage scores per restoration were averaged and three values of various test groups were subjected to the Kruskal-Wallis and Dunn test at a significance level of p < 0.05. The All Bond 2/Resinomer showed significantly less microleakage at gingival margins than the Vitrebond and Copalite lined to amalgam restorations. The Vitrebond fresh mixed, lined to amalgam restorations, showed significantly less microleakage than the Copalite lined to amalgam restorations.