\"Estudo das propriedades das blendas de amido termoplástico e látex natural\"
Autor(a) principal: | |
---|---|
Data de Publicação: | 2006 |
Tipo de documento: | Tese |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações da USP |
Texto Completo: | http://www.teses.usp.br/teses/disponiveis/75/75131/tde-26042007-090356/ |
Resumo: | Este trabalho tem como objetivos a preparação e a caracterização de blendas de amido termoplástico e borracha natural, obtidos a partir dos amidos de mandioca e milho e do látex de borracha natural utilizado diretamente como extraído da seringueira, sem nenhum tipo de tratamento prévio. Os amidos termoplásticos (TPS) foram processados em misturador intensivo em duas temperaturas diferentes (120oC e 150oC), utilizando como plasticizantes a glicerina, o etilenoglicol e o propilenoglicol na proporção de 30 % em massa na matriz, e teores de látex de borracha natural (NRL) variando na proporção de 2,5 a 10 % em massa na blenda. As propriedades das blendas foram avaliadas por difração de Raios-X, por termogravimetria (TG), ensaios mecânicos de resistência à tração, por ensaios de absorção de água e por microscopia eletrônica de varredura (SEM). O cisalhamento desenvolvido durante o processamento em misturador intensivo levou à perda da estrutura cristalina e à desestruturação dos grânulos de amido. A adição de látex diminuiu os valores de índice de cristalinidade dos TPS, não alterando, entretanto, o comportamento cristalográfico com relação ao tipo de padrão de cristalinidade apresentado pelos TPS. Com relação à estabilidade térmica, os TPS mostraram-se dependentes da fonte de amido utilizado, do tipo de plasticizante, da temperatura de processamento e do teor de látex presente. Quanto à resistência mecânica, o TPS de milho se mostrou mais resistente que o de mandioca, principalmente quando plasticizado com glicerina, tendo a temperatura de processamento pouca influência sobre os resultados. Com relação aos teores de látex adicionados, não foi observada nenhuma melhora significativa sobre a resistência mecânica dos TPS, exceto um pequeno aumento nos valores de alongamento à ruptura. A adição de látex proporcionou uma diminuição linear na absorção máxima de água no equilíbrio, assim como uma redução nos valores de coeficiente de difusão de água apresentado pelos TPS. Uma vez que o processo de mistura desempenha uma função importante na morfologia destas blendas, na maioria dos TPS plasticizados com glicerina, entretanto, para os TPS plasticizados com etilenoglicol e com propilenoglicol não houve uma boa dispersão dos componentes das misturas. Os TPS de milho plasticizados com glicerina à 150oC foram os que apresentaram uma melhor dispersão das partículas de látex quando comparado com os demais. A qualidade destas dispersões foi uma conseqüência da utilização do látex ao invés da borracha sólida, uma vez que o primeiro apresenta a presença de proteínas e lipídeos na superfície das partículas de borracha presentes no látex, atuando como um compatibilizante entre o amido, uma matriz polar, e a borracha, um material não-polar. |
id |
USP_e27a6cb4221c4f458ee23aefba2bddab |
---|---|
oai_identifier_str |
oai:teses.usp.br:tde-26042007-090356 |
network_acronym_str |
USP |
network_name_str |
Biblioteca Digital de Teses e Dissertações da USP |
repository_id_str |
2721 |
spelling |
\"Estudo das propriedades das blendas de amido termoplástico e látex natural\"\"Study of properties of thermoplastic starch - natural rubber blends\"amido termoplásticoblendas poliméricasborracha naturalnatural rubberpolymeric blendsthermoplastic starchEste trabalho tem como objetivos a preparação e a caracterização de blendas de amido termoplástico e borracha natural, obtidos a partir dos amidos de mandioca e milho e do látex de borracha natural utilizado diretamente como extraído da seringueira, sem nenhum tipo de tratamento prévio. Os amidos termoplásticos (TPS) foram processados em misturador intensivo em duas temperaturas diferentes (120oC e 150oC), utilizando como plasticizantes a glicerina, o etilenoglicol e o propilenoglicol na proporção de 30 % em massa na matriz, e teores de látex de borracha natural (NRL) variando na proporção de 2,5 a 10 % em massa na blenda. As propriedades das blendas foram avaliadas por difração de Raios-X, por termogravimetria (TG), ensaios mecânicos de resistência à tração, por ensaios de absorção de água e por microscopia eletrônica de varredura (SEM). O cisalhamento desenvolvido durante o processamento em misturador intensivo levou à perda da estrutura cristalina e à desestruturação dos grânulos de amido. A adição de látex diminuiu os valores de índice de cristalinidade dos TPS, não alterando, entretanto, o comportamento cristalográfico com relação ao tipo de padrão de cristalinidade apresentado pelos TPS. Com relação à estabilidade térmica, os TPS mostraram-se dependentes da fonte de amido utilizado, do tipo de plasticizante, da temperatura de processamento e do teor de látex presente. Quanto à resistência mecânica, o TPS de milho se mostrou mais resistente que o de mandioca, principalmente quando plasticizado com glicerina, tendo a temperatura de processamento pouca influência sobre os resultados. Com relação aos teores de látex adicionados, não foi observada nenhuma melhora significativa sobre a resistência mecânica dos TPS, exceto um pequeno aumento nos valores de alongamento à ruptura. A adição de látex proporcionou uma diminuição linear na absorção máxima de água no equilíbrio, assim como uma redução nos valores de coeficiente de difusão de água apresentado pelos TPS. Uma vez que o processo de mistura desempenha uma função importante na morfologia destas blendas, na maioria dos TPS plasticizados com glicerina, entretanto, para os TPS plasticizados com etilenoglicol e com propilenoglicol não houve uma boa dispersão dos componentes das misturas. Os TPS de milho plasticizados com glicerina à 150oC foram os que apresentaram uma melhor dispersão das partículas de látex quando comparado com os demais. A qualidade destas dispersões foi uma conseqüência da utilização do látex ao invés da borracha sólida, uma vez que o primeiro apresenta a presença de proteínas e lipídeos na superfície das partículas de borracha presentes no látex, atuando como um compatibilizante entre o amido, uma matriz polar, e a borracha, um material não-polar.The aim of the study reported here was to prepare and characterize blends of thermoplastic starch and natural rubber, based on manioc starch (tapioca), corn starch and natural rubber latex used directly as extracted from Hevea brasiliensis (Brazilian rubber tree), without prior treatment. The thermoplastic starch (TPS) matrices were prepared in a high-intensity mixer at two temperatures (120°C and 150°C), with 30% (w/w) glycerol, ethylene glycol or propylene glycol as plasticizer, and from 2.5% to 10% (w/w) natural rubber latex (NRL) was added to form the blends. The properties of the composite blends were assessed by XRD, TGA, tensile strength tests, water absorption tests and SEM. The shearing forces developed during mixing resulted in a loss of crystallinity and breakdown of the starch granule structure. The addition of NRL reduced the crystallinity index of the TPS, but did not change the type of crystal structure exhibited by this phase. The thermal stability of the TPS matrix was found to depend on the origin of the starch, the type of plasticizer, the processing temperature and the latex content. In the mechanical strength tests, the cornstarch TPS proved stronger than the manioc product, especially when plasticized with glycerol, while the mixing temperature had little influence. With the addition of NRL, no significant was observed in the mechanical properties, except for a small increase in the elongation of the material at breakpoint. As latex was added there was a linear decrease in the maximum absorption of water at equilibrium, as well as a reduction in the diffusion coefficient of water in the matrix. While the mixing process played an important part in producing an adequate blend morphology in most of the mixtures containing glycerol, the components of blends in which the TPS was plasticized with ethylene or propylene glycol were not well-dispersed. The TPS that afforded the best dispersion of latex particles was composed of cornstarch and glycerol and plasticized at 150°C. The highquality dispersion achieved was a consequence of using raw latex instead of solid rubber, since in the latex the rubber particles are coated with surface proteins and lipids that help to compatibilize the starch, a polar matrix, with the nonpolar rubber.Biblioteca Digitais de Teses e Dissertações da USPCurvelo, Antonio Aprigio da SilvaJacob, Ricardo Francischetti2006-11-24info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisapplication/pdfhttp://www.teses.usp.br/teses/disponiveis/75/75131/tde-26042007-090356/reponame:Biblioteca Digital de Teses e Dissertações da USPinstname:Universidade de São Paulo (USP)instacron:USPLiberar o conteúdo para acesso público.info:eu-repo/semantics/openAccesspor2016-07-28T16:09:51Zoai:teses.usp.br:tde-26042007-090356Biblioteca Digital de Teses e Dissertaçõeshttp://www.teses.usp.br/PUBhttp://www.teses.usp.br/cgi-bin/mtd2br.plvirginia@if.usp.br|| atendimento@aguia.usp.br||virginia@if.usp.bropendoar:27212016-07-28T16:09:51Biblioteca Digital de Teses e Dissertações da USP - Universidade de São Paulo (USP)false |
dc.title.none.fl_str_mv |
\"Estudo das propriedades das blendas de amido termoplástico e látex natural\" \"Study of properties of thermoplastic starch - natural rubber blends\" |
title |
\"Estudo das propriedades das blendas de amido termoplástico e látex natural\" |
spellingShingle |
\"Estudo das propriedades das blendas de amido termoplástico e látex natural\" Jacob, Ricardo Francischetti amido termoplástico blendas poliméricas borracha natural natural rubber polymeric blends thermoplastic starch |
title_short |
\"Estudo das propriedades das blendas de amido termoplástico e látex natural\" |
title_full |
\"Estudo das propriedades das blendas de amido termoplástico e látex natural\" |
title_fullStr |
\"Estudo das propriedades das blendas de amido termoplástico e látex natural\" |
title_full_unstemmed |
\"Estudo das propriedades das blendas de amido termoplástico e látex natural\" |
title_sort |
\"Estudo das propriedades das blendas de amido termoplástico e látex natural\" |
author |
Jacob, Ricardo Francischetti |
author_facet |
Jacob, Ricardo Francischetti |
author_role |
author |
dc.contributor.none.fl_str_mv |
Curvelo, Antonio Aprigio da Silva |
dc.contributor.author.fl_str_mv |
Jacob, Ricardo Francischetti |
dc.subject.por.fl_str_mv |
amido termoplástico blendas poliméricas borracha natural natural rubber polymeric blends thermoplastic starch |
topic |
amido termoplástico blendas poliméricas borracha natural natural rubber polymeric blends thermoplastic starch |
description |
Este trabalho tem como objetivos a preparação e a caracterização de blendas de amido termoplástico e borracha natural, obtidos a partir dos amidos de mandioca e milho e do látex de borracha natural utilizado diretamente como extraído da seringueira, sem nenhum tipo de tratamento prévio. Os amidos termoplásticos (TPS) foram processados em misturador intensivo em duas temperaturas diferentes (120oC e 150oC), utilizando como plasticizantes a glicerina, o etilenoglicol e o propilenoglicol na proporção de 30 % em massa na matriz, e teores de látex de borracha natural (NRL) variando na proporção de 2,5 a 10 % em massa na blenda. As propriedades das blendas foram avaliadas por difração de Raios-X, por termogravimetria (TG), ensaios mecânicos de resistência à tração, por ensaios de absorção de água e por microscopia eletrônica de varredura (SEM). O cisalhamento desenvolvido durante o processamento em misturador intensivo levou à perda da estrutura cristalina e à desestruturação dos grânulos de amido. A adição de látex diminuiu os valores de índice de cristalinidade dos TPS, não alterando, entretanto, o comportamento cristalográfico com relação ao tipo de padrão de cristalinidade apresentado pelos TPS. Com relação à estabilidade térmica, os TPS mostraram-se dependentes da fonte de amido utilizado, do tipo de plasticizante, da temperatura de processamento e do teor de látex presente. Quanto à resistência mecânica, o TPS de milho se mostrou mais resistente que o de mandioca, principalmente quando plasticizado com glicerina, tendo a temperatura de processamento pouca influência sobre os resultados. Com relação aos teores de látex adicionados, não foi observada nenhuma melhora significativa sobre a resistência mecânica dos TPS, exceto um pequeno aumento nos valores de alongamento à ruptura. A adição de látex proporcionou uma diminuição linear na absorção máxima de água no equilíbrio, assim como uma redução nos valores de coeficiente de difusão de água apresentado pelos TPS. Uma vez que o processo de mistura desempenha uma função importante na morfologia destas blendas, na maioria dos TPS plasticizados com glicerina, entretanto, para os TPS plasticizados com etilenoglicol e com propilenoglicol não houve uma boa dispersão dos componentes das misturas. Os TPS de milho plasticizados com glicerina à 150oC foram os que apresentaram uma melhor dispersão das partículas de látex quando comparado com os demais. A qualidade destas dispersões foi uma conseqüência da utilização do látex ao invés da borracha sólida, uma vez que o primeiro apresenta a presença de proteínas e lipídeos na superfície das partículas de borracha presentes no látex, atuando como um compatibilizante entre o amido, uma matriz polar, e a borracha, um material não-polar. |
publishDate |
2006 |
dc.date.none.fl_str_mv |
2006-11-24 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/doctoralThesis |
format |
doctoralThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://www.teses.usp.br/teses/disponiveis/75/75131/tde-26042007-090356/ |
url |
http://www.teses.usp.br/teses/disponiveis/75/75131/tde-26042007-090356/ |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.none.fl_str_mv |
|
dc.rights.driver.fl_str_mv |
Liberar o conteúdo para acesso público. info:eu-repo/semantics/openAccess |
rights_invalid_str_mv |
Liberar o conteúdo para acesso público. |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.coverage.none.fl_str_mv |
|
dc.publisher.none.fl_str_mv |
Biblioteca Digitais de Teses e Dissertações da USP |
publisher.none.fl_str_mv |
Biblioteca Digitais de Teses e Dissertações da USP |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações da USP instname:Universidade de São Paulo (USP) instacron:USP |
instname_str |
Universidade de São Paulo (USP) |
instacron_str |
USP |
institution |
USP |
reponame_str |
Biblioteca Digital de Teses e Dissertações da USP |
collection |
Biblioteca Digital de Teses e Dissertações da USP |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações da USP - Universidade de São Paulo (USP) |
repository.mail.fl_str_mv |
virginia@if.usp.br|| atendimento@aguia.usp.br||virginia@if.usp.br |
_version_ |
1815257354634002432 |