Effect of the superficial treatment in the repair of silorane-based composite aged artificially

• Autor(a) principal: DALAZEN,Chaiane Emilia
• Data de Publicação: 2015
• Outros Autores: SINHORETI,Mario Alexandre Coelho, COUTINHO,Margareth
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: RGO - Revista Gaúcha de Odontologia (Online)
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1981-86372015010500376
• topic: Dental restoration repair; Dental restoration failure; Dental materials; Tensile strength

Objective: To evaluate the effects of different surface treatments, in repair bond strength of an aged silorane-based composite. Methods: Specimens were made of a silorane-based composite (P90, 3M/ESPE), aged with thermal-cycling (10,000 cycles; 5-55ºC) and randomly submitted to different surface treatments (each group n = 24): control group (no repair); group 1 (only application of P90 adhesive); group 2 (diamond bur asperization + P90 adhesive); group 3 (aluminum oxide sandblasting + P90 adhesive) and group 4 (asperization + sandblasting + P90 adhesive). Then, the specimens were repaired with the same silorane-based composite and each group randomly subdivided into 2 subgroups: stored in distilled water at 37 °C for 7 days or submitted to thermal-cycling (5,000 cycles). After aging, the tensile test was carried out. The data was submitted to 2-way analysis of variance (2-way ANOVA). Results: The repaired groups aged with oven storage for 7 days did not statistically differ (p>0.05) from the corresponding groups aged with thermal-cycling. The bond strength of the specimens was significantly influenced by the superficial treatment (p<0.01). The highest values of tensile bond strength were found in groups 3 (20.76 ± 4.51 MPa) and 4 (20.67± 3.96 MPa), regardless of aging and repair. Conclusion: The repair of silorane-based composite showed to be stable after aging, and the superficial treatment with aluminum oxide sandblasting was the most effective.