Termoformação de compósitos de biopolímeros com resíduos de cartão

Detalhes bibliográficos
Autor(a) principal: Marinho, Francisca da Silva
Data de Publicação: 2022
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
Texto Completo: https://hdl.handle.net/1822/82391
Resumo: Dissertação de mestrado integrado em Engenharia de Polímeros
id RCAP_a6aca9b6c05ec03f6c2f410784bf528d
oai_identifier_str oai:repositorium.sdum.uminho.pt:1822/82391
network_acronym_str RCAP
network_name_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository_id_str 7160
spelling Termoformação de compósitos de biopolímeros com resíduos de cartãoResíduos de cartãoBiopolímerosCompósitos de fibras naturaisTermoformaçãoCardboard wasteBiopolymersNatural fibber compositesThermoformingEngenharia e Tecnologia::Engenharia dos MateriaisDissertação de mestrado integrado em Engenharia de PolímerosNeste trabalho desenvolveu-se compósitos de biopolímeros com resíduos de cartão provenientes de indústria da embalagem, nomeadamente, de embalagens de ovos, para a produção de embalagens termoformadas. A incorporação destes numa matriz de um biopolímero tem como principal objetivo desenvolver embalagens reutilizáveis que no seu fim de vida útil sejam compostáveis, mitigando o impacto ambiental. O cartão foi caracterizado morfologicamente e termicamente, de modo a avaliar a sua apetência para ser processado por extrusão. Os resultados do TGA mostraram estabilidade térmica do cartão até cerca de 200C. Prepararam-se compósitos com o biopolímero Inzea F38 da Nurel e cartão com diferentes taxas de incorporação, nomeadamente, 5%, 10% e 15%. Inicialmente, preparam-se dois masterbatch com 50% de carga, um com F38 de injeção e outro com Vinnex8880, um agente compatibilizador que visa melhorar a interação entre carga-polímero adequado para biopolímeros. Seguidamente, foram preparadas por extrusão as várias composições em forma de folha, diluindo nas proporções adequadas os masterbatch para se obter composições com 5%, 10% e 15% de carga. Para as composições de 15% de carga, estudou-se ainda a influência da adição de outros polímeros, nomeadamente do biopolímero da Inzea o F10 e do Vinnex 2504, com ductibilidade superior ao F38, para mitigar o possível aumento de rigidez provocado pela incorporação das cargas. Para a caracterização mecânica dos materiais compósitos foram cortados provetes no sentido da extrusão e no sentido perpendicular à extrusão. Os resultados mostraram que os compósitos são materiais com menor deformação à rotura. A adesão carga-matriz foi observada por SEM em amostras cortadas em folhas antes de termoformar e em regiões das peças termoformadas que sofreram maior deformação. Em ambas as situações, mostram uma excelente compatibilidade e adesão entre carga e a matriz polimérica. A presença do aditivo, também identificada nas imagens de SEM como uma fase não miscível e muito bem distribuída, facilitando o processo de adesão. A termoformabilidade dos materiais compósitos foi estudada termoformando as folhas obtidas, usando um molde protótipo com diferentes razões de estiramento e a várias temperaturas. Os resultados mostraram que a termoformabilidade depende da percentagem de incorporação de carga, obtendo-se um rácio de área máximo de 2 para 5% e de 7 para 15% de carga em molde fêmea.In this dissertation biopolymers composites were developed with cardboard waste sourced from the packing industry, particularly, egg packaging, to produce thermoformed packaging. The incorporation of this waste into a polymeric matrix has as its main objective the development of reusable packaging which, at in the end of their useful life are compostable, to mitigate their environmental impact. The cardboard was characterized morphologically and thermally in order to evaluate its capability to be processed by extrusion. The results of TGA shows thermal stability of cardboard up to 200C. Composites were prepared with Nurel's Inzea F38 biopolymer and cardboard wastes with different incorporation rates, specifically, 5%, 10% and 15%. In a first phase, two masterbatches with 50% filler were prepared one with injection grade F38 and other with Vinnex8880, a dispersant and coupling agent, aiming the improvement of fillers-polymer interaction, and it is compatible with biopolymers. In a second phase of the work, were extruded sheets, diluting the masterbatch in the adequate proportions, of both F38 and Vinnex 8880, to obtain compositions with 5%, 10% and 15% of filers. For compositions with 15% filler, the influence of the addition of other polymers was also studied, particularly, Nurel's Inzea F10 biopolymer and Vinnex8880, whose ductility is higher than F38, to minimaze the possible rigidity increment due to the incorporation. For the mechanical characterization of composite materials test stamples were cut from the extruded sheets, in the direction of extrusion and perpendicular to the extrusion. The results showed that the materials present lower strain at break and higher elastic modulus when compared the neat materials, keeping the ductile behaviour. The filler-polymers adhesion was observed by SEM in samples collected from sheets before thermoforming and and in regions of thermoformed parts that suffered the highest deformation. In both situations, they show an excellent compatibility and adhesion between the filler and the polymeric matrix. The presence of the additive, also identified in the SEM images as an immiscible phase and with a good distribution, enhance the adhesion process. The thermoformability of composite materials was studied by thermoforming the extruded sheets, using a prototype mould with different stretch ratios and various temperatures. The results show that the thermoformability is strongly dependent on the percentage of filler incorporation, obtaining a maximum area ratio of 2 for 5% and 7 for 15% load on the female part of the mould.Duarte, F. M.Universidade do MinhoMarinho, Francisca da Silva2022-11-282022-11-28T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdfhttps://hdl.handle.net/1822/82391por203114647info:eu-repo/semantics/openAccessreponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãoinstacron:RCAAP2023-07-21T12:12:51Zoai:repositorium.sdum.uminho.pt:1822/82391Portal AgregadorONGhttps://www.rcaap.pt/oai/openaireopendoar:71602024-03-19T19:04:51.359326Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informaçãofalse
dc.title.none.fl_str_mv Termoformação de compósitos de biopolímeros com resíduos de cartão
title Termoformação de compósitos de biopolímeros com resíduos de cartão
spellingShingle Termoformação de compósitos de biopolímeros com resíduos de cartão
Marinho, Francisca da Silva
Resíduos de cartão
Biopolímeros
Compósitos de fibras naturais
Termoformação
Cardboard waste
Biopolymers
Natural fibber composites
Thermoforming
Engenharia e Tecnologia::Engenharia dos Materiais
title_short Termoformação de compósitos de biopolímeros com resíduos de cartão
title_full Termoformação de compósitos de biopolímeros com resíduos de cartão
title_fullStr Termoformação de compósitos de biopolímeros com resíduos de cartão
title_full_unstemmed Termoformação de compósitos de biopolímeros com resíduos de cartão
title_sort Termoformação de compósitos de biopolímeros com resíduos de cartão
author Marinho, Francisca da Silva
author_facet Marinho, Francisca da Silva
author_role author
dc.contributor.none.fl_str_mv Duarte, F. M.
Universidade do Minho
dc.contributor.author.fl_str_mv Marinho, Francisca da Silva
dc.subject.por.fl_str_mv Resíduos de cartão
Biopolímeros
Compósitos de fibras naturais
Termoformação
Cardboard waste
Biopolymers
Natural fibber composites
Thermoforming
Engenharia e Tecnologia::Engenharia dos Materiais
topic Resíduos de cartão
Biopolímeros
Compósitos de fibras naturais
Termoformação
Cardboard waste
Biopolymers
Natural fibber composites
Thermoforming
Engenharia e Tecnologia::Engenharia dos Materiais
description Dissertação de mestrado integrado em Engenharia de Polímeros
publishDate 2022
dc.date.none.fl_str_mv 2022-11-28
2022-11-28T00:00:00Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/1822/82391
url https://hdl.handle.net/1822/82391
dc.language.iso.fl_str_mv por
language por
dc.relation.none.fl_str_mv 203114647
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
instname:Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron:RCAAP
instname_str Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
instacron_str RCAAP
institution RCAAP
reponame_str Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
collection Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos)
repository.name.fl_str_mv Repositório Científico de Acesso Aberto de Portugal (Repositórios Cientìficos) - Agência para a Sociedade do Conhecimento (UMIC) - FCT - Sociedade da Informação
repository.mail.fl_str_mv
_version_ 1799132459289280512

Registros relacionados